Structure property correlations in wet-spun textile PAN fibers for cost-effective carbon fibers applicable in H2 storage tank manufacturing

The economic viability of high-strength carbon fibers is pivotal for their integration into Type IV compressed hydrogen storage tanks. Oak Ridge National Laboratory is advancing this objective by developing cost-effective, textile-grade polyacrylonitrile (PAN) precursor fibers through an optimized wet spinning-process to garner more microstructural control over the precursor fibers. This study examines the microstructural characteristics of PAN fibers, particularly the crystalline orientation factor, and their impact on mechanical properties in both precursor and thermally converted carbon fibers (CFs). Three wet-spun PAN fibers, all having diameters of 12-13 µm but varying orientation factors were assessed. Comprehensive characterization using X-ray scattering and microscopy revealed that fibers with higher orientation factors exhibited enhanced crystallinity and optimized crystallite sizes. Mechanical testing demonstrated that the PAN fiber with the highest orientation factor achieved the greatest tensile strength (98 ksi) and modulus (1.60 Msi). Additionally optical and scanning electron microscopy confirmed smooth and defect-free surfaces across all samples. These findings indicate that manipulating spinning parameters to maximize orientation factor is more impactful in achieving high strength and modulus over factors attributed to crystallinity and crystallite sizes. Here, highest performing CFs, thermally processed in lab from textile-grade precursor averaged 558 ksi, a 10% increase over previous results.