Enhancement of Thermal Performance of Composite Phase Change Materials by Graphite In Situ Modified Al2O3 Porous Support
Source abstract
Abstract
Three-dimensionally connected, pore-adjustable, high-porosity Al 2 O 3 foam (AF) and graphite in situ modified Al 2 O 3 foams (GAFs) were prepared by using the particle-stabilized emulsion as a template. A graphite layer was coated on the surface of Al 2 O 3 particles by using sucrose as a carbon resource, preventing PEG leakage and improving the thermal conductivity. After encapsulating PEG with AF and GAF, we obtained a series of stabilized composite phase change materials (sPCMs). The melting enthalpy of PGAF can reach up to 152.4, which is 27.2% higher than that of PAF. The thermal conductivity of PGAF 30 is 0.79 W/(m K), which is 1.47 times that of PEG, and the light-to-heat conversion efficiency can reach 81.31%. The prepared sPCM has broad application prospects in solar energy utilization, waste heat recovery, building energy saving, and power peak regulation.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Phase Change Materials Research · Solar Thermal and Photovoltaic Systems · Adsorption and Cooling Systems
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Beijing Key Laboratory of Materials Utilization of Nonmetallic Minerals and Solid Wastes, National Laboratory of Mineral Materials, School of Materials Science and Technology, China University of Geosciences, Beijing 100083, P. R. China
Institute of Circular Economy, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100124, P. R. China
Institute of Analysis and Testing, Beijing Academy of Science and Technology (Beijing Center for Physical & Chemical Analysis), Beijing 100089, P. R. China
Funding
National Natural Science Foundation of China · Beijing University of Technology · Beijing Municipal Reform and Development Project
References (51)
Show source-provided references
1. 10.1016/j.energy.2018.04.12810.1016/j.energy.2018.04.128 ↗
2. 10.1016/j.applthermaleng.2018.04.12210.1016/j.applthermaleng.2018.04.122 ↗
3. 10.1016/j.enbuild.2017.08.03710.1016/j.enbuild.2017.08.037 ↗
4. 10.1016/j.apenergy.2012.03.05810.1016/j.apenergy.2012.03.058 ↗
5. 10.1016/j.enconman.2016.02.04510.1016/j.enconman.2016.02.045 ↗
6. 10.1016/j.enbuild.2012.12.04210.1016/j.enbuild.2012.12.042 ↗
7. 10.1021/acs.energyfuels.3c0026610.1021/acs.energyfuels.3c00266 ↗
8. 10.1016/j.coco.2023.10161410.1016/j.coco.2023.101614 ↗
9. 10.1016/j.apenergy.2022.12037510.1016/j.apenergy.2022.120375 ↗
10. 10.1016/j.rser.2020.11025910.1016/j.rser.2020.110259 ↗
11. 10.1016/j.rser.2020.11013510.1016/j.rser.2020.110135 ↗
12. 10.1016/j.pmatsci.2014.03.00510.1016/j.pmatsci.2014.03.005 ↗
13. 10.1016/j.carbon.2015.03.00910.1016/j.carbon.2015.03.009 ↗
14. 10.1016/j.solmat.2014.08.01710.1016/j.solmat.2014.08.017 ↗
15. 10.1016/j.nanoen.2015.11.00110.1016/j.nanoen.2015.11.001 ↗
16. 10.1016/j.enconman.2015.01.08410.1016/j.enconman.2015.01.084 ↗
17. 10.1016/j.solmat.2010.09.03310.1016/j.solmat.2010.09.033 ↗
18. 10.1016/j.carbon.2015.03.00910.1016/j.carbon.2015.03.009 ↗
19. 10.1016/j.carbon.2015.10.08210.1016/j.carbon.2015.10.082 ↗
20. 10.1016/j.enconman.2014.04.00210.1016/j.enconman.2014.04.002 ↗
21. 10.1016/j.apenergy.2015.05.04210.1016/j.apenergy.2015.05.042 ↗
22. 10.1016/j.solmat.2015.01.02710.1016/j.solmat.2015.01.027 ↗
23. 10.1039/C5TA00309A10.1039/C5TA00309A ↗
24. 10.1016/j.cej.2016.03.06810.1016/j.cej.2016.03.068 ↗
25. 10.1016/j.rser.2015.04.04410.1016/j.rser.2015.04.044 ↗
26. 10.1016/j.rser.2012.01.01510.1016/j.rser.2012.01.015 ↗
27. 10.1016/j.apenergy.2015.09.06910.1016/j.apenergy.2015.09.069 ↗
28. 10.1016/j.cej.2015.04.07710.1016/j.cej.2015.04.077 ↗
29. 10.1016/j.solmat.2014.11.00110.1016/j.solmat.2014.11.001 ↗
30. 10.1016/j.enconman.2015.03.07110.1016/j.enconman.2015.03.071 ↗
31. 10.1016/j.apenergy.2013.01.00510.1016/j.apenergy.2013.01.005 ↗
32. 10.1016/j.matchemphys.2007.12.01610.1016/j.matchemphys.2007.12.016 ↗
33. 10.1016/j.enconman.2014.11.04010.1016/j.enconman.2014.11.040 ↗
34. 10.1016/j.energy.2010.09.04610.1016/j.energy.2010.09.046 ↗
35. 10.1016/j.cej.2012.11.07710.1016/j.cej.2012.11.077 ↗
36. 10.1002/adma.20180175410.1002/adma.201801754 ↗
37. 10.1039/D2TA05582A10.1039/D2TA05582A ↗
38. 10.1016/j.solmat.2012.05.03110.1016/j.solmat.2012.05.031 ↗
39. 10.1016/j.carbon.2016.01.06310.1016/j.carbon.2016.01.063 ↗
40. 10.1016/j.pnsc.2012.05.00410.1016/j.pnsc.2012.05.004 ↗
41. 10.1016/j.enbuild.2013.12.02810.1016/j.enbuild.2013.12.028 ↗
42. 10.1016/j.apenergy.2016.03.01010.1016/j.apenergy.2016.03.010 ↗
43. 10.1007/s40145-016-0187-z10.1007/s40145-016-0187-z ↗
44. 10.1016/j.ceramint.2016.02.06910.1016/j.ceramint.2016.02.069 ↗
45. 10.1021/la00009a04910.1021/la00009a049 ↗
46. 10.1016/j.colsurfa.2012.02.05510.1016/j.colsurfa.2012.02.055 ↗
47. 10.1016/j.cis.2021.10237710.1016/j.cis.2021.102377 ↗
48. 10.1021/acssuschemeng.7b0088910.1021/acssuschemeng.7b00889 ↗
49. 10.1016/j.energy.2014.05.04910.1016/j.energy.2014.05.049 ↗
50. 10.1016/j.energy.2020.11958810.1016/j.energy.2020.119588 ↗
51. 10.1016/j.enbuild.2013.07.05610.1016/j.enbuild.2013.07.056 ↗