Effects of NiO content on the microstructure and mechanical properties of AgSnO 2 NiO composites
Source abstract
Abstract
Abstract The AgSnO 2 NiO composites were prepared by internal oxidation method. The effects of different NiO content on the microstructure and mechanical properties of AgSnO 2 NiO composites were studied. The phase structure and surface morphology of the prepared AgSnO 2 NiO materials were characterized by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Metallographic Microscopy (MM). The results showed that the AgSnO 2 NiO composites with different NiO content can be obtained by the process of preoxidation of AgSn alloy powder and internal oxidation of ingot containing Ni. The agglomeration phenomenon of Ni in the silver matrix was serious, which led to the agglomeration of in-situ generated NiO particles after internal oxidation. After the multi-pass drawing, the SnO 2 particles dispersedly distributed in the AgSnO 2 NiO composites and the NiO particles gradually dispersed from the agglomerated state of the sintered ingot billet. The hardness of the prepared AgSnO 2 NiO composites increased slightly with the increase of NiO content. The mechanical properties test showed that the introduction of NiO particles significantly improved the tensile strength and elongation of AgSnO 2 materials to a certain degree. Adding proper amount of NiO is beneficial to improve the overall performance of AgSnO 2 materials.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Electrical Contact Performance and Analysis · ZnO doping and properties · Gas Sensing Nanomaterials and Sensors
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Materials Science and Engineering, Kunming University of Science and Technology/Key Laboratory of Advanced Materials of Yunnan Province/Key Laboratory of Advanced Materials in Rare& Precious and Nonferrous Metals, Ministry of Education , Kunming , Yunnan, 650093 , China
Kunming Institute of Precious Metals , Kunming , Yunnan, 650106 , China
Guilin Key Laboratory of Microelectronic Electrode Materials and Biological Nanomaterials, China Nonferrous Metal (Guilin) Geology and Mining Co., Ltd , Guilin , 541004 , China
References (24)
Show source-provided references
1. Reti A. Silver: Alloying, Properties and Applications[J]. Encyclopedia of Materials Science & Technology, 2001, 23(1):8618-8621.10.1016/B0-08-043152-6/01536-9 ↗
2. Ommer M, Klotz U E, Fischer-Bühner J. Structure Characterization of Switched Ag–metal Oxide Contact Materials[J]. Materialwissenschaft Und Werkstofftechnik, 2008, 39(12):928-932.10.1002/mawe.20080040810.1002/mawe.200800408 ↗
3. Verma P, Pandey O P, Verma A. Influence of Metal Oxides on the Arc Erosion Behaviour of Silver Metal Oxides Electrical Contact Materials[J]. Journal of Materials Science & Technology, 2004, 20(1):49-52.
4. Nilsson O, Hauner F, Jeannot D. Replacement of AgCdO by AgSnO2 in DC Contactors[C]// Electrical Contacts, 2004. Proceedings of the IEEE Holm Conference on Electrical Contacts and the, International Conference on Electrical Contacts. IEEE, 2004:70-74.10.1109/HOLM.2004.1353097 ↗
5. Pons F, Cherkaoui M, IIali I. Evolution of the AgCdO Contact Material Surface Microstructure with the Number of Arcs[J]. Journal of Electronic Materials, 2010, 39(4):456-463.10.1007/s11664-010-1097-410.1007/s11664-010-1097-4 ↗
6. Zhu Y, Wang J, Wang H. Study on Arc Erosion Resistance Properties of Nano-AgSnO2 Electrical Contact Materials Doped with Bi[J]. Rare Metal Materials & Engineering, 2013, 42(1):149-152.
