Systematic control of optical features in aluminosilicate glass waveguides using direct femtosecond laser writing

Abstract Low loss optical waveguides inside aluminosilicate glasses have been successfully fabricated using direct femtosecond laser writing. To establish the influence of pulse energy and host variations on the optical waveguides have been tentatively explored and systematically studied with the help of different spectroscopic techniques. Isochronal annealing treatment effectively reduces the insertion losses to 1.01 ± 0.28 dB at 632.8 nm. A red shift of the Raman band has been observed with increasing Al 2 O 3 content due to the bond angle variations. The point defects such as non-bridging oxygen hole centers have been corroborated by the photoluminescence studies and significant red-shift has also been documented with increasing Al 2 O 3 content. In addition, there is no NBOHC defects perceived after isochronal annealing treatment inside the glass waveguides. Our results envisage that the present glass waveguides should be promising and potential for applications in passive waveguides and integrated photonic devices.