Dehydration processing of Er3+-doped barium gallo-germanate glasses with ultra-low hydroxyl absorption for near and mid-infrared applications

Florian Calzavara, V.A.G. Rivera, Alexandre Fargues, Jean-Paul Salvetat, Marc Dussauze, Younès Messaddeq, Théo Guérineau, Véronique Jubera, Thierry Cardinal, Évelyne Fargin

Optical Materials· Volume 165

Abstract

In barium gallo-germanate glasses, the extrinsic absorption losses from hydroxyl (-OH) groups are mostly due to the hygroscopic nature seen in the glass, its raw precursors and from the environment during the melting process. Their vibrations (harmonic or overtone) cause detrimental absorption bands in the infrared region which limit their use as host materials for rare-earth ions emitting in the infrared. It is therefore essential to minimize the concentration of (-OH) groups in the glass. Here, we present a dehydration method to prepare barium gallo-germanate glasses at high temperature (>1500 °C) under a controlled atmosphere (Ar-filled, with 0.1 ppm O 2 and 0.1 ppm H 2 O) with ammonium bi-fluoride (NH 4 F–HF) as dehydrating agent to lower (–OH)–based absorption coefficient down to 0.006 cm −1 at 3300 nm wavelength. This improvement allows a significant lengthening of the lifetimes of the electronic transition in the near infrared at 1000 nm ( 4 I 11/2 → 4 I 15/2 ) and 1537 nm ( 4 I 13/2 → 4 I 15/2 ) in the glasses with ultra-low hydroxyl content due to reduced (-OH) quenching. This work paves the way for developing efficient barium gallo-germanate solid-state laser components for sensing operation in the near and mid-infrared spectral range (1–5 μm). We investigated dehydration routes to synthesize barium gallo-germanate glasses with ultra-low hydroxyl (-OH) groups at high temperature (>1500 °C). We demonstrate that the synthesis under a controlled atmosphere (Ar-filled, with 0.1 ppm O 2 and 0.1 ppm H 2 O) allows to reduce signicantly the amount of –OH groups in the glass. This preparation method combined with the introduction of ammonium bi-fluoride (NH 4 F–HF) as dehydrating agent enables to obtain t a significant lengthening of the lifetimes corresponding to the electronic transition in the near infrared at 1000 nm ( 4 I 11/2 → 4 I 15/2 ) and 1537 nm ( 4 I 13/2 → 4 I 15/2 ) in the glasses with ultra-low hydroxyl content due to reduced –OH quenching is shown. This work paves the way for developing efficient barium gallo-germanate solid-state laser components in the short wave infrared range and opens up potential applications in the mid wave infrared range.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Glass properties and applications · Solid State Laser Technologies · Luminescence Properties of Advanced Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (43)

