Load-Driven Tribofilm Formation: Friction-Wear Trade-Off in Ti 2 AlN and Ti 2 NT x Multilayered Nanosheet Coatings
Source abstract
Abstract
MXenes have gained considerable attention in solid lubrication due to their involved tribofilm formation offering low friction and extended durability at the same time. While the solid lubrication performance of carbide systems has been well explored, research on nitride MXenes remains considerably scarce. Therefore, we synthesized multilayer Ti 2 NT x from its parental Ti 2 AlN precursor. Coatings consisting of multilayer Ti 2 NT x were spray-coated onto AISI 304 steel substrates to assess their solid lubrication performance using linear reciprocating ball-on-disk tribometry varying normal loads (0.1–1.0 N) and durations (15–60 min). In case of Ti 2 NT x, the specific wear rates ranged between 5.09 and 6.79 ×10 –8 mm 3 /(N·mm) for 15 min testing and decreased to about 1.30 × 10 –8 mm 3 /(N·mm) for extended durations (60 min and 1 N). In contrast, the Ti 2 AlN coating exhibited substantially higher friction (COF ≈ 0.55 for 0.4 N), while demonstrating lower wear rates of (2.84–3.17) × 10 –8 mm 3 /(N·mm) for a test duration of 15 min. To understand the involved friction and wear mechanism as well as tribochemistry, the corresponding wear tracks were assessed by complementary materials characterization. While bare steel exhibited a high, noisy friction, characteristic for abrasion- and debris-dominated tribosystems, the Ti 2 AlN coatings showed similarly high friction under low loads, which is consistent with a formation of a rigid, oxide-rich tribofilm. In striking contrast, the Ti 2 NT x coatings rapidly run into a low and remarkably stable friction, insensitive to both load and sliding time, thus evidencing the development of a more continuous, easy-to-shear tribofilm. The results indicated that the lamellar structure of Ti 2 NT x lamellae and its chemistry promote a self-replenishing tribofilm, whereas the Ti 2 AlN coating and the steel reference remain governed by abrasive circulation of oxide/debris. Using simple, scalable spray-coating, this MAX-to-MXene route delivers durable, low-friction surfaces thus extending the concept of 2D solid lubrication to Ti 2 NT x, highlighting their potential for tribological applications.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: MXene and MAX Phase Materials · Metal and Thin Film Mechanics · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Departamento de Ingeniería Química, Biotecnología y Materiales, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Beauchef 851, Santiago 8370456, Chile
ANID − Millennium Science Initiative Program, Millennium Nuclei of Advanced MXenes for Sustainable Applications (AMXSA), Beauchef 851, Santiago 8370456, Chile
Departamento de Geología Facultad de Ciencias Físicas y Matemáticas
Universidad de Chile
Funding
Fondo Nacional de Desarrollo Cient?fico y Tecnol?gico · Agencia Nacional de Investigaci?n y Desarrollo
References (51)
Show source-provided references
1. 10.1016/j.cis.2023.10302110.1016/j.cis.2023.103021 ↗
2. 10.1007/s11249-021-01531-w10.1007/s11249-021-01531-w ↗
3. Kumar P. · Jurnal Tribologi · 2017 · 13 · 36
4. 10.1002/adma.20100172210.1002/adma.201001722 ↗
5. 10.1016/j.measen.2022.10059210.1016/j.measen.2022.100592 ↗
6. 10.1002/adma.20130413810.1002/adma.201304138 ↗
7. Barsoum M. W. · 201310.1002/9783527654581 ↗
8. 10.1039/C6NR02253G10.1039/C6NR02253G ↗
9. 10.1039/C5DT01247C10.1039/C5DT01247C ↗
10. 10.1021/acsnano.9b0473110.1021/acsnano.9b04731 ↗
11. 10.1021/acsenergylett.8b0071810.1021/acsenergylett.8b00718 ↗
12. 10.1021/acsnano.1c0024810.1021/acsnano.1c00248 ↗
13. 10.1002/adma.20180765810.1002/adma.201807658 ↗
14. 10.1038/s41929-018-0195-110.1038/s41929-018-0195-1 ↗
15. 10.1038/s41598-017-01714-310.1038/s41598-017-01714-3 ↗
16. 10.1016/j.apsusc.2020.14650310.1016/j.apsusc.2020.146503 ↗
17. 10.1007/s40544-022-0709-310.1007/s40544-022-0709-3 ↗
18. 10.1021/acsanm.4c0485810.1021/acsanm.4c04858 ↗
19. 10.1021/acsanm.5c0199310.1021/acsanm.5c01993 ↗
20. 10.1016/j.mssp.2025.10953110.1016/j.mssp.2025.109531 ↗
21. 10.1088/1361-6463/ade81310.1088/1361-6463/ade813 ↗
22. 10.1016/j.est.2024.11435410.1016/j.est.2024.114354 ↗
23. 10.1126/science.abf158110.1126/science.abf1581 ↗
24. 10.1021/acsomega.0c0121510.1021/acsomega.0c01215 ↗
25. 10.1038/s41699-021-00239-810.1038/s41699-021-00239-8 ↗
26. 10.1080/01694243.2014.99737910.1080/01694243.2014.997379 ↗
27. 10.1021/acsnano.7b0312910.1021/acsnano.7b03129 ↗
28. 10.1016/j.triboint.2020.10677210.1016/j.triboint.2020.106772 ↗
29. Richard G. · 2004
30. Beer F. · Mech. Mater. · 1992 · A2
31. 10.1016/j.ijhydene.2024.08.01010.1016/j.ijhydene.2024.08.010 ↗
32. 10.1186/s12951-019-0545-410.1186/s12951-019-0545-4 ↗
33. 10.1039/D0CE01013H10.1039/D0CE01013H ↗
34. 10.1039/D2SE01532C10.1039/D2SE01532C ↗
35. 10.1021/acs.jpcc.3c0671710.1021/acs.jpcc.3c06717 ↗
36. 10.1038/s41598-021-04640-710.1038/s41598-021-04640-7 ↗
37. 10.1016/j.ceramint.2024.09.23410.1016/j.ceramint.2024.09.234 ↗
38. 10.1016/j.jallcom.2013.05.19910.1016/j.jallcom.2013.05.199 ↗
39. 10.1088/2051-672X/ac9d5110.1088/2051-672X/ac9d51 ↗
40. 10.1016/j.jallcom.2018.08.10010.1016/j.jallcom.2018.08.100 ↗
41. 10.1016/j.carbon.2022.05.01210.1016/j.carbon.2022.05.012 ↗
42. Gupta S. · 2006
43. 10.1016/j.surfin.2025.10737510.1016/j.surfin.2025.107375 ↗
44. 10.1016/j.mtnano.2024.10046410.1016/j.mtnano.2024.100464 ↗
45. 10.1039/C7TA01082F10.1039/C7TA01082F ↗
46. 10.1039/c3ra45872e10.1039/c3ra45872e ↗
47. 10.1021/acsanm.1c0255610.1021/acsanm.1c02556 ↗
48. 10.3390/ma1816373810.3390/ma18163738 ↗
49. 10.1016/j.jallcom.2016.11.28410.1016/j.jallcom.2016.11.284 ↗
50. 10.1021/acsanm.4c0250310.1021/acsanm.4c02503 ↗
51. 10.1002/adma.20220775710.1002/adma.202207757 ↗