Tailor-Made Magnetic Fe₃O₄@mTiO₂ Microspheres with a Tunable Mesoporous Anatase Shell for Highly Selective and Effective Enrichment of Phosphopeptides

Selective enrichment of phosphoproteins or phosphopeptides from complex mixtures is essential for MS-based phosphoproteomics, but still remains a challenge. In this article, we described an unprecedented approach to synthesize magnetic mesoporous Fe(3)O(4)@mTiO(2) microspheres with a well-defined core/shell structure, a pure and highly crystalline TiO(2) layer, high specific surface area (167.1 m(2)/g), large pore volume (0.45 cm(3)/g), appropriate and tunable pore size (8.6-16.4 nm), and high magnetic susceptibility. We investigated the applicability of Fe(3)O(4)@mTiO(2) microspheres in a study of the selective enrichment of phosphopeptides. The experiment results demonstrated that the Fe(3)O(4)@mTiO(2) possessed remarkable selectivity for phosphopeptides even at a very low molar ratio of phosphopeptides/non-phosphopeptides (1:1000), large enrichment capacity (as high as 225 mg/g, over 10 times as that of the Fe(3)O(4)@TiO(2) microspheres), extreme sensitivity (the detection limit was at the fmol level), excellent speed (the enrichment can be completed in less than 5 min), and high recovery of phosphopeptides (as high as 93%). In addition, the high magnetic susceptibility allowed convenient separation of the target peptides by magnetic separation. These outstanding features give the Fe(3)O(4)@mTiO(2) composite microspheres high benefit for mass spectrometric analysis of phosphopeptides.