Coordinatively and Spatially Coconfining High-Loading Atomic Sb in Sulfur-Rich 2D Carbon Matrix for Fast K⁺ Diffusion and Storage

The atomically dispersed materials promise ultrafast redox kinetics for alkali-ion storage. However, their relatively low mass loading limits their application. Herein, well-dispersed Sb atoms with high-loading of 23.3 wt % anchored in sulfur-rich amorphous carbon-coated reduced graphene oxide matrix (SbSA/C) are prepared by a coordinative and spatial coconfinement methodology including freeze-casting the well-dissolved Sb-chelates (Sb-thioglycolate) within graphene oxide suspension and post heating-treatment. The reduced graphene oxide substrate features open two-dimensional spatial framework for loading atomically dispersive Sb species, and the pyrolyzed Sb-chelates would provide not only massive desirable heteroatoms (S, O) for coordinating the Sb atoms but also in situ pyrolytic carbon for further spatially separating those dispersive atoms. The coordinative and spatial coconfinement engineering also endows the SbSA/C composite with atomic-level Sb atoms against migration and agglomeration during electrochemical K-storage cycling. In situ TEM reveals the uniform potassiation behavior of the SbSA/C without obvious volume change; DFT calculation and electrochemical characterization suggest the significantly lower K-ion diffusion energy barrier. Therefore, on the basis of both the active Sb center and the coordinative heteroatom, the SbSA/C electrode delivers high fast-charging capacity, outstanding rate capability and long-lifespan performance in half/full K-ion batteries (e.g., a stable capacity of 331.3 mA h g–1 is maintained over 1100 cycles at 1.0 A g–1 for half-cell).