Combined effect of strontium modifier and antimony refiner on texture and growth mode of eutectic phase in an Al-11Si-2Cu-0.8Zn-0.6Fe cast alloy
Source abstract
Abstract
Results of electron back-scattered diffraction and transmission electron microscopy studies reveal that the orientation of aluminium in the eutectic phase is different from the surrounding aluminium dendrites and that twin spacing of eutectic silicon increased significantly due to the interaction between strontium and antimony. In addition, the formation of ternary Mg2Sb2Sr intermetallic compound that precedes the eutectic reaction was proposed to be responsible for interaction.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Aluminum Alloy Microstructure Properties · Aluminum Alloys Composites Properties · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (12)
Show source-provided references
1. 10.1016/j.jallcom.2013.11.14510.1016/j.jallcom.2013.11.145 ↗
2. 10.1023/A:102287000672110.1023/A:1022870006721 ↗
3. 10.1007/BF0291547610.1007/BF02915476 ↗
4. 10.1016/S1044-5803(00)00089-910.1016/S1044-5803(00)00089-9 ↗
5. 10.1016/j.matlet.2007.05.02010.1016/j.matlet.2007.05.020 ↗
6. Wang W. · AFS Trans. · 1990 · 98 · 227
7. 10.1016/j.msea.2005.09.05510.1016/j.msea.2005.09.055 ↗
8. 10.1016/j.jallcom.2013.05.13910.1016/j.jallcom.2013.05.139 ↗
9. 10.1016/S1471-5317(02)00005-610.1016/S1471-5317(02)00005-6 ↗
10. 10.1016/j.scriptamat.2006.07.02910.1016/j.scriptamat.2006.07.029 ↗
11. 10.1016/j.actamat.2012.03.03110.1016/j.actamat.2012.03.031 ↗
12. 10.1016/j.tca.2014.04.00110.1016/j.tca.2014.04.001 ↗