Synthesis and optical characterization of n-ZnO and p-Cu2ZnSnS4 nanocrystalline thin films for low cost solar cells

Abstract High quality ZnO/Cu2ZnSnS4 thin films as a window/absorber layers were successfully synthesized via spin coating the sol-gel precursor of each composition without using any vacuum facilities. In this study, the impact of annealing temperature (400 °C, 3 h) on the ZnO window layer and different thickness (3 and 5 layers) of the Cu2ZnSnS4 (CZTS) absorber layer were investigated. X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDX), scanning electron microscope (SEM) and UV–vis–NIR spectroscopy were used for the structural, compositional, morphological and optical absorption analysis of each layer. ZnO exhibits wurtzite hexagonal crystal structure with particle size equals to 8.60 and 28.59 nm for fresh and annealed films, respectively. Micro-strain and dislocations density decreased with the annealing temperature. X-ray diffraction patterns for CZTS films show small peak at (112) according to the kesterite structure with particle size in nano-scale for the two thicknesses. ZnO films demonstrated direct optical band gap of 3.23 and 3.21 eV for fresh and annealed films, respectively. CZTS films (3 and 5 layers) also have direct optical band with optimum value (1.51 eV) for thickness of 5 layers. The J-V characteristics of the CZTS-based thin film solar cells (CZTS/ZnO/ZnO:Ag) were measured under air mass AM 1.5 and 100 mW/cm2 illumination. The values of the short circuit current (Jsc), open circuit voltage (Voc) and fill factor (FF) also have been obtained.