Weakening Ionic Coordination for High Ionic Conductivity Composite Solid Electrolytes
Source abstract
Abstract
High Resolution Image Download MS PowerPoint Slide The special chemistry of N,N-dimethylformamide (DMF)-solvated Li + [Li(DMF) x ] + migration results in polyvinylidene fluoride (PVDF)-based solid polymer electrolytes exhibiting high ionic conductivities. Incorporating ceramic fillers into PVDF electrolytes can further enhance the ionic conductivities. However, there is limited understanding of the desolvation process of Li + during its transport through the ceramic fillers. Herein, we reveal that this desolvation process exhibits a large energy barrier that hinders the Li + transport. The introduction of poly(methylhydrosiloxane) (PMHS) can weaken the ion–solvent coordination, forming loosely complexed [Li(DMF) x ] + and reducing their desolvation energy. This promotes rapid ceramic-involved Li + pathways, enabling the electrolyte with a high ambient ionic conductivity of 7.5 × 10 –4 S cm –1 . Moreover, the facile desolvation process can enhance the kinetics and reduce side reactions at the electrode/electrolyte interfaces. Therefore, solid-state Li–Li symmetric cells can operate for a record 11 800 h, and LiNi 0.8 Co 0.1 Mn 0.1 O 2 |Li solid-state batteries also demonstrated exceptional cycling stability for more than 2200 cycles at 2 C .
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced Battery Materials and Technologies · Advancements in Battery Materials · Thermal Expansion and Ionic Conductivity
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Mechanical Engineering, Imperial College London, London SW7 2AZ, United Kingdom.
Shenzhen Geim Graphene Center, Institute of Materials Research (IMR), Tsinghua Shenzhen International Graduate School, Tsinghua University, Shenzhen 518055, China
Department of Mechanical and Manufacturing Engineering, University of Cyprus, Nicosia 1678, Cyprus
Funding
Imperial College London · National Key Research and Development Program of China · National Natural Science Foundation of China
References (29)
Show source-provided references
1. 10.1038/natrevmats.2016.10310.1038/natrevmats.2016.103 ↗
2. 10.1016/j.nanoen.2017.01.02810.1016/j.nanoen.2017.01.028 ↗
3. 10.1002/idm2.1211110.1002/idm2.12111 ↗
4. 10.1002/aenm.20247000910.1002/aenm.202470009 ↗
5. 10.1038/1973010.1038/19730 ↗
6. 10.1038/3508753810.1038/35087538 ↗
7. 10.1016/S0013-4686(97)10168-210.1016/S0013-4686(97)10168-2 ↗
8. 10.1002/aenm.20210372010.1002/aenm.202103720 ↗
9. 10.1039/D3EE01696J10.1039/D3EE01696J ↗
10. 10.1002/anie.20070114410.1002/anie.200701144 ↗
11. 10.1002/adma.20220895110.1002/adma.202208951 ↗
12. 10.1016/j.ssi.2007.12.02210.1016/j.ssi.2007.12.022 ↗
13. 10.1002/adma.20190622110.1002/adma.201906221 ↗
14. 10.1021/acsenergylett.9b0169310.1021/acsenergylett.9b01693 ↗
15. 10.1021/acs.chemmater.6b0499010.1021/acs.chemmater.6b04990 ↗
16. 10.1021/acs.chemrev.9b0076010.1021/acs.chemrev.9b00760 ↗
17. 10.1002/advs.20190308810.1002/advs.201903088 ↗
18. 10.1038/s41467-024-45372-210.1038/s41467-024-45372-2 ↗
19. 10.1038/s41586-021-03885-610.1038/s41586-021-03885-6 ↗
20. 10.1021/jacs.7b0636410.1021/jacs.7b06364 ↗
21. 10.1002/adma.20180608210.1002/adma.201806082 ↗
22. 10.1002/anie.20211091710.1002/anie.202110917 ↗
23. 10.1016/j.ensm.2022.02.04810.1016/j.ensm.2022.02.048 ↗
24. 10.1038/s41565-023-01341-210.1038/s41565-023-01341-2 ↗
25. 10.1002/batt.20200008110.1002/batt.202000081 ↗
26. 10.1016/j.ensm.2022.06.04010.1016/j.ensm.2022.06.040 ↗
27. 10.1016/j.xcrp.2023.10138210.1016/j.xcrp.2023.101382 ↗
28. 10.1016/j.saa.2021.11949110.1016/j.saa.2021.119491 ↗
29. 10.1002/adma.20200002610.1002/adma.202000026 ↗