Carbon Molecular Sieve Membranes from Multiring Highly Aromatic Functional Copolymers

Jesús Ortiz-Espinoza, María Isabel Loría-Bastarrachea, Olivia Hernández-Cruz, Carla Aguilar-Lugo, Ángel de Jesus Montes-Luna, Mikhail Zolotukhin, Francisco Alberto Ruiz-Treviño, Manuel Aguilar-Vega

ACS Applied Polymer Materials· Volume 6· Issue 2
Publisher page

Abstract

A linear, highly aromatic, random (50/50 mol %), film-forming copolymer was synthesized by a one-pot, metal-free, superacid-catalyzed reaction of isatin with multiring aromatic compounds aceanthrenequinone and p- terphenyl ( CP - NH ). The chemical modification of the copolymer by the reaction of the side oxindole groups with 1-(bromoacetyl)pyrene and tert -butyl bromoacetate afforded copolymers containing thermolabile tert -butyl acetate ( CP-Tba ) and acetyl pyrene ( CP - Prn ) moieties. The polymers obtained were completely soluble in common organic solvents NMP, DMF, and THF, and flexible transparent films could be cast from the solutions. Spectroscopic characterization corroborated the structure of the copolymers. Nonporous films from the CP-NH copolymer show high thermal resistance with onset of decomposition, T d, above 500 °C. Substitution of tert -butyl acetate and acetyl pyrene groups in the copolymer increases density and diminishes FFV. Pure gas permeability coefficients are larger for CP-NH and lower for CP-Prn in agreement with FFV. A mixed gas permeability test for a binary gas sample CO 2 /CH 4 (10/90 mol %) shows that P CO2 and P CH4 decrease compared to pure gases and also decrease with increasing pressure. Carbon molecular sieve membranes (CMSMs) prepared from film precursors CP-NH, CP-Tba, and CP-Prn at a 600 °C final temperature show at least 1 order of magnitude increase in pure gas permeability and around 2 times increase in selectivity for gas pairs O 2 /N 2, CO 2 /CH 4, and N 2 /CH 4 . The tert -butyl acetate and acetyl pyrene substitutions in the copolymer precursor increase gas permeability and increase selectivity in CMS membranes. As a result, the performance of pyrolyzed CP-NH, CP-Tba, and CP-Prn CMS membranes is similar to that of other CMSMs reported in the literature in terms of permeability and selectivity.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Membrane Separation and Gas Transport · Muon and positron interactions and applications · Covalent Organic Framework Applications

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Unidad de Materiales, Laboratorio de Membranas, Centro de Investigación Científica de Yucatán A.C., Calle 43 × 32 y 34, Chuburná de Hidalgo, 97205 Mérida, Yucatán, México

Instituto de Investigación en Materiales, Universidad Nacional Autónoma de México, Apartado Postal 70-360, CU Coyoacán, 04510 México D.F., México

Departamento de Ingeniería y Ciencias Químicas, Universidad Iberoamericana, Prol. Paseo de la Reforma No. 880, 01219 México D.F., México

Funding

Direcci?n General de Asuntos del Personal Acad?mico, Universidad Nacional Aut?noma de M?xico · Consejo Nacional de Ciencia y Tecnolog?a

References (44)

Show source-provided references
1. 10.1021/ma501488s10.1021/ma501488s ↗
2. 10.1126/science.aba980610.1126/science.aba9806 ↗
3. 10.1038/nmat480510.1038/nmat4805 ↗
4. 10.1016/j.polymer.2020.12217010.1016/j.polymer.2020.122170 ↗
5. 10.1016/j.polymer.2018.01.01310.1016/j.polymer.2018.01.013 ↗
6. 10.1016/j.memsci.2008.04.03010.1016/j.memsci.2008.04.030 ↗
7. 10.1039/C9EE01384A10.1039/C9EE01384A ↗
8. 10.3390/membranes903004110.3390/membranes9030041 ↗
9. 10.1016/j.memsci.2013.08.04910.1016/j.memsci.2013.08.049 ↗
10. 10.1016/j.seppur.2014.01.01210.1016/j.seppur.2014.01.012 ↗
11. 10.1016/S0008-6223(02)00309-310.1016/S0008-6223(02)00309-3 ↗
12. Saufi S. M. · Songklanakarin J. Sci. Technol. · 2002 · 24 · 843
13. 10.1016/S1387-1811(98)00204-210.1016/S1387-1811(98)00204-2 ↗
14. 10.1016/j.carbon.2006.10.01710.1016/j.carbon.2006.10.017 ↗
15. 10.1016/j.carbon.2017.11.03110.1016/j.carbon.2017.11.031 ↗
16. 10.1016/j.memsci.2019.11770310.1016/j.memsci.2019.117703 ↗
17. 10.1021/ma101048z10.1021/ma101048z ↗
18. 10.1021/acs.iecr.8b0273510.1021/acs.iecr.8b02735 ↗
19. 10.1021/acs.iecr.8b0052910.1021/acs.iecr.8b00529 ↗
20. 10.1021/ma502288d10.1021/ma502288d ↗
21. 10.1002/polb.1071710.1002/polb.10717 ↗
22. 10.1002/polb.1993.09031111610.1002/polb.1993.090311116 ↗
23. 10.1016/j.memsci.2010.11.02810.1016/j.memsci.2010.11.028 ↗
24. 10.1016/j.memsci.2018.05.05410.1016/j.memsci.2018.05.054 ↗
25. 10.1016/j.carbon.2017.01.01510.1016/j.carbon.2017.01.015 ↗
26. 10.1016/j.cryogenics.2017.04.00110.1016/j.cryogenics.2017.04.001 ↗
27. 10.1016/j.jfluchem.2008.09.01110.1016/j.jfluchem.2008.09.011 ↗
28. 10.3390/membranes1007014110.3390/membranes10070141 ↗
29. 10.1039/C7RA11710H10.1039/C7RA11710H ↗
30. Van Krevelen D. W. · 200910.1016/B978-0-08-054819-7.00001-7 ↗
31. 10.1002/cssc.20200156710.1002/cssc.202001567 ↗
32. 10.1007/s12678-018-0478-y10.1007/s12678-018-0478-y ↗
33. 10.1016/j.jiec.2018.06.03110.1016/j.jiec.2018.06.031 ↗
34. 10.1149/2.079207jes10.1149/2.079207jes ↗
35. 10.1039/C6RA26137J10.1039/C6RA26137J ↗
36. 10.1016/j.memsci.2013.07.05710.1016/j.memsci.2013.07.057 ↗
37. 10.1002/(SICI)1099-0488(20000115)38:2<273::AID-POLB1>3.0.CO;2-X10.1002/(SICI)1099-0488(20000115)38:2<273::AID-POLB1>3.0.CO;2-X ↗
38. 10.1002/(SICI)1099-0488(20000201)38:3<415::AID-POLB8>3.0.CO;2-Z10.1002/(SICI)1099-0488(20000201)38:3<415::AID-POLB8>3.0.CO;2-Z ↗
39. 10.2516/ogst:200102110.2516/ogst:2001021 ↗
40. 10.1016/j.polymer.2017.06.00610.1016/j.polymer.2017.06.006 ↗
41. 10.1016/j.memsci.2023.12157010.1016/j.memsci.2023.121570 ↗
42. 10.1016/j.carbon.2015.09.00510.1016/j.carbon.2015.09.005 ↗
43. 10.1039/c3py00451a10.1039/c3py00451a ↗
44. 10.1021/ma500922610.1021/ma5009226 ↗