Synthesis of poly glycidylmethacrylate grafted azobenzene copolymer: Photosensitivity and nonlinear optical properties

Abstract In this work poly glycidylmethacrylate grafted 4-hydroxy-4′-methoxy-azobenzene (Azo-PGMA) was synthesized. For this propose firstly 4-hydroxy-4′-methoxy-azobenzene (AZO) was prepared, then poly glycidylmethacrylate was prepared by free radical polymerization of glycidylmethacrylate in the presence of benzoyl peroxide as initiator under inert atmosphere in dry THF. Finally the homopolymer was functionalized by AZO moieties. The characterization of the synthesized copolymer was carried out by 1H NMR, FT-IR, thermal gravimetric analyze (TGA), differential scanning calorimetry (DSC) and optical polarizing microscope (POM) analysis. The UV–vis studies were carried out on Azo-PGMA copolymer and the results showed that the synthesized Azo-PGMA copolymer has ultra-fast response to UV light and has slow relaxation time. Also the third-order nonlinear optical properties of the Azo-PGMA copolymer and AZO were studied by using Z-scan technique. Nonlinear refraction and absorption coefficients of the above mentioned materials were measured by the closed and open aperture Z-scan method using a continuous wave Nd-YAG laser at 532 nm. The positive nonlinear absorption in Azo-PGMA and AZO was investigated at the wavelength of λ = 532 nm, respectively and the measured values of nonlinear refraction in both of the samples were from the order of 10−8 cm2/W.