Rheological and mechanical properties of cemented foam backfill: Effect of mineral admixture type and dosage
Source abstract
Abstract
Abstract In this work, the effect of mineral admixture type and dosage on the rheological and mechanical behaviors of a newly developed backfilling material, cemented foam backfill (CFB), is comprehensively investigated. Fly ash (FA), ground granulated blast-furnace slag (GGBS) and quicklime are selected as mineral admixtures, while H2O2 and CaCO3 whisker are used as foaming agent and foaming stabilizer respectively. CFB samples are prepared with solid content between 70% and 76%, replacement rates of cement with FA or GGBS between 0% and 30% and cured at 7, 14 and 28 days. In addition, 5 wt % of FA or GGBS is replaced by an equal amount of quicklime to accelerate pozzolanic reaction in a portion of CFB samples. Then, fresh CFB is subjected to the rheological property (i.e., apparent viscosity and equivalent Bingham yield stress) test, while hardened CFB is subjected to porosity and mechanical tests. Additionally, thermogravimetric and X-ray diffractogram analyses are conducted on 7- and 28-day hydrated binder pastes (pure cement, cement + FA/GGBS, cement + FA/GGBS + quicklime) to reveal the influence of mineral admixture type and dosage on the hydration product of CFB.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Tailings Management and Properties · Rock Mechanics and Modeling · Grouting, Rheology, and Soil Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (65)
Show source-provided references
1. Utilization of water-reducing admixtures in cemented paste backfill of sulphide-rich mill tailings10.1016/j.jhazmat.2010.03.096 ↗
2. Experimental investigation into the compressive strength development of cemented paste backfill containing Nano-silica10.1016/j.cemconcomp.2016.06.016 ↗
3. Coupled effects of sulphate and temperature on the strength development of cemented tailings backfills: portland cement-paste backfill10.1016/j.cemconcomp.2010.08.002 ↗
4. Initial temperature-dependence of strength development and self-desiccation in cemented paste backfill that contains sodium silicate10.1016/j.cemconcomp.2016.01.005 ↗
5. Strength and self-desiccation of slag-cemented paste backfill at early ages: link to initial sulphate concentration10.1016/j.cemconcomp.2017.09.019 ↗
6. Analytical solution for determining the required strength of mine backfill based on its damage constitutive model10.1007/s11204-018-9483-7 ↗
7. Strength characteristics and failure mechanism of cemented super-fine unclassified tailings backfill10.3390/min7040058 ↗
8. Use of cemented super-fine unclassified tailings backfill for control of subsidence10.3390/min7110216 ↗
9. Influence of binder content on temperature and internal strain evolution of early age cemented tailings backfill10.1016/j.conbuildmat.2018.09.032 ↗
10. Effect of superplasticizer type and dosage on fluidity and strength behavior of cemented tailings backfill with different solid contents10.1016/j.conbuildmat.2018.07.155 ↗
11. Dynamic model validation using blast vibration monitoring in mine backfill10.1016/j.ijrmms.2018.04.047 ↗
12. Cemented paste backfill of sulphide-rich tailings: importance of binder type and dosage10.1016/j.cemconcomp.2009.01.008 ↗
13. Impact law of the bulk ratio of backfilling body to overlying strata movement in fully mechanized backfilling mining10.1134/S1062739147010096 ↗
14. A study of technical measures for increasing the roof-contacted ratio in stope and cavity filling
15. Evaluation of the strength and ultrasonic properties of foam-cemented paste backfill10.1080/17480930.2016.1215782 ↗
16. Utilization of foaming technology in cemented paste backfill of high-mud superfine unclassified tailings
17. Monitoring and mechanisms of ground deformation and ground fissures induced by cut-and-fill mining in the Jinchuan Mine 2, China10.1007/s12665-012-1877-7 ↗
18. Mechanical properties of porous ceramic scaffolds: influence of internal dimensions10.1016/j.ceramint.2015.03.044 ↗
19. Ordinary Portland Cement composition for the optimization of the synergies of supplementary cementitious materials of ternary binders in hydration processes10.1016/j.cemconcomp.2017.12.016 ↗
20. A review of binders used in cemented paste tailings for underground and surface disposal practices10.1016/j.jenvman.2013.09.039 ↗
21. Use of binary and ternary blends in high strength concrete10.1016/j.conbuildmat.2007.03.026 ↗
22. Properties of concrete produced from multicomponent blended cements10.1016/S0008-8846(02)00907-9 ↗
23. De Belie · 2018 · vol. 25 · 123
24. A review on the utilization of fly ash10.1016/j.pecs.2009.11.003 ↗
25. Efficiency of mineral admixtures in concrete: microstructure, compressive strength and stability of hydrate phases10.1016/j.clay.2013.08.021 ↗
