New intelligent multifunctional SiO₂/VO₂ composite films with enhanced infrared light regulation performance, solar modulation capability, and superhydrophobicity

Highly transparent, energy-saving, and superhydrophobic nanostructured SiO₂/VO₂ composite films have been fabricated using a sol-gel method. These composite films are composed of an underlying infrared (IR)-regulating VO₂ layer and a top protective layer that consists of SiO₂ nanoparticles. Experimental results showed that the composite structure could enhance the IR light regulation performance, solar modulation capability, and hydrophobicity of the pristine VO₂ layer. The transmittance of the composite films in visible region (T_lum) was higher than 60%, which was sufficient to meet the requirements of glass lighting. Compared with pristine VO₂ films and tungsten-doped VO₂ film, the near IR control capability of the composite films was enhanced by 13.9% and 22.1%, respectively, whereas their solar modulation capability was enhanced by 10.9% and 22.9%, respectively. The water contact angles of the SiO₂/VO₂ composite films were over 150°, indicating superhydrophobicity. The transparent superhydrophobic surface exhibited a high stability toward illumination as all the films retained their initial superhydrophobicity even after exposure to 365 nm light with an intensity of 160 mW ^. cm^-2 for 10 h. In addition, the films possessed anti-oxidation and anti-acid properties. These characteristics are highly advantageous for intelligent windows or solar cell applications, given that they can provide surfaces with anti-fogging, rainproofing, and self-cleaning effects. Our technique offers a simple and low-cost solution to the development of stable and visible light transparent superhydrophobic surfaces for industrial applications.