Bimetal‐Organic‐Framework Derivation of Ball‐Cactus‐Like Ni‐Sn‐P@C‐CNT as Long‐Cycle Anode for Lithium Ion Battery

Small 2017, 13, 1700521 DOI: 10.1002/smll.201700521 In this manuscript, several SEM/EDS measurements were performed. A silicon wafer substrate was used to support samples for EDS measurements which results in a high-density peak for Si centered at ≈1.8 keV. The authors removed this peak in all EDS-spectra to ensure clear presentation of the results but failed to inform readers about this image processing step. Figures 2, 5, and S1 containing unaltered EDS-spectra are found below. The conclusions of this article remain unchanged by this processing step. The authors apologize for this unintended mistake.