Faulted defects in γ-brass-type alloys

The nature of faulted defects observed in thin foils of γ-brass-type alloys is determined by the image-matching technique. The defects occur on a wide range of planes; are prismatic with vacancy character, and have Burgers vectors of the types n 〈111〉 and m 〈110〉 where n and m are approximately 0.175 → 0.1875 and 0.350 → 0.375, respectively. These Burgers vectors are in good agreement with an analysis of likely partial dislocations in the γ-brass lattice based upon maintaining the tetrahedral configurations of all atoms in the γ-brass structure. It is proposed that the vacancies required for defect formation arise from oxidation of the thin foils. Die Art der Stapelfehler, die in dünnen Schichten von γ-Mesing-Legierungen beobachtet werden, wird durch Bild-Anpassungstechnik bestimmt. Die Defekte treten auf einem weiten Bereich von Ebenen auf, sind prismatisch mit Leerstellencharakter und besitzen Burgersvektoren vom Typ n 〈111〉 und m 〈110〉, wobei n und m näherungsweise 0,175 → 0,1875 bzw. 0,350 → 0,375 ist. Die Burgersvektoren sind in guter Übereinstimmung mit einer Analyse von wahrscheinlich Teilversetzungen im γ-Messinggitter, die auf der Aufrechterhaltung der Tetraederkonfigurationen aller Atome in der γ-Messingstruktur beruht. Es wird angenommen, daß die für die Defektbildung erforderlichen Leerstellen von der Oxidation der dünnen Schichten herrühren.