Improvement of radiation stability of semi-insulating gallium arsenide crystals by deposition of diamond-like carbon films

Abstract We studied the properties of optical elements for the IR spectral range based on semi-insulating gallium arsenide (SI-GaAs) and antireflecting diamond-like carbon films (DLCF). Particular attention has been paid to the effect of penetrating γ-radiation on transmission of the developed optical elements. A Co 60 source and step-by-step gaining of γ-irradiation dose were used for treatment of both an initial SI-GaAs crystal and DLCF/SI-GaAs structures. It was shown that DLCF deposition essentially increases degradation resistance of the SI-GaAs-based optical elements to γ-radiation. Particularly, the transmittance of the DLCF/SI-GaAs structure after γ-irradiation with a dose 9⋅10 4 Gy even exceeds that of initial structures. The possible mechanism that explains the effect of γ-radiation on the SI-GaAs crystals and the DLCF/SI-GaAs structures at different irradiation doses was proposed. The effect of small doses is responsible for non-monotonic transmission changes in both SI-GaAs crystals and DLCF/SI-GaAs structures. At further increasing the γ-irradiation dose, the variation of properties of both DLCF and SI-GaAs crystal influences on the transmission of DLCF/SI-GaAs system. At high γ-irradiation dose 1.4⋅10 5 Gy, passivation of radiation defects in the SI-GaAs bulk by hydrogen diffused from DLCF leads to increasing the degradation resistance of the SI-GaAs crystals coated with DLCF as compared with the crystals without DLCF.