Show source-provided references
1. A review of visible, near-IR, and mid-IR transitions in rare-earth doped glass waveguides for remote sensing and LIDAR
2. Rare-earth-doped glasses for fiber amplifiers in broadband telecommunication10.1016/S1631-0748(02)01449-2 ↗
3. Frequency-comb-based remote sensing of greenhouse gases over kilometer air paths10.1364/OPTICA.1.000290 ↗
4. Bio-inspired imager improves sensitivity in near-infrared fluorescence image-guided surgery10.1364/OPTICA.5.000413 ↗
5. High‐power ZBLAN glass fiber lasers: review and prospect
6. Liquid-cooled 24 W mid-infrared er: ZBLAN fiber laser10.1364/OL.34.003062 ↗
7. 30 W fluoride glass all-fiber laser at 2.94 μm10.1364/OL.40.002882 ↗
8. Fluoride fibre laser operating at 3.9 μm10.1049/el:19950858 ↗
9. Deep-ultraviolet to mid-infrared supercontinuum generated in solid-core ZBLAN photonic crystal fibre10.1038/nphoton.2014.320 ↗
10. Heavy-oxide glasses with superior mechanical assets for nonlinear fiber applications in the mid-infrared10.1364/OME.417699 ↗
11. Demonstration of a 0.8 W continuous wave bulk laser around 2 μm in a Tm3+: ga-Rich BGG glass10.1364/OME.524064 ↗
12. Lasing in a femtosecond-laser-written single-scan waveguide fabricated in Tm-doped BGG glass10.1364/OL.547643 ↗
13. 2.7 μm mid‐infrared emission in highly erbium‐doped lanthanum gallate glasses prepared via an aerodynamic levitation technique10.1002/adom.201701283 ↗
14. Novel insights into the electronic and optical properties of the 1.53-μm emission in Er3+-doped oxide-and oxyfluoride-tellurite glasses for optical communications10.1016/j.jallcom.2023.173182 ↗
15. Expanding broadband emission in the near-IR via energy transfer between Er3+–Tm3+ co-doped tellurite-glasses10.1016/j.jlumin.2013.08.071 ↗
16. Reduction of OH− ions in tellurite glasses using chlorine and oxygen gases10.1557/jmr.2013.341 ↗
17. Hydroxyl groups in erbium-doped germanotellurite glasses10.1016/S0022-3093(00)00429-4 ↗
18. TeO2-ZnO-La2O3 tellurite glass purification for mid-infrared optical fibers manufacturing10.1364/OME.438588 ↗
19. Development of low‐loss lead‐germanate glass for mid‐infrared fiber optics: I. Glass preparation optimization10.1111/jace.17503 ↗
20. Extended germano-gallate fiber drawing domain: from germanates to gallates optical fibers10.1364/OME.9.002437 ↗
21. Resolved‐detrimental surface crystallization in yttrium lanthanum gallate glasses for optical fiber applications10.1111/jace.19184 ↗
22. Toward low-loss mid-infrared Ga2O3–BaO–GeO2 optical fibers10.1038/s41598-023-30522-1 ↗
23. Photosensitivity of barium germano-gallate glasses under femtosecond laser direct writing for Mid-IR applications10.1016/j.ceramint.2021.08.333 ↗
24. Investigation of Ga2O3-BaO-GeO2 glasses for ultrafast laser inscription10.1364/OME.491952 ↗
25. Structure and properties of gallate and germanate langasite infrared optical glass materials10.1016/j.jnoncrysol.2024.123204 ↗
26. m-lines technique: prism coupling measurement and discussion of accuracy for homogeneous waveguides10.1088/1464-4258/2/3/304 ↗
27. Luo · 2007
28. Influence of fluorine on thermal properties of lead oxyfluoride glass10.1007/s10973-013-3047-x ↗
29. Effect of fluorine content on the crystallization of fluorsilicic mica glass10.1023/A:1014941722122 ↗
30. Effect of fluorine and nitrogen content on the properties of Ca-Mg-Si-Al-O-(N)-(F) glasses10.1016/j.ceramint.2016.12.046 ↗
31. Energy levels of the laser active Er3+ ion in each of the two crystallographic sites of yttrium orthosilicate10.1088/0953-8984/7/26/017 ↗
32. The spectra of the doubly and triply ionized rare earths10.1364/AO.2.000675 ↗
33. Structural influences on the hydroxyl spectra of barium gallogermanate glasses10.1016/0022-3093(94)00471-4 ↗
34. Influence of hydroxyl group on IR transparency of tellurite‐based glasses10.1111/ijag.12044 ↗
35. Glass forming regions, structure and properties of lanthanum barium germanate and gallate glasses10.1016/j.jnoncrysol.2021.121064 ↗
36. Q speciation in alkali germanate glasses10.1016/j.jnoncrysol.2010.03.023 ↗
37. Principal vibration modes of the La2O3-Ga2O3 binary glass originated from diverse coordination environments of oxygen atoms10.1021/acs.jpcb.0c02147 ↗
38. Low phonon energies and wideband optical windows of La2O3-Ga2O3 glasses prepared using an aerodynamic levitation technique10.1038/srep45600 ↗
39. Structure and properties of gallium-rich sodium germano-gallate glasses10.1021/acs.jpcc.8b08632 ↗
40. Characterization of the structure of calcium alumino-silicate and calcium fluoro-alumino-silicate glasses by magic angle spinning nuclear magnetic resonance (MAS-NMR)10.1016/j.jnoncrysol.2003.09.049 ↗
41. Preferential binding of fluorine to aluminum in high peralkaline aluminosilicate glasses10.1021/jp073687j ↗
42. Local structure of Er3+ in multicomponent glasses10.1016/S0022-3093(98)00733-9 ↗
43. Energy level decay and excited state absorption processes in erbium-doped tellurite glass10.1063/1.3651399 ↗