The effect of blue and infrared laser melting frequency on oxide morphology in 304L

Continuous Wave Laser Beam (LB) melting offers control over the localised heating and cooling of melt pools for welding, brazing, additive manufacturing and solidification. Research into laserliquid metal interactions has primarily focused on the heat and mass transport under large thermal gradients imposed by the localised melting conditions. Recent commercial availability of blue (450 nm) wavelength lasers has enabled the printing of material with poor IR (1064) nm attenuation like Cu. However, little research has been conducted into varying input laser frequency and scan rate at fixed absorption to understand the effects of laser light on surface oxide formation and the underlying liquid metal thermodynamic response. This article conducts laser melting of 304L under Blue (450 nm) and Infrared (IR, 1064 nm) laser frequencies and examines their impact on laser oxide thickness, chemistry and coloration. We find that laser frequencies induce changes in the oxide layer thickness and chemistry that cannot be explained using conventional thermal absorption shifts and fluid dynamics. We suggest that light coupling may have thermodynamic implications for the chemical potential of the liquid metal, which may drive the observed phase behaviour. Identifying mechanisms for the tuning of the chemical potential via laser frequency control could enable the ability to control solidification microstructure and atomic ordering in laser welding and additive manufacturing processes.