Corrosion resistance of CaO–Al2O3–SiO2 glasses used for flame spraying on concrete
Source abstract
Abstract
Concrete components can severely suffer from corrosion during their service lifetime. To achieve higher durability, glass coatings can be applied onto the concrete surface for protection purposes. Current solutions for protection measures are either sticking thin glass panes onto the concrete or applying plastic layers using flame spraying. The aim of this work was to develop an optimised glass composition for protective layers, in order to be suitable for flame spraying on concrete. The main advantage of this process is the deposition of continuous and joint-free glass layers onto complex geometries. Dense glass layers provide a much higher corrosion resistance and lifetime compared to polymer layers. The challenge encountered by these glass coatings resides in the contact with strong acidic fluids on one side and with the alkaline concrete on the other. Therefore, a new glass appropriate for flame spraying has been developed. The composition of this glass is cheaper compared to established reference glass products while providing comparable alkaline resistance. As the acid resistance of this glass is not sufficient, in order to ensure the desired requirements of an adequate corrosion protection, a multilayer glass coating was developed, in which the first layer consists of the alkaline-resistant CaO–Al2O3–SiO2 glass and the second layer of an acid-resistant glass.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Magnesium Oxide Properties and Applications · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
RWTH Aachen University Institute of Mineral Engineering
Funding
Deutsche Forschungsgemeinschaft
References (29)
Show source-provided references
1. 1. Bayer, E., Kampen, R., Bose, T. & Klose, N. Betonbauwerke in Abwasseranlagen – Planung, Bau, Instandhaltung, Fifth Edition, BetonMarketing Deutschland GmbH, Verlag Bau+Technik GmbH, Düsseldorf, 2011.
2. 2. Raupach, M. & Orlowsky, J. Erhaltung von Betonbauwerken – Baustoffe und ihre Eigenschaften, First Edition, Vieweg+Teubner, GWV Fachverlage GmbH, Wiesbaden, 2008.
3. 3. Breit, W. Säurewiderstand von Beton. In vdz Betontechnische Berichte 2001–2003, Ed. G. Thielen, Verlag Bau+Technik, Düsseldorf, 2004.
4. 4. Diepenseifen, M., Dietmar, H., Schultz, W. Beton mit hohem Widerstand gegen Säureangriff - auf Basis des Premium-Zements Dyckerhoff VARIODUR, In BetonWerk Int., 2008, 6.
5. 5. Taylor, H. F. W. Cement Chemistry, Second Edition, Thomas Telford Publishing, London, 1997.10.1680/cc.25929 ↗
6. 6. Phase Equilibria Diagrams. Database Version 4.0, American Ceramic Society, 2014.
7. 7. Moesgaard, M., Herfort, D., Skibsted, J. & Yue, Y. Calcium aluminosilicate glasses as supplementary cementitious materials. Glass Technol.: Eur. J. Glass Sci. Technol. A, 2010, 51 (5), 183–90.
8. 8. Moesgaard, M. Glass Particles as an Active and CO2 Reducing Component in Future Cement, PhD Dissertation, Aalborg Universitet, 2012.
9. 9. Dimbleby, V. & Turner, W. E. The relationship between chemical composition and the resistance of glasses to the action of chemical reagents. J. Soc. Glass Technol., 1926, 10, 304–58.
10. 10. Yale, B. Pilkington Brother Ltd. Improvements relating to glass compositions. 1971. GB000001389019A.
11. 11. Hellmann, K. Application-oriented glass development on the example of the system CaO–Al2O3–SiO2, Dissertation, Aachen, Universitätsbibliothek der RWTH Aachen, 2016.
12. 12. Conradt, R. Chemical durability of oxide glasses in aqueous solutions. A review. J. Am. Ceram. Soc., 2008, 91, 728–35.10.1111/j.1551-2916.2007.02101.x ↗
13. 13. Dahlmann, U. Zur Modellierung der chemischen Beständigkeit von oxidischen Gläsern, Dissertation, Aachen, Logos Verlag Berlin, 2002.
14. 14. Conradt, R. Chemische Beständigkeit. Physikalische und chemische Eigenschaften von Gläsern und Glasschmelzen. Werkstoffdaten für die Praxis, Fortbildungskurs, Hüttentechnische Vereinigung der Deutschen Glasindustrie, 2009.
15. 15. Scholze, H. Glass: Nature, Structure, and Properties, Springer-Verlag, Berlin, 1988.
16. 16. Das, C. R. Diffusion-controlled attack of glass surfaces by aqueous solutions. J. Am. Ceram.Soc., 1980, 63, 160–5.10.1111/j.1151-2916.1980.tb10683.x ↗
17. 17. Scholze, H. Bedeutung der ausgelaugten Schicht für die chemische Beständigkeit: Untersuchungen an einem Kalk-Natronsilicatglas. Glastech. Ber., 1985, 58 (5), 116–24.
18. 18. Conradt, R. Thermochemistry and Structure of Oxide Glasses. Analysis of the Composition and Structure of Glass and Glass Ceramics, Eds H. Bach & D. Krause, Springer, 1999.
19. 19. Bergeron, C. G., Risbud, S. H., Bereron, C. G. Introduction to Phase Equilibria in Ceramics, American Ceramic Society, 2004.
20. 20. Conradt, R. Chemical structure, medium range order, and crystalline reference state of multicomponent oxide liquids and glasses. J. Non-Cryst. Solids, 2004, 345–6, 16–23.10.1016/j.jnoncrysol.2004.07.038 ↗
21. 21. Philipps, K. Konzeption hochmoduliger Gläser mittels thermodynamischer und strukturchemischer Methoden, Dissertation, Aachen, Universitätsbibliothek der RWTH Aachen, 2018.
22. 22. Kölker, K. A systematic approach to fibre glass development, Dissertation, Aachen, Universitätsbibliothek der RWTH Aachen, 2017.
23. 23. FactSage. Thermafact and GTT-Technologies, Aachen, Germany, Montreal, Canada, 2004.
24. 24. Wallenberger, F. T., Hicks, R. J., Sincic, P. N. & Bierhals, A. T. New environmentally and energy friendly fiberglass compositions (E glass, ECR glass, C glass and A glass) – advances since 1998. Glass Technol.: Eur. J. Glass Science Technol. A, 2007, 48 (6) 305–15.10.1007/978-1-4419-0736-3_2 ↗
25. 25. Scholze, H., Conradt, R., Engelke, H. & Roggendorf, H. Determination of the corrosion mechanisms of high-level waste containing glass. MRS Proc., 1981, 11, 466.10.1557/proc-11-173 ↗
26. 26. Groß, S.-M. Zur hydrolytischen Beständigkeit von Glas in wässrigen Lösungen bei Anwesenheit von organischen Säuren, Dissertation, Aachen, Mensch-und-Buch-Verlag, Berlin, 2003.
27. 27. Wasserbeständigkeit von Glasgrieß bei 98°C. Deutsches Institut für Normung e.V, 1989, DIN ISO 719.10.31030/2330592 ↗
28. 28. Jantzen, C. M. & Plodinec, M. J. Thermodynamic model of natural, medieval and nuclear waste glass durability. J. Non-Cryst. Solids, 1984, 67 (1–3), 207–30.10.1016/0022-3093(84)90151-0 ↗
29. 29. Djambazov, P. Theoretische und experimentelle Untersuchungen der Frühstadien bei der wässrigen Korrosion von Silicatgläsern, Dissertation, Aachen, Universitätsbibliothek der RWTH Aachen, 2014.