LVI and post-LVI mechanical degenerate behaviors of GFRP T-joint after seawater hydrothermal aging
Source abstract
Abstract
Abstract This paper aims to investigate the effect of seawater hydrothermal aging on the mechanical performance of the glass fiber reinforced polymer (GFRP) T-joint, fabricated via vacuum-assisted resin infusion (VARI) process, and which is a typical structure between the primary and secondary components in a ship structure. After subjecting the samples to hydrothermal aging at varying temperatures and durations, we conducted low-velocity impact (LVI) tests followed by post-LVI tensile tests with the help of self-designed fixtures and standard testing protocols. The results reveal the mechanical responses and failure morphology of the GFRP T-joints, thereby elucidating their failure mechanisms. The results show that the seawater hydrothermal environment of either higher temperature or longer duration could accelerate the aging. Moreover, compared to conventional hydrothermal aging, the seawater hydrothermal environment significantly reduces the performance of T-joint structures in both LVI and post-LVI tests.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Cellular and Composite Structures · Polymer crystallization and properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Civil and Architecture Engineering , Nanchang Institute of Technology , Nanchang , China
College of Aerospace and Civil Engineering , Harbin Engineering University , Harbin , China
Funding
Foundation of Jiangxi Province of China Educational Committee · The Innovative Projects of NIT
References (26)
Show source-provided references
1. Hosseini, A, Raji, A. Improved double impact and flexural performance of hybridized glass basalt fiber reinforced composite with graphene nanofiller for lighter aerostructures. Polym Test 2023;125:108107. https://doi.org/10.1016/j.polymertesting.2023.108107.10.1016/j.polymertesting.2023.108107 ↗
2. Nawawithan, N, Kittisakpairach, P, Nithiboonyapun, S, Ruangjirakit, K, Jongpradist, P. Design and performance simulation of hybrid hemp/glass fiber composites for automotive front bumper beams. Compos Struct 2024;335:118003. https://doi.org/10.1016/j.compstruct.2024.118003.10.1016/j.compstruct.2024.118003 ↗
3. Khan, SA, Koloor, SSR, Wong, KJ, Dickhut, T, Tamin, MN. An interlaminar fatigue damage model based on property degradation of carbon fiber-reinforced polymer composites. Eng Fract Mech 2024;302:110066. https://doi.org/10.1016/j.engfracmech.2024.110066.10.1016/j.engfracmech.2024.110066 ↗
4. Wang, J, Qin, T, Mekala, NR, Li, Y, Heidari-Rarani, M, Schröder, K. Three-dimensional progressive damage and failure analysis of double-lap composite bolted joints under quasi-static tensile loading. Compos Struct 2022;285:115227. https://doi.org/10.1016/j.compstruct.2022.115227.10.1016/j.compstruct.2022.115227 ↗
5. Kaybal, HB, Ulus, H, Eskizeybek, V, Avcı, A. An experimental study on low velocity impact performance of bolted composite joints-part 2: influence of long-term seawater aging. Compos Struct 2021;272:113571. https://doi.org/10.1016/j.compstruct.2021.113571.10.1016/j.compstruct.2021.113571 ↗
6. Cao, Z, Cardew-Hall, M. Interference-fit riveting technique in fiber composite laminates. Aerosp Sci Technol 2006;10:327–30. https://doi.org/10.1016/j.ast.2005.11.003.10.1016/j.ast.2005.11.003 ↗
7. Yang, J, Smith, ST, Wu, Y, Feng, P. Strengthening single-bolt timber joints with externally bonded CFRP composites. Structures 2020;28:2671–85. https://doi.org/10.1016/j.istruc.2020.10.024.10.1016/j.istruc.2020.10.024 ↗
8. Omairey, S, Jayasree, N, Kazilas, M. Defects and uncertainties of adhesively bonded composite joints. SN Appl Sci 2021;3:769. https://doi.org/10.1007/s42452-021-04753-8.10.1007/s42452-021-04753-8 ↗
9. Wan, Y, Liu, Y, Hu, C, Yao, J, Wang, F, Yang, B. Failure mechanism of curved composite laminates subjected to low-velocity impact. Acta Mech Sin 2023;39:1–11.10.1007/s10409-023-23113-x ↗
10. Xie, C, Wan, Y, Wang, L, Yu, X, Ma, Y. Experimental investigation on the compression-after double-impact behaviors of GFRP laminates embedded with aluminum mesh. Polym Compos 2025;46:2138–48. https://doi.org/10.1002/pc.29094.10.1002/pc.29094 ↗
