Rheology and Processing of High-Strength Liquid Crystal Polymer Reinforced Thermoplastic Composite Materials

Liquid crystal polymer (LCP) composites are presented as lightweight, high-strength, thermoplastic composites. Fumed silica (FS), carbon black (CB), carbon nanostructures (CNS), and boron nitride (BN) added to the polyphenylene sulfide (PPS) increased the viscosity ratio of the PPS to the LCP. PPS filled with 5 wt.% FS was used to optimize injection molding conditions and had a viscosity ratio ranging from 2 to 13. Increasing fill time to 5 s brought about the highest tensile strength of 99 MPa and modulus of 12.5 GPa, while the tool and melt temperatures imparted no significant effect. Mechanical and thermal properties of select LCP materials processed using molding conditions optimized for the experimental materials are presented. Mechanical properties in the crossflow direction were lower than in the flow direction, which could be overcome with tool design and placement of valve gates to tailor the flow patterns. BN filled composites increased the thermal conductivity to a value of 0.26 W/mK at 16 wt.% loading.