Low-Temperature-Toughened Polypropylene Blends with Highly Packed Elastomeric Domains
Source abstract
Abstract
Despite its versatility, the use of polypropylene (PP) has been limited to subzero temperature applications owing to its inherent brittleness at low temperatures. Herein, we introduce a PP ternary blend toughened by tailoring the domains of ethylene-propylene rubber (EPR) and poly(ethylene-co-octene) (EOC) within a PP matrix. The PP ternary blend was fabricated by melt-blending a PP and EOC binary mixture; a PP copolymer (PPC) was used as an additive. The Izod impact strength of the PP ternary blends dramatically increased between −50–20 °C compared to that of the iPP/EOC binary blend. Particularly, PP ternary blends with specific compositions exhibited impact strengths above 70 kJ/m2 even at −40 °C. The retraction rate of these blends was similar to that of high-performance specialty rubbers. Moreover, the blends exhibited a low brittleness temperature of −72.9 °C and, hence, may replace the expensive rubber products currently used for various low-temperature applications.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Polymer crystallization and properties · Polymer Nanocomposites and Properties · biodegradable polymer synthesis and properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Insulation Materials Research Center, Korea Electrotechnology Research Institute (KERI), Changwon 51543, Korea
Electro-Functional Materials Engineering, University of Science and Technology (UST), Changwon 51543, Korea
Funding
Korea Electrotechnology Research Institute
References (35)
Show source-provided references
1. 10.1038/211514a010.1038/211514a0 ↗
2. 10.1021/ma100209d10.1021/ma100209d ↗
3. 10.1021/ja063464r10.1021/ja063464r ↗
4. 10.1126/science.aah574410.1126/science.aah5744 ↗
5. 10.1021/ma900126910.1021/ma9001269 ↗
6. 10.1016/s0032-3861(02)00590-610.1016/s0032-3861(02)00590-6 ↗
7. 10.1002/app.205710.1002/app.2057 ↗
8. 10.1016/j.polymer.2004.10.03010.1016/j.polymer.2004.10.030 ↗
9. 10.1002/(sici)1097-4628(20000711)77:2<409::aid-app18>3.0.co;2-n10.1002/(sici)1097-4628(20000711)77:2<409::aid-app18>3.0.co;2-n ↗
10. 10.1021/acs.macromol.7b0055010.1021/acs.macromol.7b00550 ↗
11. 10.1002/app.206610.1002/app.2066 ↗
12. 10.1016/s0032-3861(99)00747-810.1016/s0032-3861(99)00747-8 ↗
13. 10.1021/acs.macromol.0c0032810.1021/acs.macromol.0c00328 ↗
14. 10.1016/j.polymer.2014.08.01210.1016/j.polymer.2014.08.012 ↗
15. 10.1021/ma990522310.1021/ma9905223 ↗
16. 10.1002/app.2464410.1002/app.24644 ↗
17. 10.1016/j.polymer.2003.12.08310.1016/j.polymer.2003.12.083 ↗
18. 10.1021/ma001792k10.1021/ma001792k ↗
19. 10.1021/ma00002a03410.1021/ma00002a034 ↗
20. 10.1016/j.polymer.2020.12267410.1016/j.polymer.2020.122674 ↗
21. 10.1016/j.polymer.2011.08.01910.1016/j.polymer.2011.08.019 ↗
22. 10.1016/j.eurpolymj.2007.04.02610.1016/j.eurpolymj.2007.04.026 ↗
23. 10.1016/0032-3861(91)90088-z10.1016/0032-3861(91)90088-z ↗
24. 10.1002/app.3962610.1002/app.39626 ↗
25. 10.1002/(sici)1097-4628(19971107)66:6<1007::aid-app1>3.0.co;2-m10.1002/(sici)1097-4628(19971107)66:6<1007::aid-app1>3.0.co;2-m ↗
26. 10.1021/ma071512210.1021/ma0715122 ↗
27. 10.1002/app.3962610.1002/app.39626 ↗
28. 10.1016/j.polymer.2005.02.08810.1016/j.polymer.2005.02.088 ↗
29. 10.1016/s0032-3861(97)00219-x10.1016/s0032-3861(97)00219-x ↗
30. 10.1016/j.compscitech.2019.10784610.1016/j.compscitech.2019.107846 ↗
31. 10.1021/ma062234u10.1021/ma062234u ↗
32. 10.1021/am201564f10.1021/am201564f ↗
33. 10.1002/1097-4628(20001031)78:5<962::aid-app40>3.0.co;2-510.1002/1097-4628(20001031)78:5<962::aid-app40>3.0.co;2-5 ↗
34. 10.1016/j.polymer.2016.06.05110.1016/j.polymer.2016.06.051 ↗
35. 10.1016/0032-3861(85)90015-110.1016/0032-3861(85)90015-1 ↗