PREPARATION AND GRAIN-GROWTH OF MAGNESIA-ALUMINA SPINEL/YTTRIUM ALUMINUM GARNET COMPOSITE FIBERS
Source abstract
Abstract
Magnesia-alumina spinel/yttrium aluminum garnet composite fibers were prepared by sol-gel method. The spinnability of precursor sol remarkably depended on the addition amount of polyvinylpyrrolidone. Long gel fibers, with 80 cm in length, were obtained by adding 28 wt. % spinning additive. The phases of composite fibers were magnesia-alumina spinel and yttrium aluminum garnet after heating at 1400C for 2 h. The Mg iron can hinder the yttrium aluminum garnet grain growth by solute drag and grain boundary pinning. The grain growth exponent was about 3.7 at 1600C.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Aluminum Alloys Composites Properties · Advanced ceramic materials synthesis · Additive Manufacturing and 3D Printing Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (24)
Show source-provided references
1. 10.1016/j.matchemphys.2008.07.02510.1016/j.matchemphys.2008.07.025 ↗
2. 10.1016/j.jallcom.2017.01.12810.1016/j.jallcom.2017.01.128 ↗
3. 10.1016/j.jeurceramsoc.2005.03.25410.1016/j.jeurceramsoc.2005.03.254 ↗
4. 10.1016/S0955-2219(98)00283-010.1016/S0955-2219(98)00283-0 ↗
5. 10.1016/j.jeurceramsoc.2017.11.02610.1016/j.jeurceramsoc.2017.11.026 ↗
6. 10.1016/S1359-835X(01)00014-810.1016/S1359-835X(01)00014-8 ↗
7. 10.1016/j.jeurceramsoc.2017.02.01010.1016/j.jeurceramsoc.2017.02.010 ↗
8. 10.1016/j.jeurceramsoc.2005.06.04510.1016/j.jeurceramsoc.2005.06.045 ↗
9. 10.1016/j.ceramint.2017.10.12410.1016/j.ceramint.2017.10.124 ↗
10. 10.1016/j.jeurceramsoc.2004.08.02010.1016/j.jeurceramsoc.2004.08.020 ↗
11. 10.1007/s10971-009-2106-z10.1007/s10971-009-2106-z ↗
12. 10.1016/j.matlet.2015.08.02710.1016/j.matlet.2015.08.027 ↗
13. 10.1007/s10971-015-3868-010.1007/s10971-015-3868-0 ↗
14. 10.1007/s10971-017-4410-310.1007/s10971-017-4410-3 ↗
15. 10.1016/j.ceramint.2007.07.03210.1016/j.ceramint.2007.07.032 ↗
16. 10.1016/j.jcrysgro.2008.05.05410.1016/j.jcrysgro.2008.05.054 ↗
17. 10.1016/j.jeurceramsoc.2017.09.01710.1016/j.jeurceramsoc.2017.09.017 ↗
18. 10.1016/j.materresbull.2017.10.01910.1016/j.materresbull.2017.10.019 ↗
19. 10.1016/j.commatsci.2012.11.04510.1016/j.commatsci.2012.11.045 ↗
20. 10.1016/S0921-5107(03)00198-310.1016/S0921-5107(03)00198-3 ↗
21. 10.1016/j.ceramint.2016.11.13110.1016/j.ceramint.2016.11.131 ↗
22. 10.1016/j.jeurceramsoc.2009.03.00310.1016/j.jeurceramsoc.2009.03.003 ↗
23. 10.1016/j.msea.2006.04.07210.1016/j.msea.2006.04.072 ↗
24. 10.1016/j.jeurceramsoc.2007.12.00610.1016/j.jeurceramsoc.2007.12.006 ↗