Relaxation of intrinsic and extrinsic electronic excitations in nano- and micro-size alumina

Abstract Nanopowders consisting of mixed α-alumina and transition alumina phases were prepared by combustion synthesis and investigated using low temperature time-resolved cathodoluminescence and photoluminescence spectroscopy under VUV excitation. The onsets of the intrinsic absorption for different alumina phases were revealed in mixed phase nanopowders by analysing luminescence excitation spectra. All synthesized nanopowders possessed the intrinsic luminescence band with a maximum at 4.6 eV, which is assigned to the radiative decay of triplet self-trapped excitons with ∼750 μs decay time at 78 K. A red shift by 0.3 eV was revealed for the peak of the O2− – Cr3+ charge transfer band near 7 eV as a function of particle size. This shift is correlated with the decrease of α-alumina particle size from 180 to 80 nm. Its origin is discussed in the framework of the Kroning-Penney model.