Enhanced Anticorrosion, Antifouling, and Tribological Properties of PANI Composite Coating Reinforced by PVA, 2-Aminophenol, and Acrylic to Fabricate Sustainable Passive Film on 304 SS
Source abstract
Abstract
An anti-corrosion and electroactive coating of PANI/PVA was electrodeposited on the 304 SS to improve the interface passive film. However, due to poor physical stability and tribological properties, PANI/PVA is copolymerized by various amounts (0.25–1 M) of 2-aminophenol (2-AP) and covered by a thin layer of acrylic (AC). According to the results, not only is the corrosion resistance of PANI/PVA/AP@AC about 100 times higher than PANI/PVA in 3.5 wt % NaCl (EIS), but its wear rate has also decreased by ∼60% (pin-on-disk). Moreover, the friction coefficient of PANI/PVA/AP@AC has increased by 40% compared to PANI/PVA. The adhesion energy of PANI/PVA/AP@AC to the substrate is ∼34% higher than that of PANI/PVA (pull-off). In addition, the nickel content of passive film under PANI/PVA/AP@AC reached 4.7% from ∼0% for PANI/PVA (EDS). The defect density of the passive film decreased ∼100 times by increasing the concentration of 2-AP to 1 M (Mott–Schottky). Moreover, uncoated 304 SS was protected galvanically with SS@PANI/PVA/AP@AC (with noise corrosion resistance of R n ∼ 10 6 Ω according to the galvanic corrosion evaluation). Finally, PANI/PVA/AP@AC remained intact after 160 h of immersion in the NaCl, and its potential reached +200 mV (electrochemical potentiometry). Therefore, PANI/PVA/AP@AC as a hybrid composite coating can sustain in situ anodic protection of 304 SS under harsh environmental conditions.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Conducting polymers and applications · Advanced Sensor and Energy Harvesting Materials · Tribology and Wear Analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran 159163-4311, Iran
Department of Materials Science and Engineering, University of Sheffield, Sheffield S1 3JD, United Kingdom
References (37)
Show source-provided references
1. 10.1021/acsapm.3c0234710.1021/acsapm.3c02347 ↗
2. 10.1016/j.jiec.2023.08.04010.1016/j.jiec.2023.08.040 ↗
3. 10.1021/acs.langmuir.4c0171810.1021/acs.langmuir.4c01718 ↗
4. 10.1016/j.porgcoat.2013.11.00210.1016/j.porgcoat.2013.11.002 ↗
5. 10.1016/j.porgcoat.2020.10590810.1016/j.porgcoat.2020.105908 ↗
6. 10.1021/acsapm.3c0294410.1021/acsapm.3c02944 ↗
7. 10.1016/j.cej.2021.13054010.1016/j.cej.2021.130540 ↗
8. 10.1016/j.porgcoat.2022.10683510.1016/j.porgcoat.2022.106835 ↗
9. 10.1016/j.corsci.2022.11069610.1016/j.corsci.2022.110696 ↗
10. 10.1016/j.corsci.2020.10909410.1016/j.corsci.2020.109094 ↗
11. 10.1021/acsami.3c0346110.1021/acsami.3c03461 ↗
12. 10.1080/01694243.2023.227464510.1080/01694243.2023.2274645 ↗
13. 10.1016/j.porgcoat.2023.10755910.1016/j.porgcoat.2023.107559 ↗
14. 10.1016/j.porgcoat.2023.10747210.1016/j.porgcoat.2023.107472 ↗
15. 10.1016/j.porgcoat.2023.10767110.1016/j.porgcoat.2023.107671 ↗
16. 10.1007/s40544-022-0638-110.1007/s40544-022-0638-1 ↗
17. 10.1016/j.apsusc.2022.15415610.1016/j.apsusc.2022.154156 ↗
18. 10.1016/j.corsci.2023.11131810.1016/j.corsci.2023.111318 ↗
19. 10.1016/j.apsusc.2018.10.27710.1016/j.apsusc.2018.10.277 ↗
20. 10.1016/j.eurpolymj.2022.11171410.1016/j.eurpolymj.2022.111714 ↗
21. 10.1016/j.rineng.2023.10125010.1016/j.rineng.2023.101250 ↗
22. 10.1016/j.conbuildmat.2021.12613610.1016/j.conbuildmat.2021.126136 ↗
23. 10.1016/j.porgcoat.2022.10671810.1016/j.porgcoat.2022.106718 ↗
24. 10.1016/j.cej.2019.02.06410.1016/j.cej.2019.02.064 ↗
25. 10.1016/j.cej.2022.13782110.1016/j.cej.2022.137821 ↗
26. 10.1016/j.corsci.2019.10824610.1016/j.corsci.2019.108246 ↗
27. 10.1016/j.cej.2022.13576510.1016/j.cej.2022.135765 ↗
28. 10.1016/j.cej.2023.14186110.1016/j.cej.2023.141861 ↗
29. 10.1016/j.cej.2023.14592710.1016/j.cej.2023.145927 ↗
30. 10.1021/acs.iecr.0c0287610.1021/acs.iecr.0c02876 ↗
31. 10.1016/j.cej.2023.14148110.1016/j.cej.2023.141481 ↗
32. 10.1016/j.cej.2020.12467510.1016/j.cej.2020.124675 ↗
33. 10.1016/j.jiec.2023.03.01510.1016/j.jiec.2023.03.015 ↗
34. 10.1016/j.porgcoat.2020.10575010.1016/j.porgcoat.2020.105750 ↗
35. 10.1016/j.jcis.2023.12.14310.1016/j.jcis.2023.12.143 ↗
36. 10.1016/j.electacta.2013.10.06210.1016/j.electacta.2013.10.062 ↗
37. 10.1016/j.jelechem.2022.11666510.1016/j.jelechem.2022.116665 ↗