Regulating the Interfacial Solvation Environment by a Pyran-Based Polymer for High-Areal-Capacity and Low-Temperature-Endurable Magnesium Metal Batteries
Source abstract
Abstract
Regulating the artificial solid electrolyte interphase (SEI) and interfacial solvation structure of the electrolyte is crucial for developing rechargeable magnesium batteries (RMBs) with long cycling life, high current density tolerance, and fast ion transport capability operated under extreme environments, such as low temperatures. Herein, an effective strategy using oligomeric poly(3,4-dihydro-2 H -pyran) (polyDHP) is proposed to modulate the interfacial solvation structure of RMBs, with the construction of an artificial SEI with rapid Mg-ion conductivity. The steric hindrance of polyDHP and its electrostatic interaction with Mg 2+ reduce the solvent molecules in the first solvation shell, allowing polyDHP molecules to participate in coordination, thus lowering the desolvation energy barrier of Mg 2+ and facilitating their deposition and stripping. Furthermore, due to the glass transition behavior, oligomeric polyDHP exhibits a more ordered structure with more continuous internal ion transport channels at −20 °C, therefore enabling stable RMB operation at lower temperatures for the first time. The corresponding Mg symmetric cells display a much lower overpotential (400 mV) and excellent cycling stability at both room temperature (over 5000 h at 5 mA cm –2 and 10 mA h cm –2 ) and a low temperature of −20 °C (over 1300 h at 3 mA cm –2 and 3 mA h cm –2 ). This strategy supports the stable cycling of CuS∥Mg full cells for over 200 cycles at −20 °C. This work reveals the importance of regulating the interfacial solvation structure, promoting the realistic applications of RMBs under extreme conditions.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced Battery Materials and Technologies · Advancements in Battery Materials · Supercapacitor Materials and Fabrication
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, 585 He Shuo Road, Shanghai 201899, China
School of Materials Science and Engineering
Shanghai University
CAS Key Laboratory of Materials for Energy Conversion
Shanghai Institute of Ceramics, Chinese Academy of Sciences
Center of Materials Science and Optoelectronics Engineering
University of Chinese Academy of Sciences
Funding
National Natural Science Foundation of China
References (59)
Show source-provided references
1. 10.1038/s41467-022-35636-010.1038/s41467-022-35636-0 ↗
2. 10.1038/s41560-020-00734-010.1038/s41560-020-00734-0 ↗
3. 10.1002/smtd.20230110910.1002/smtd.202301109 ↗
4. 10.1021/acsenergylett.1c0248610.1021/acsenergylett.1c02486 ↗
5. 10.1038/3503755310.1038/35037553 ↗
6. 10.1149/1.208655310.1149/1.2086553 ↗
7. 10.1039/C3CC47896C10.1039/C3CC47896C ↗
8. 10.1021/acsnano.4c0396810.1021/acsnano.4c03968 ↗
9. 10.1002/anie.20141220210.1002/anie.201412202 ↗
10. 10.1021/acs.nanolett.3c0003310.1021/acs.nanolett.3c00033 ↗
11. 10.1021/acsami.7b1649110.1021/acsami.7b16491 ↗
12. 10.1021/acs.jpclett.8b0220910.1021/acs.jpclett.8b02209 ↗
13. 10.1126/science.abg395410.1126/science.abg3954 ↗
14. 10.1002/aenm.20230154410.1002/aenm.202301544 ↗
15. 10.1021/acsenergylett.2c0252510.1021/acsenergylett.2c02525 ↗
16. 10.1002/aenm.20230179510.1002/aenm.202301795 ↗
17. 10.1002/aenm.20220260210.1002/aenm.202202602 ↗
18. 10.1002/aenm.20170172810.1002/aenm.201701728 ↗
19. 10.1016/j.ensm.2019.11.01210.1016/j.ensm.2019.11.012 ↗
20. 10.1021/acsami.1c0764810.1021/acsami.1c07648 ↗
21. 10.1246/cl.21007210.1246/cl.210072 ↗
22. 10.1021/acsami.3c0722310.1021/acsami.3c07223 ↗
23. 10.1021/acsenergylett.1c0124310.1021/acsenergylett.1c01243 ↗
24. 10.1021/acsenergylett.3c0176110.1021/acsenergylett.3c01761 ↗
25. 10.1002/smll.20210216810.1002/smll.202102168 ↗
26. 10.1039/D2TA02083A10.1039/D2TA02083A ↗
27. 10.1021/acsami.2c1191110.1021/acsami.2c11911 ↗
28. 10.1016/j.cej.2023.14819310.1016/j.cej.2023.148193 ↗
29. 10.1021/acs.macromol.3c0046310.1021/acs.macromol.3c00463 ↗
30. 10.1002/pola.2278510.1002/pola.22785 ↗
31. 10.1016/j.jpowsour.2021.22994610.1016/j.jpowsour.2021.229946 ↗
32. 10.1038/s41467-023-38890-y10.1038/s41467-023-38890-y ↗
33. 10.1126/sciadv.abj149110.1126/sciadv.abj1491 ↗
34. 10.1016/j.joule.2023.10.01210.1016/j.joule.2023.10.012 ↗
35. 10.1016/j.ensm.2021.12.02310.1016/j.ensm.2021.12.023 ↗
36. 10.1021/acsami.2c2057110.1021/acsami.2c20571 ↗
37. 10.1093/nsr/nwz15710.1093/nsr/nwz157 ↗
38. 10.1039/D1EE00614B10.1039/D1EE00614B ↗
39. 10.1016/j.ensm.2019.06.03510.1016/j.ensm.2019.06.035 ↗
40. 10.1016/j.cej.2021.13075110.1016/j.cej.2021.130751 ↗
41. 10.1021/acs.nanolett.2c0371010.1021/acs.nanolett.2c03710 ↗
42. 10.1002/adfm.20221063910.1002/adfm.202210639 ↗
43. 10.1038/s41557-018-0019-610.1038/s41557-018-0019-6 ↗
44. 10.1016/j.ensm.2022.06.01410.1016/j.ensm.2022.06.014 ↗
45. 10.1002/adma.20210811410.1002/adma.202108114 ↗
46. 10.1002/aenm.20240150710.1002/aenm.202401507 ↗
47. 10.1016/j.nanoen.2018.02.06010.1016/j.nanoen.2018.02.060 ↗
48. 10.3390/polym1104060110.3390/polym11040601 ↗
49. 10.3390/polym1521426810.3390/polym15214268 ↗
50. 10.1016/j.ccr.2017.03.00210.1016/j.ccr.2017.03.002 ↗
51. 10.1039/D4EE01463D10.1039/D4EE01463D ↗
52. 10.1039/D0EE03952G10.1039/D0EE03952G ↗
53. 10.1016/0039-6028(96)00083-010.1016/0039-6028(96)00083-0 ↗
54. 10.1039/D1CC02048J10.1039/D1CC02048J ↗
55. 10.1002/smll.20240556810.1002/smll.202405568 ↗
56. 10.15541/jim2021035310.15541/jim20210353 ↗
57. 10.34133/2022/984083710.34133/2022/9840837 ↗
58. 10.1038/s41467-024-46186-y10.1038/s41467-024-46186-y ↗
59. 10.1016/j.fuel.2020.11832310.1016/j.fuel.2020.118323 ↗