Enhancing frost resistance of alkali-activated slag concrete using surfactants: sodium dodecyl sulfate, sodium abietate, and triterpenoid saponins
Source abstract
Abstract
Abstract To investigate surfactants for enhancing the frost resistance of alkali-activated slag concrete (AASC), three surfactants were selected: Sodium Dodecyl Sulfate (SDS), Sodium Abietate (SA), and Triterpenoid Saponins (TS). The setting time of alkali-activated slag (AAS) was tested at surfactant dosages of 0.01 %, 0.03 %, 0.05 %, 0.07 %, and 0.09 %. The 28 days compressive strength, freeze-thaw resistance (mass loss, relative dynamic modulus of elasticity (RDME), and strength loss after 28 cycles), and water absorption were evaluated. The microstructure was observed using a scanning electron microscope, and the hole structure was analyzed using mercury intrusion porosimeter. The results indicate that all three surfactants reduce the initial setting time and increase the final setting time of AAS. When the dosage of TS is 0.01 %, the mass loss after 20 freeze-thaw cycles is reduced by 39.2 %, the RDME increases by 13.9 %, the water absorption rate is reduced by 50 %, and the compressive strength loss rate is reduced by 55.3 %. The incorporation of TS surfactants increases the number of closed micro-bubbles in the concrete, reduces the most probable hole size and average hole size, and decreases the proportion of large and harmful holes that improved the frost resistance of AASC.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Microbial Applications in Construction Materials · Concrete Properties and Behavior
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Civil Engineering and Geomatics , Shandong University of Technology , Zibo , 255000 , China
References (43)
Show source-provided references
1. Zhao, H, Jiang, K, Yang, R, Tang, Y, Liu, J. Experimental and theoretical analysis on coupled effect of hydration, temperature and humidity in early-age cement-based materials. Int J Heat Mass Tran 2020;146:118784. https://doi.org/10.1016/j.ijheatmasstransfer.2019.118784.10.1016/j.ijheatmasstransfer.2019.118784 ↗
2. Gartner, E. Industrially interesting approaches to “low-CO2” cements. Cem Concr Res 2004;34:1489–98. https://doi.org/10.1016/j.cemconres.2004.01.021.10.1016/j.cemconres.2004.01.021 ↗
3. Tong, S, Yuqi, Z, Qiang, WJ. Recent advances in chemical admixtures for improving the workability of alkali-activated slag-based material systems. Constr Build Mater 2021;272:121647. https://doi.org/10.1016/j.conbuildmat.2020.121647.10.1016/j.conbuildmat.2020.121647 ↗
4. Zhao, Z, Wang, S, Ren, J, Wang, Y, Wang, C. Fatigue characteristics and prediction of cement-stabilized cold recycled mixture with road-milling materials considering recycled aggregate composition. Constr Build Mater 2021;301:124122. https://doi.org/10.1016/j.conbuildmat.2021.124122.10.1016/j.conbuildmat.2021.124122 ↗
5. Awoyera, P, Adesina, A. A critical review on application of alkali activated slag as a sustainable composite binder. Case Stud Constr Mater 2019;11:e00268. https://doi.org/10.1016/j.cscm.2019.e00268.10.1016/j.cscm.2019.e00268 ↗
6. Luukkonen, T, Abdollahnejad, Z, Yliniemi, J, Kinnunen, P, Illikainen, M. One-part alkali-activated materials: a review. Cem Concr Res 2018;103:21–34. https://doi.org/10.1016/j.cemconres.2017.10.001.10.1016/j.cemconres.2017.10.001 ↗
7. Provis, JL. Alkali-activated materials. Cem Concr Res 2018;114:40–8. https://doi.org/10.1016/j.cemconres.2017.02.009.10.1016/j.cemconres.2017.02.009 ↗
8. Provis, JL, Palomo, A, Shi, C. Advances in understanding alkali-activated materials. Cem Concr Res 2015;78:110–25. https://doi.org/10.1016/j.cemconres.2015.04.013.10.1016/j.cemconres.2015.04.013 ↗
9. Duxson, P, Fernández-Jiménez, A, Provis, JL, Lukey, GC, Palomo, A, Van Deventer, JS. Geopolymer technology: the current state of the art. J Mater Sci 2007;42:2917–33. https://doi.org/10.1007/s10853-006-0637-z.10.1007/s10853-006-0637-z ↗
10. Marvila, MT, Azevedo, ARG, Vieira, CMF. Reaction mechanisms of alkali-activated materials. Rev IBRACON Estrut Mater 2021;14:e14309. https://doi.org/10.1590/S1983-41952021000300009.10.1590/s1983-41952021000300009 ↗
