Phase Restructuring in Transition Metal Dichalcogenides for Highly Stable Energy Storage
Source abstract
Abstract
High Resolution Image Download MS PowerPoint Slide Achieving homogeneous phase transition and uniform charge distribution is essential for good cycle stability and high capacity when phase conversion materials are used as electrodes. Herein, we show that chemical lithiation of bulk 2H-MoS 2 distorts its crystalline domains in three primary directions to produce mosaic-like 1T′ nanocrystalline domains, which improve phase and charge uniformity during subsequent electrochemical phase conversion. 1T′-Li x MoS 2, a macroscopic dense material with interconnected nanoscale grains, shows excellent cycle stability and rate capability in a lithium rechargeable battery compared to bulk or exfoliated-restacked MoS 2 . Transmission electron microscopy studies reveal that the interconnected MoS 2 nanocrystals created during the phase change process are reformable even after multiple cycles of galvanostatic charging/discharging, which allows them to play important roles in the long term cycling performance of the chemically intercalated TMD materials. These studies shed light on how bulk TMDs can be processed into quasi-2D nanophase material for stable energy storage.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: 2D Materials and Applications · Perovskite Materials and Applications · Chalcogenide Semiconductor Thin Films
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemistry, National University of Singapore, 3 Science Drive 3, Singapore 117543
Solar Energy Research Institute of Singapore (SERIS), 7 Engineering Drive 1, Singapore 117574
Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, United States
Center for Advanced 2D Materials and Graphene Research Centre, 2 Science Drive 2, Singapore 117526
Funding
National Research Foundation Singapore
References (25)
Show source-provided references
1. 10.1038/nchem.158910.1038/nchem.1589 ↗
2. 10.1038/ncomms521410.1038/ncomms5214 ↗
3. 10.1039/C5CS00151J10.1039/C5CS00151J ↗
4. 10.1038/ncomms931110.1038/ncomms9311 ↗
5. 10.1021/nl403661s10.1021/nl403661s ↗
6. 10.1021/ar400231210.1021/ar4002312 ↗
7. 10.1021/ja404523s10.1021/ja404523s ↗
8. 10.1038/nnano.2015.4010.1038/nnano.2015.40 ↗
9. 10.1139/p83-01310.1139/p83-013 ↗
10. 10.1021/ja501686w10.1021/ja501686w ↗
11. 10.1021/acsnano.5b0525910.1021/acsnano.5b05259 ↗
12. 10.1103/PhysRevB.8.371910.1103/PhysRevB.8.3719 ↗
13. 10.1038/nnano.2014.6410.1038/nnano.2014.64 ↗
14. 10.1021/nn302422x10.1021/nn302422x ↗
15. 10.1021/acs.chemmater.5b0098610.1021/acs.chemmater.5b00986 ↗
16. 10.1021/acs.nanolett.5b0119610.1021/acs.nanolett.5b01196 ↗
17. 10.1021/nn100393710.1021/nn1003937 ↗
18. 10.1088/2053-1583/2/3/03501310.1088/2053-1583/2/3/035013 ↗
19. 10.1021/jp510083w10.1021/jp510083w ↗
20. 10.1038/ncomms1084310.1038/ncomms10843 ↗
21. 10.1103/PhysRevB.88.24542810.1103/PhysRevB.88.245428 ↗
22. 10.1063/1.482708210.1063/1.4827082 ↗
23. 10.1038/ncomms399510.1038/ncomms3995 ↗
24. 10.1002/anie.20120556910.1002/anie.201205569 ↗
25. 10.1021/ja404523s10.1021/ja404523s ↗