11. Chen, Y, Wan, Y, Li, C, Zhang, J. Post-LVI tensile behavior of mechanical joint for GFRP/metal mesh hybrid laminate. Polym Compos 2025;46:7882–95. https://doi.org/10.1002/pc.29463.10.1002/pc.29463 ↗
12. Saeedifar, M, Mansvelder, J, Mohammadi, R, Zarouchas, D. Using passive and active acoustic methods for impact damage assessment of composite structures. Compos Struct 2019;226:111252. https://doi.org/10.1016/j.compstruct.2019.111252.10.1016/j.compstruct.2019.111252 ↗
13. Sasikumar, A, Trias, D, Costa, J, Blanco, N, Orr, J, Linde, P. Effect of ply thickness and ply level hybridization on the compression after impact strength of thin laminates. Compos A Appl Sci Manuf 2019;121:232–43. https://doi.org/10.1016/j.compositesa.2019.03.022.10.1016/j.compositesa.2019.03.022 ↗
14. Wan, Y, Wang, L, Liu, Y, Wu, Y. Experimental investigation on the low-velocity impact response and the residual strength of CFRP tubes. Polym Compos 2024;45:8677–93. https://doi.org/10.1002/pc.28368.10.1002/pc.28368 ↗
15. Wan, Y, Hu, W, Yang, B, Zhao, X, Xian, G, Yuan, Y, et al.. On-line tensile damage monitoring of WGF/epoxy T-joint by the embedded MWCNT@WGF sensor. Compos Commun 2021;23:100541. https://doi.org/10.1016/j.coco.2020.100541.10.1016/j.coco.2020.100541 ↗
16. Wan, Y, Tang, C, Jian, Z, Wang, F, Hu, C, Yang, B. Structural enhancement and repair of CFRP T-joint by the cross-embedded SMA wire. Compos Commun 2023;41:101634.10.1016/j.coco.2023.101634 ↗
17. Wu, Y, You, P, Xiong, J, Li, M, Wan, Y. An experimental study on the failure mechanism of local-strengthening glass fiber reinforced polymer T-joints under/after the low-velocity impact loading. Compos Mater 2023;57:4699–708. https://doi.org/10.1177/00219983231216435.10.1177/00219983231216435 ↗
18. Zhou, S, Jia, Y, Xu, L, Wang, L, Hui, L. Study on the damage behavior of carbon fiber composite after low-velocity impact under hydrothermal aging. Appl Polym Sci. 2020;138.10.1002/app.50289 ↗
19. Wang, K, Chen, Y, Long, H, Baghani, M, Rao, Y, Peng, Y. Hygrothermal aging effects on the mechanical properties of 3D printed composites with different stacking sequence of continuous glass fiber layers. Polym Test 2021;100:107242. https://doi.org/10.1016/j.polymertesting.2021.107242.10.1016/j.polymertesting.2021.107242 ↗
20. Guermazi, N, Ben Tarjem, A, Ksouri, I, Ayedi, HF. On the durability of FRP composites for aircraft structures in hydrothermal conditioning. Composites Part B 2016;85:294–304. https://doi.org/10.1016/j.compositesb.2015.09.035.10.1016/j.compositesb.2015.09.035 ↗
21. Zuo, W, Luo, Q, Li, Q, Sun, G. Effect of thermal and hydrothermal aging on the crashworthiness of carbon fiber reinforced plastic composite tubes. Compos Struct 2023;303:116136. https://doi.org/10.1016/j.compstruct.2022.116136.10.1016/j.compstruct.2022.116136 ↗
22. Krauklis, AE, Starkova, O, Gibhardt, D, Kalinka, G, Aouissi, HA, Burlakovs, J, et al.. Reversible and irreversible effects on the epoxy GFRP fiber–matrix interphase due to hydrothermal aging. Compos C Open Access 2023;12:100395. https://doi.org/10.1016/j.jcomc.2023.100395.10.1016/j.jcomc.2023.100395 ↗
23. Sang, L, Wang, Y, Wang, C, Peng, X, Hou, W, Tong, L. Moisture diffusion and damage characteristics of carbon fabric reinforced polyamide 6 laminates under hydrothermal aging. Compos A Appl Sci Manuf 2019;123:242–52. https://doi.org/10.1016/j.compositesa.2019.05.023.10.1016/j.compositesa.2019.05.023 ↗
24. Wu, Y, Gao, X, Li, M, Zou, T, Wang, F. Artificial seawater aging effects on residual compression strength of CFRP circular tubes subjected to low-velocity impact. Compos Mater 2025;59:189–215. https://doi.org/10.1177/00219983251357661.10.1177/00219983251357661 ↗
25. Liu, Y, Wu, Y. Influence of hydrothermal aging on the mechanical performance of foam core sandwich panels subjected to low-velocity impact. Sci Eng Compos Mater 2022;29:9–22. https://doi.org/10.1515/secm-2022-0003.10.1515/secm-2022-0003 ↗
26. Chen, H, Li, M, Shen, Z, Zhang, Y, Zhu, Y, Wu, Y. Experimental investigation on tensile behavior of CFRP bolted joints subjected to hydrothermal aging. E-Polymers 2024;24:20230183. https://doi.org/10.1515/epoly-2023-0183.10.1515/epoly-2023-0183 ↗