11. Yang, Z, Tang, W, Zhang, D, Zhang, J, Wang, K, Zhao, Z. Hydration mechanism of alkali-activated cementitious materials entirely prepared by solid wastes. J Build Eng 2024;97:110921. https://doi.org/10.1016/j.jobe.2024.110921.10.1016/j.jobe.2024.110921 ↗
12. Su, C, Zhang, J, Ding, Y. Research on reactivity evaluation and micro-mechanism of various solid waste powders for alkali-activated cementitious materials. Constr Build Mater 2024;411:134374. https://doi.org/10.1016/j.conbuildmat.2023.134374.10.1016/j.conbuildmat.2023.134374 ↗
13. Zhao, C, Wang, Z, Zhu, Z, Guo, Q, Wu, X, Zhao, R. Research on different types of fiber reinforced concrete in recent years: an overview. Constr Build Mater 2023;365:130075. https://doi.org/10.1016/j.conbuildmat.2022.130075.10.1016/j.conbuildmat.2022.130075 ↗
14. Rodrigue, A, Duchesne, J, Fournier, B, Bissonnette, B. Frost resistance of alkali-activated combined slag and fly ash concrete cured at ambient temperature. ACI Mater J 2022;119:3–13. https://doi.org/10.14359/51734600.10.14359/51734600 ↗
15. Zheng, X, Liu, F, Luo, T, Duan, Y, Yi, Y, Hua, C. Study on durability and hole characteristics of concrete under salt freezing environment. Materials 2021;14:7228. https://doi.org/10.3390/ma14237228.10.3390/ma14237228 ↗
16. Shang, HS, Yi, TH. Freeze-thaw durability of air-entrained concrete. Sci World J 2013;2013:650791. https://doi.org/10.1155/2013/650791.10.1155/2013/650791 ↗
17. Ke, G, Zhang, J, Tian, B, Wang, J. Characteristic analysis of concrete air entraining agents in different media. Cem Concr Res 2020;135:106142. https://doi.org/10.1016/j.cemconres.2020.106142.10.1016/j.cemconres.2020.106142 ↗
18. He, J, Gao, Q, Song, X, Bu, X, He, J. Effect of foaming agent on physical and mechanical properties of alkali-activated slag foamed concrete. Constr Build Mater 2019;226:280–7. https://doi.org/10.1016/j.conbuildmat.2019.07.302.10.1016/j.conbuildmat.2019.07.302 ↗
19. Sun, Q, Wei, X, Li, T, Zhang, L. Strengthening behavior of cemented paste backfill using alkali-activated slag binders and bottom ash based on the response surface method. Materials 2020;13:855. https://doi.org/10.3390/ma13040855.10.3390/ma13040855 ↗
20. Chen, Y, Al-Neshawy, F, Punkki, J. Investigation on the effect of entrained air on hole structure in hardened concrete using MIP. Constr Build Mater 2021;292:123441. https://doi.org/10.1016/j.conbuildmat.2021.123441.10.1016/j.conbuildmat.2021.123441 ↗
21. Li, M, Zhou, X, Zhao, J, Qu, S, Wang, P, Li, G. Preliminary exploration of a novel high-performance air entraining agent based on sodium dodecyl sulfate added self-made fluorocarbon surfactant. Constr Build Mater 2023;370:130564. https://doi.org/10.1016/j.conbuildmat.2023.130564.10.1016/j.conbuildmat.2023.130564 ↗
22. Peng, GF, Ma, Q, Hu, HM, Gao, R, Yao, QF, Liu, YF. The effects of air entrainment and pozzolans on frost resistance of 50-60 MPa grade concrete. Constr Build Mater 2007;21:1034–9. https://doi.org/10.1016/j.conbuildmat.2006.02.002.10.1016/j.conbuildmat.2006.02.002 ↗
23. Ouyang, X, Guo, Y, Qiu, X. The feasibility of synthetic surfactant as an air entraining agent for the cement matrix. Constr Build Mater 2008;22:1774–9. https://doi.org/10.1016/j.conbuildmat.2007.05.002.10.1016/j.conbuildmat.2007.05.002 ↗
24. Łaźniewska-Piekarczyk, B. The type of air-entraining and viscosity modifying admixtures and porosity and frost durability of high performance self-compacting concrete. Constr Build Mater 2013;40:659–71. https://doi.org/10.1016/j.conbuildmat.2012.11.032.10.1016/j.conbuildmat.2012.11.032 ↗
25. Deo, O, Neithalath, N. Compressive behavior of pervious concretes and a quantification of the influence of random hole structure features. Mater Sci Eng A 2010;528:402–12. https://doi.org/10.1016/j.msea.2010.09.024.10.1016/j.msea.2010.09.024 ↗
26. Tunstall, LE, Ley, MT, Scherer, GW. Air entraining admixtures: mechanisms, evaluations, and interactions. Cem Concr Res 2021;150:106557. https://doi.org/10.1016/j.cemconres.2021.106557.10.1016/j.cemconres.2021.106557 ↗
27. Feng, T, Yang, H, Zhang, J, Zong, C. Applicability of cationic surfactants, anionic surfactants, and nonionic surfactants as foaming agents for foamed concrete: surface activity, foamability, and interaction with cement. J Sustain Cem-Based Mater 2024;13:1330–47. https://doi.org/10.1080/21650373.2023.2292205.10.1080/21650373.2024.2379406 ↗