26. Activation of fly ash cementitious systems in the presence of quicklime: Part I. Compressive strength and pozzolanic reaction rate10.1016/j.cemconres.2003.08.008 ↗
27. The effect of grinding on the physical properties of fly ashes and a portland cement clinker10.1016/S0008-8846(97)00194-4 ↗
28. Acceleration of strength gain of lime-pozzolan cements by thermal activation10.1016/0008-8846(93)90036-9 ↗
29. Hardening mechanisms of an alkaline-activated class F fly ash10.1016/S0008-8846(01)00571-3 ↗
30. Pozzolanic reaction in the presence of chemical activators: Part II. Reaction products and mechanism10.1016/S0008-8846(00)00214-3 ↗
31. Studies on several factors affecting hydration and properties of lime-pozzolan cements10.1061/(ASCE)0899-1561(2001)13:6(441) ↗
32. Effect of fly ash fineness on microstructure of blended cement paste10.1016/j.conbuildmat.2005.12.024 ↗
33. Influence of particle size on the basic and time-dependent rheological behaviors of cemented paste backfill10.1007/s11665-018-3467-7 ↗
34. The influence of mineral admixtures on the rheology of cement paste and concrete10.1016/S0008-8846(00)00454-3 ↗
35. Effect of mineral admixtures on rheological properties of cement paste10.4028/www.scientific.net/AMR.936.1409 ↗
36. 2019
37. Cementitious backfill with high sulfur content Physical, chemical, and mineralogical characterization - stabilite chimique des hydrates10.1016/S0008-8846(99)00023-X ↗
38. Specimen size effect on strength behavior of cemented paste backfills subjected to different placement conditions10.1016/j.enggeo.2014.11.015 ↗
39. Novel porous fly-ash containing geopolymer monoliths for lead adsorption from wastewaters10.1016/j.jhazmat.2016.07.059 ↗
40. Thermal insulating foamy geopolymers from perlite10.1016/j.mineng.2010.07.015 ↗
41. Thermal insulation and thermally resistant materials made of geopolymer foams10.1016/j.proeng.2016.07.350 ↗
42. Characterization of mechanical behavior and mechanism of calcium carbonate whisker-reinforced cement mortar10.1016/j.conbuildmat.2014.05.059 ↗
43. Rheological behaviour of cement paste added with natural fibres10.1016/j.conbuildmat.2018.11.179 ↗
44. Chapter 1 - non-Newtonian fluid behaviour
45. Ultimate limit state of pre-stressed reinforced concrete elements10.1016/j.matdes.2015.02.020 ↗
46. Study on volume stability of chemical foaming cement paste10.1007/s12205-017-0985-z ↗
47. Effect of different substitution of natural aggregate by recycled aggregate on performance characteristics of pervious concrete10.1617/s11527-014-0517-y ↗
48. Preparation and characterization of high porosity cement-based foam material10.1016/j.conbuildmat.2015.05.032 ↗
49. Non-isothermal kinetics of biomass-pyrolysis-derived-tar (BPDT) thermal decomposition via thermogravimetric analysis10.1016/j.enconman.2017.02.013 ↗
50. Experimental application of mineral admixtures in lightweight concrete with high strength and workability10.1016/j.conbuildmat.2007.03.001 ↗
51. Mechanical characteristics of hardened concrete with different mineral admixtures: a review
52. The composition of fly ash glass phase and its dissolution properties applying to geopolymeric materials10.1111/j.1551-2916.2010.04337.x ↗
53. Effect of lime putty addition on structural and durability properties of concrete10.1016/S0008-8846(01)00744-X ↗
54. Utilization of limestone powder and water-reducing admixture in cemented paste backfill of coarse copper mine tailings10.1016/j.conbuildmat.2016.07.055 ↗
55. Effect of age on diffusion in hydrated alite cement10.1111/j.1151-2916.1984.tb18837.x ↗
56. Analytical study of pure and extended portland cement pastes: II, fly ash‐ and slag‐cement pastes10.1111/j.1151-2916.1985.tb10125.x ↗
57. A simultaneous semi-isothermal method of thermogravimetry and derivative thermogravimetry, and its application to cement pastes10.1016/0008-8846(77)90086-2 ↗
58. Influence of limestone on the hydration of Portland cements10.1016/j.cemconres.2008.01.002 ↗
59. Activation of fly ash cementitious systems in the presence of quicklime. Part II: nature of hydration products, porosity and microstructure development10.1016/j.cemconres.2006.09.013 ↗
60. Shiyuan · 1981
61. Pore structures of fly ashes activated by Ca(OH)2 and CaSO4 · 2H2O10.1016/0008-8846(95)00027-5 ↗
62. Glass phase structure of blast furnace slag10.4028/www.scientific.net/AMR.168-170.3 ↗
63. Discussion of C. Li et al.,“A review: the comparison between alkali-activated slag (Si+ Ca) and metakaolin (Si+ Al) cements10.1016/j.cemconres.2010.08.005 ↗
64. A review: the comparison between alkali-activated slag (Si+ Ca) and metakaolin (Si+ Al) cements10.1016/j.cemconres.2010.03.020 ↗
65. Experimental hydration of two synthetic glassy blast furnace slags in water and alkaline solutions (NaOH and KOH 0.1 N) at 40° C: structure, composition and origin of the hydrated layer10.1007/BF00638034 ↗