7. Wang Y, Li H. Improved Workability of the Nanocomposited AgSnO2 Contact Material and Its Microstructure Control During the Arcing Process[J]. Metallurgical And Materials Transactions A-Physical Metallurgy And Materials Science, 2016, 48:1-8.10.1007/s11661-016-3859-y ↗
8. Zhang M, Wang X H, Yang X H. Arc Erosion Behaviors of AgSnO2 Contact Materials Prepared with Different SnO2 Particle Sizes[J]. Transactions of Nonferrous Metals Society of China, 2016, 26(3):783-790.10.1016/S1003-6326(16)64168-710.1016/S1003-6326(16)64168-7 ↗
9. Wu C P, Yi D Q, Li J. Investigation on Microstructure and Performance of Ag/ZnO Contact Material[J]. Journal of Alloys & Compounds, 2008, 457(1–2):565-570.10.1016/j.jallcom.2007.03.09910.1016/j.jallcom.2007.03.099 ↗
10. Swingler J, Sumption A. Arc Erosion of AgSnO2 Electrical Contacts at Different Stages of a Break Operation[J]. Rare Metal Materials & Engineering, 2010, 29(3):248-254.10.1007/s12598-010-0043-110.1007/s12598-010-0043-1 ↗
11. DU, Zuojuan, YANG. Preparation of Silver Tin Oxide Powders by Hydrothermal Reduction and Crystallization[J]. Rare Metals, 2007, 26(5):470-475.10.1016/S1001-0521(07)60247-210.1016/S1001-0521(07)60247-2 ↗
12. Zhou X, Tao Q, Zhou Y. Microstructure and Properties of AgSnO2 Composites by Accumulative Roll-bonding Process[J]. Rare Metal Materials & Engineering, 2017, 46(4):942-945.10.1016/S1875-5372(17)30126-110.1016/S1875-5372(17)30126-1 ↗
13. Mcdonnell D. Comparison of the Switching Behavior of Internally Oxidized and Powder Metallurgical Silver Metal Oxide Contact Materials[C]// Electrical Contacts, 1994. Proceedings of the Fortieth IEEE Holm Conference on Electrical Contacts. IEEE, 1994:253-260.10.1109/HOLM.1994.636845 ↗
14. Wang S, Chen J, Zheng T. Influence of Preparation Technology on Microstructure and Properties of AgSnO2 (12) Electrical Contact Material[J]. Precious Metals, 2015, 36(4):32-36. (in Chinese)
15. Leung C, Streicher E, Fitzgerald D. Contact Erosion of Ag/SnO2/In2O3 Made by Internal Oxidation and Powder Metallurgy[C]// IEEE Holm Conference on. IEEE Xplore, 2005:22-27.
16. Jeannot D, Pinard J, Ramoni P. Physical and Chemical Properties of Metal Oxide Additions to Ag-SnO2 Contact Materials and Predictions of Electrical Performance[J]. IEEE Transactions on Components Packaging & Manufacturing Technology Part A, 1994, 17(1):17-23.10.1109/95.29636310.1109/95.296363 ↗
17. Chun-Ping WU, Dan-Qing YI, Weng W. Influence of Alloy Components on Arc Erosion Morphology of Ag/MeO Electrical Contact Materials[J]. Transactions of Nonferrous Metals Society of China, 2016, 26(1):185-195.10.1016/S1003-6326(16)64105-510.1016/S1003-6326(16)64105-5 ↗
18. Li G, Cui H, Chen J. Formation and Effects of CuO Nanoparticles on Ag/SnO2 Electrical Contact Materials[J]. Journal of Alloys & Compounds, 2017, 696.10.1016/j.jallcom.2016.12.092 ↗
19. Wang H, Wang J, Du J. Influence of Rare Earth on the Wetting Ability of AgSnO2Contact Material[J]. Rare Metal Materials & Engineering, 2014, 43(8):1846-1849.10.1016/S1875-5372(14)60143-010.1016/S1875-5372(14)60143-0 ↗
20. Wang J, Liu W, Li D. The Behavior and Effect of CuO in Ag/SnO2 Materials[J]. Journal of Alloys & Compounds, 2014, 588:378-383.10.1016/j.jallcom.2013.11.04010.1016/j.jallcom.2013.11.040 ↗
21. Chen J, Jia H, Zhu G. Observation on AgSnO2In2O3 Molten Bridge Phenomena under Different Currents[J]. Indian Journal of Engineering & Materials Sciences, 2017, 24(5):369-376.
22. Zhang L, Tao S, Shen Q. Anti-Arc Erosion Properties of Ag-La2Sn2O7/SnO2 Contacts[J]. Rare Metal Materials & Engineering, 2016.
23. Wu C, Yi D, Weng W. Arc Erosion Behavior of Ag/Ni Electrical Contact Materials[J]. Materials & Design, 2015, 85:511-519.10.1016/j.matdes.2015.06.14210.1016/j.matdes.2015.06.142 ↗
24. Wang S, Xie M, Liu M. Research Progress of AgNi Contact Materials[J]. Rare Metal Materials & Engineering, 2013.