Excitonic luminescence in ZnO nanopowders and ceramics

Abstract Fast photoluminescence spectra in the spectral region of 3.1–3.45 eV in ZnO and ZnO:Al ceramics were studied at 14 and 300 K. Ceramics with grains smaller than 100 nm were sintered from nanopowders by high pressure (8 GPa) and low temperature (350 °C). Ceramics with grain sizes 1–5 μm were sintered at 1400 °C. It is shown that excitonic luminescence spectra depend on the ceramics grain size, post preparing annealing and doping. The excitonic luminescence decay time was faster than 2 ns and the afterglow at 30 ns was ∼0.05%.