Luminescence properties of La2Si6O3N8:Eu2+ phosphors prepared by spark plasma sintering
Source abstract
Abstract
Abstract Bluish green-emitting La2Si6O3N8:Eu2+ phosphors were synthesized by a spark plasma sintering (SPS) method, and the effects of sintering temperature, Eu doping concentration, post-annealing, and acid washing on the photoluminescence (PL) properties were investigated. A single phase La2Si6O3N8:Eu2+ was successfully achieved at 1700 °C by SPS. As-synthesized La2Si6O3N8:Eu2+ phosphors exhibited a single band emission centered at 483–496 nm under the excitation of 370 nm. The post-annealing and acid-washing significantly improved the emission intensity by increasing the crystallinity, reducing the carbon content, and changing the morphology of particles. Unexpectedly, La2Si6O3N8:Eu2+ phosphors showed a strong thermal quenching.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Luminescence Properties of Advanced Materials · Advanced Photocatalysis Techniques · MXene and MAX Phase Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. Xie · Appl. Phys. Lett. · 2004 · 84 · 540410.1063/1.1767596 ↗
2. Yamada · Jpn. J. Appl. Phys. · 2003 · 42 · L2010.1143/JJAP.42.L20 ↗
3. Pan · J. Phys. Chem. Solids · 2004 · 65 · 84510.1016/j.jpcs.2003.08.018 ↗
4. Do · J. Electrochem. Soc. · 2006 · 153 · H14210.1149/1.2200299 ↗
5. Yang · Appl. Phys. Lett. · 2007 · 90 · 12350310.1063/1.2714326 ↗
6. Sheu · IEEE Photon. Technol. Lett. · 2003 · 15 · 1810.1109/LPT.2002.805852 ↗
7. Dierre · J. Mater. Res. · 2007 · 22 · 193310.1557/jmr.2007.0231 ↗
8. Takahashi · Appl. Phys. Lett. · 2007 · 91 · 09192310.1063/1.2779093 ↗
9. van Krevel · J. Alloys Comp. · 1998 · 268 · 27210.1016/S0925-8388(97)00550-1 ↗
10. Grins · J. Mater. Chem. · 2001 · 11 · 235810.1039/b102340n ↗
11. Harris · Chem. Mater. · 1992 · 4 · 26010.1021/cm00020a009 ↗
12. Long · Chin. Phys. B · 2010 · 19 · 12780710.1088/1674-1056/19/12/127807 ↗
13. Choi · J. Electrochem. Soc. · 2010 · 157 · J29710.1149/1.3454237 ↗
14. Li · Int. J. Appl. Ceram. Technol. · 2009 · 6 · 45910.1111/j.1744-7402.2009.02370.x ↗
15. Zeuner · Chem. Mater. · 2009 · 21 · 246710.1021/cm900341f ↗
16. Zeuner · Chem. Mater. · 2008 · 21 · 33610.1021/cm8024796 ↗
17. Piao · Chem. Mater. · 2007 · 19 · 459210.1021/cm070623c ↗
18. Bachmann · Chem. Mater. · 2008 · 21 · 31610.1021/cm802394w ↗
19. Yu · Mater. Lett. · 2011 · 65 · 269010.1016/j.matlet.2011.05.101 ↗
20. Sohn · J. Electrochem. Soc. · 2008 · 155 · 5810.1149/1.2817892 ↗
21. Do · J. Am. Ceram. Soc. · 2009 · 93 · 35610.1111/j.1551-2916.2009.03424.x ↗
22. Choi · Opt. Mater. · 2011 · 33 · 170010.1016/j.optmat.2011.05.025 ↗
23. Zhang · Mater. Lett. · 2005 · 59 · 74910.1016/j.matlet.2004.11.014 ↗
24. Yang · Mater. Lett. · 2008 · 62 · 188410.1016/j.matlet.2007.10.030 ↗
25. Ryu · J. Electrochem. Soc. · 2008 · 155 · J9910.1149/1.2834453 ↗
26. de Graaf · J. Eur. Ceram. Soc. · 2003 · 23 · 109310.1016/S0955-2219(02)00236-4 ↗
27. Zhang · J. Alloy. Comp. · 2005 · 400 · 22210.1016/j.jallcom.2005.04.001 ↗
28. Dorenbos · J. Lumin. · 2008 · 128 · 57810.1016/j.jlumin.2007.09.005 ↗
29. Srivastava · J. Lumin. · 2009 · 129 · 63410.1016/j.jlumin.2009.01.008 ↗