Photochromic lens mirror-coated with Cr

Abstract We have designed and fabricated mirror-coated photochromic lenses for use in sunglasses. These lenses consisted of a Cr thin film sandwiched between two SiO 2 layers on the front surface and an anti-reflection (AR) coating on the backside. The SiO 2 films above and below the Cr layer were introduced as the protection and buffer layers, respectively. The AR coating was to suppress back-reflection from the lens surface. Deposition of all coating layers were carried out by an e-beam evaporator under Ar atmosphere at P = 10 −5 Torr and T = 70 °C. As expected, the overall transmittance decreased with increasing Cr thickness. For a Cr layer of 5 nm thickness, it changed from about 45% in the bleached state down to 25% after exposure to sunlight. This is consistent with the transmission range typically required for sunglasses.