28. Chen, J, Qiao, M, Gao, N, Ran, Q, Wu, J, Shan, G, et al.. Cationic oligomeric surfactants as novel air entraining agents for concrete. Colloids Surf A Physicochem Eng Asp 2018;538:686–93. https://doi.org/10.1016/j.colsurfa.2017.11.065.10.1016/j.colsurfa.2017.11.065 ↗
29. Yan, DM, Ruan, SQ, Chen, SK, Liu, Y, Tian, Y, Wang, HL, et al.. Effects and mechanisms of surfactants on physical properties and microstructures of metakaolin-based geopolymer. J Zhejiang Univ - Sci 2021;22:130–46. https://doi.org/10.1631/jzus.A2000059.10.1631/jzus.A2000059 ↗
30. Sahu, SS, Gandhi, ISR. Studies on influence of characteristics of surfactant and foam on foam concrete behaviour. J Build Eng 2021;40:102333. https://doi.org/10.1016/j.jobe.2021.102333.10.1016/j.jobe.2021.102333 ↗
31. Zhang, J, Qi, Y, Lv, T, Niu, X, Tai, B. Effects of sodium dodecyl sulfate on nano carbon black-filled cement paste: performance and microstructure. J Mater Res Technol 2023;24:1706–15. https://doi.org/10.1016/j.jmrt.2023.03.055.10.1016/j.jmrt.2023.03.055 ↗
32. Wu, J. Study on the effect of different air-entraining agents on the properties of concrete. E3S Web Conf 2025;618:02001. https://doi.org/10.1051/e3sconf/202561802001.10.1051/e3sconf/202561802001 ↗
33. Li, Q, Ge, Y, Yang, W. Effect of sodium sulfate and sodium nitrite on air-void system in air-entrained concrete. Mag Concr Res 2016;68:1200–9. https://doi.org/10.1680/jmacr.15.00373.10.1680/jmacr.15.00373 ↗
34. Sun, C, Zhu, Y, Guo, J, Zhang, Y, Sun, G. Effects of foaming agent type on the workability, drying shrinkage, frost resistance and hole distribution of foamed concrete. Constr Build Mater 2018;186:833–9. https://doi.org/10.1016/j.conbuildmat.2018.08.019.10.1016/j.conbuildmat.2018.08.019 ↗
35. Hu, J, Zhao, F, Kuang, Y, Yang, D, Zheng, M, Zhao, L. Microscopic characteristics of the action of an air entraining agent on cemented paste backfill holes. Alexandria Eng J 2020;59:1583–93. https://doi.org/10.1016/j.aej.2020.04.005.10.1016/j.aej.2020.04.005 ↗
36. Yang, Q, Zhu, P, Wu, X, Huang, S. Properties of concrete with a new type of saponin air-entraining agent. Cem Concr Res 2000;30:1313–7. https://doi.org/10.1016/S0008-8846(00)00340-9.10.1016/S0008-8846(00)00340-9 ↗
37. Maglad, AM, Mydin, MAO, Datta, SD, Abbood, IS, Tayeh, BA. Impact of anionic surfactant-based foaming agents on the properties of lightweight foamed concrete. Constr Build Mater 2024;438:137119. https://doi.org/10.1016/j.conbuildmat.2024.137119.10.1016/j.conbuildmat.2024.137119 ↗
38. Wang, X, Wu, Y, Li, X, Li, Y, Tang, W, Dan, J, et al.. Effect of triterpenoid saponins as foaming agent on mechanical properties of geopolymer foam concrete. Materials 2024;17:3921. https://doi.org/10.3390/ma17163921.10.3390/ma17163921 ↗
39. Zhou, X, Bai, S, Zhou, X, Zhang, Y, Ding, Q. Effect of foaming characteristics of air entrained agents on mechanical properties and hole structures of cement-based materials in plateau mountainous regions. J Build Eng 2024;91:109590. https://doi.org/10.1016/j.jobe.2024.109590.10.1016/j.jobe.2024.109590 ↗
40. Hu, JH, Kuang, Y, Zhou, T, Zhao, F. Influence of air entraining agent on strength and microstructure properties of cemented paste backfill. IEEE Access 2019;7:140899–907. https://doi.org/10.1109/ACCESS.2019.2942360.10.1109/ACCESS.2019.2942360 ↗
41. Turkoglu, M, Bayraktar, OY, Benli, A, Kaplan, G. Effect of cement clinker type, curing regime and activator dosage on the performance of one-part alkali-activated hybrid slag/clinker composites. J Build Eng 2023;68:106164. https://doi.org/10.1016/j.jobe.2023.106164.10.1016/j.jobe.2023.106164 ↗
42. Bayraktar, OY, Kaplan, G, Benli, A. The effect of recycled fine aggregates treated as washed, less washed and unwashed on the mechanical and durability characteristics of concrete under MgSO4 and freeze-thaw cycles. J Build Eng 2022;45:103924. https://doi.org/10.1016/j.jobe.2021.103924.10.1016/j.jobe.2021.103924 ↗
43. Zhao, M, Dong, W. Grey relativity correlations between the hole structures and compressive strength of Aeolian sand concrete undergoing carbonation and freeze-thaw cycles. J Build Eng 2023;76:107515. https://doi.org/10.1016/j.jobe.2023.107515.10.1016/j.jobe.2023.107515 ↗