Growth, improved thermal stability and spectral properties of Yb 3+ -ions doped high temperature phase α-Ba 3 Gd(BO 3 ) 3 crystals co-doped by Sr 2+ , Ca 2+ and La 3+ ions

Abstract To investigate the cause of the thermal instability of Yb3+-ions doped Ba3Gd(BO3)3 crystal grown from Czochralski technique, the low temperature phase β-Ba3Gd(BO3)3 powder was synthesized at the temperature of 800 °C. To inhibit the phase transition of high temperature phase Yb:α-Ba3Gd(BO3)3 during the crystal growth process, co-doping ions Sr2+, Ca2+ and La3+ ions were introduced in Yb:α-Ba3Gd(BO3)3 crystal. The melting point increased and the thermal stability of Yb:α-Ba3Gd(BO3)3 crystal was improved by co-doping ions. The absorption peaks of co-doped crystals centered at 976 nm with FWHM of 11, 11 and 12 nm and the absorption cross sections were 3.40 × 10−21 cm2, 4.00 × 10−21 cm2 and 2.66 × 10−21 cm2, respectively. The emission cross sections at 1040 nm were 2.19 × 10−21 cm2, 2.53 × 10−21 cm2 and 1.93 × 10−21 cm2, respectively. The fluorescence times of co-doped by Sr2+, Ca2+ and La3+ ions were shorter than that of Yb:α-Ba3Gd(BO3)3 crystal. So Yb:α-Ba3Gd(BO3)3 crystals co-doped by Sr2+, Ca2+ and La3+ ions will be more suitable for LD-pumping laser.