THE ROLE OF UREA ON THE HYDROTHERMAL SYNTHESIS OF BOEHMITE NANOARCHITECTURES
Source abstract
Abstract
The AlOOH nanoarchitectures have been successfully synthesized via hydrothermal method. The effect of urea/nitrate molar ratio 1, 2, and 4 were studied to obtain the various AlOOH nanoarchitectures. The products were characterized by XRD, FT-IR, FESEM, and TEM techniques. The specific surface area of samples was determined by N 2 adsorption-desorption measurements. Our experiments showed that AlOOH nanoarchitectures have been formed in all three ratios of urea/nitrate and the increase of urea/nitrate molar ratio from 1 to 2 then it favors for the formation of flowerlike AlOOH nanoarchitectures. The microscope analysis revealed that the flowerlike AlOOH are composed of nano-layers.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Carbon Nanotubes in Composites · Diamond and Carbon-based Materials Research · Boron and Carbon Nanomaterials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (32)
Show source-provided references
1. 10.1016/j.matlet.2006.03.08310.1016/j.matlet.2006.03.083 ↗
2. 10.1016/j.matlet.2012.01.05010.1016/j.matlet.2012.01.050 ↗
3. 10.1016/j.matlet.2008.01.07810.1016/j.matlet.2008.01.078 ↗
4. 10.1016/j.tsf.2007.02.02910.1016/j.tsf.2007.02.029 ↗
5. 10.1016/j.ceramint.2008.06.00310.1016/j.ceramint.2008.06.003 ↗
6. 10.1016/j.ceramint.2011.06.02610.1016/j.ceramint.2011.06.026 ↗
7. 10.1016/j.matlet.2007.01.08510.1016/j.matlet.2007.01.085 ↗
8. 10.1016/j.matlet.2006.02.01610.1016/j.matlet.2006.02.016 ↗
9. 10.1016/j.ceramint.2010.12.00410.1016/j.ceramint.2010.12.004 ↗
10. 10.3184/174751914X1391093897274810.3184/174751914X13910938972748 ↗
11. 10.2298/JSC130903007A10.2298/JSC130903007A ↗
12. 10.1016/j.jiec.2013.08.04110.1016/j.jiec.2013.08.041 ↗
13. 10.1016/j.ceramint.2014.06.00510.1016/j.ceramint.2014.06.005 ↗
14. 10.1016/j.enconman.2015.03.06410.1016/j.enconman.2015.03.064 ↗
15. 10.1016/j.ultsonch.2015.12.01010.1016/j.ultsonch.2015.12.010 ↗
16. 10.1002/pssb.20114748410.1002/pssb.201147484 ↗
17. 10.1016/j.jiec.2011.11.07910.1016/j.jiec.2011.11.079 ↗
18. 10.1016/j.jlumin.2003.09.00410.1016/j.jlumin.2003.09.004 ↗
19. 10.1016/j.cplett.2007.03.02010.1016/j.cplett.2007.03.020 ↗
20. 10.1016/j.cplett.2007.03.02010.1016/j.cplett.2007.03.020 ↗
21. 10.1016/j.jcrysgro.2005.09.03410.1016/j.jcrysgro.2005.09.034 ↗
22. 10.1002/crat.20090051410.1002/crat.200900514 ↗
23. 10.1021/jp805751t10.1021/jp805751t ↗
24. 10.1016/j.matchemphys.2008.01.00410.1016/j.matchemphys.2008.01.004 ↗
25. 10.1021/cg700768310.1021/cg7007683 ↗
26. 10.1016/j.micromeso.2009.02.00310.1016/j.micromeso.2009.02.003 ↗
27. 10.1002/ejic.20090103610.1002/ejic.200901036 ↗
28. 10.1016/S1350-4495(01)00117-710.1016/S1350-4495(01)00117-7 ↗
29. 10.1006/jssc.2000.903410.1006/jssc.2000.9034 ↗
30. 10.1016/j.matlet.2007.08.06710.1016/j.matlet.2007.08.067 ↗
31. 10.1351/pac19855704060310.1351/pac198557040603 ↗
32. 10.1038/354056a010.1038/354056a0 ↗