FFECTS OF DIFFERENT Li₂O/Al₂O₃ RATIOS ON THE STRUCTURE, PHASE COMPOSITION, AND PROPERTIES OF Li₂O-Al₂O₃-SiO₂ Glass-Ceramics

Xiaorong Yang

Abstract

In this study, the effects of different Li₂O/Al₂O₃ ratios on the structure, phase composition and properties of Li₂O-Al₂O₃-SiO₂ glass-ceramics were investigated. The crystallisation behaviour and structure of the glass samples were investigated using differential scanning calorimetry (DSC), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, field-emission scanning electron microscopy (FE-SEM) and other characterisation methods. When the Li₂O/Al₂O₃ ratio (wt.%) was increased from 0.89 to 2.4, the main crystalline phase changed from quartz to a lithium disilicate (LD) phase, indicating that a high Li₂O/Al₂O₃ ratio (wt.%) was more favourable for the precipitation of the LD phase. Finally, a glass-ceramic with a flexural strength of 199 ± 5 MPa, a microhardness of 767 ± 20 HV and a visible light transmission rate of 80% at 550 nm was obtained. Owing to its high Li+ content, this glass-ceramic facilitates chemical strengthening to further improve its mechanical properties and expand its range of applications, such as in electronic display devices.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Glass properties and applications · Recycling and utilization of industrial and municipal waste in materials production · Microwave Dielectric Ceramics Synthesis

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (35)

Show source-provided references
1. 10.1111/j.1551-2916.2010.04220.x10.1111/j.1551-2916.2010.04220.x ↗
2. 10.1557/mrs.2017.2710.1557/mrs.2017.27 ↗
3. 10.1016/j.jeurceramsoc.2010.04.01710.1016/j.jeurceramsoc.2010.04.017 ↗
4. 10.1016/j.jeurceramsoc.2016.10.020 10.1016/j.jmbbm.2018.02.02310.1016/j.jeurceramsoc.2016.10.020 10.1016/j.jmbbm.2018.02.023 ↗
5. 10.1080/0371750x.2013.79402710.1080/0371750x.2013.794027 ↗
6. 10.1016/j.ceramint.2020.10.03910.1016/j.ceramint.2020.10.039 ↗
7. 10.1016/j.jnoncrysol.2007.08.05210.1016/j.jnoncrysol.2007.08.052 ↗
8. 10.1063/1.149998910.1063/1.1499989 ↗
9. 10.3390/ma1409209410.3390/ma14092094 ↗
10. 10.1016/j.jnoncrysol.2016.11.03210.1016/j.jnoncrysol.2016.11.032 ↗
11. 10.1016/j.jssc.2009.10.00610.1016/j.jssc.2009.10.006 ↗
12. 10.1088/2053-1591/abffa110.1088/2053-1591/abffa1 ↗
13. 10.1016/j.ceramint.2014.08.07410.1016/j.ceramint.2014.08.074 ↗
14. 10.1016/j.jeurceramsoc.2019.07.03210.1016/j.jeurceramsoc.2019.07.032 ↗
15. 10.1116/1.499872610.1116/1.4998726 ↗
16. 10.1016/j.matpr.2019.06.44610.1016/j.matpr.2019.06.446 ↗
17. 10.1016/j.ceramint.2019.05.02910.1016/j.ceramint.2019.05.029 ↗
18. 10.1016/j.matlet.2004.06.07510.1016/j.matlet.2004.06.075 ↗
19. 10.1016/S0022-2860(02)00261-210.1016/S0022-2860(02)00261-2 ↗
20. 10.1039/c4cp03609c10.1039/c4cp03609c ↗
21. 10.1063/1.43167110.1063/1.431671 ↗
22. 10.1016/j.jnoncrysol.2018.04.02110.1016/j.jnoncrysol.2018.04.021 ↗
23. 10.1111/j.1551-2916.2011.04936.x10.1111/j.1551-2916.2011.04936.x ↗
24. 10.1016/j.jnoncrysol.2006.06.03810.1016/j.jnoncrysol.2006.06.038 ↗
25. 10.1016/j.jssc.2010.04.01110.1016/j.jssc.2010.04.011 ↗
26. 10.1016/j.gca.2013.10.02510.1016/j.gca.2013.10.025 ↗
27. 10.1016/S0022-3093(00)00270-210.1016/S0022-3093(00)00270-2 ↗
28. 10.1016/j.jnoncrysol.2013.09.01910.1016/j.jnoncrysol.2013.09.019 ↗
29. 10.1016/j.matchemphys.2019.12213110.1016/j.matchemphys.2019.122131 ↗
30. 10.1016/j.jnoncrysol.2006.06.03910.1016/j.jnoncrysol.2006.06.039 ↗
31. 10.1016/j.jnoncrysol.2009.11.01510.1016/j.jnoncrysol.2009.11.015 ↗
32. 10.1063/1.44247210.1063/1.442472 ↗
33. 10.1016/j.jnoncrysol.2021.12125610.1016/j.jnoncrysol.2021.121256 ↗
34. 10.1021/ie50595a02210.1021/ie50595a022 ↗
35. 10.1021/ie50472a04210.1021/ie50472a042 ↗