Entrapped Molecule‐Like Europium‐Oxide Clusters in Zinc Oxide with Nearly Unaffected Host Structure

Abstract Nanocrystalline ZnO sponges doped with 5 mol% EuO_1.5are obtained by heating metal–salt complex based precursor pastes at 200–900 °C for 3 min. X‐ray diffraction, transmission electron microscopy, and extended X‐ray absorption fine structure (EXAFS) show that phase separation into ZnO:Eu andc‐Eu₂O₃takes place upon heating at 700 °C or higher. The unit cell of the clean oxide made at 600 °C shows only ≈0.4% volume increase versus undoped ZnO, and EXAFS shows a ZnO local structure that is little affected by the Eu‐doping and an average Eu³⁺ion coordination number of ≈5.2. Comparisons of 23 density functional theory‐generated structures having differently sized Eu‐oxide clusters embedded in ZnO identify three structures with four or eight Eu atoms as the most energetically favorable. These clusters exhibit the smallest volume increase compared to undoped ZnO and Eu coordination numbers of 5.2–5.5, all in excellent agreement with experimental data. ZnO defect states are crucial for efficient Eu³⁺excitation, whilec‐Eu₂O₃phase separation results in loss of the characteristic Eu³⁺photoluminescence. The formation of molecule‐like Eu‐oxide clusters, entrapped in ZnO, proposed here, may help in understanding the nature of the unexpected high doping levels of lanthanide ions in ZnO that occur virtually without significant change in ZnO unit cell dimensions.