Selective Cleaning of Hollow Nanoporous Carbon Cubes for Electromagnetic Wave Absorption
Source abstract
Abstract
This study introduces a method for fabricating hollow nanoporous carbon cubes (HPCCs), utilizing the selective purification effect of acetone on a small-molecule phenolic resin (PR)/NaCl precursor. The impact of acetone-induced purification on the nanoscale microstructure and electromagnetic wave-absorbing properties of HPCCs is systematically explored. Using a template-etch-carbonization process, the HPCCs exhibit a significant increase in specific surface area from 149.61 m 2 /g (HPCCs0min) to 315.86 m 2 /g (HPCCs10min), highlighting the nanoscale structural modifications induced by acetone treatment. At 5 wt % absorber content and a 2.7 mm thickness, HPCCs treated for 10 min demonstrate optimal wave-absorbing performance, achieving a peak reflection loss (RL min ) of −24.1 dB and an effective absorption bandwidth (EAB) of 7.3 GHz. These results underscore the critical role of nanoscale surface area and pore volume modulation in enhancing the electromagnetic wave absorption capabilities of HPCCs.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Electromagnetic wave absorption materials · Advanced Antenna and Metasurface Technologies · Cellular and Composite Structures
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Engineering
Xihang University
School of Materials Science and Chemical Engineering
Xian Technological University
Funding
Shaanxi Provincial Innovative Talent Promotion Plan - Youth Science and Technology New Star Project · Innovation and Entrepreneurship Training Program for University Students · Youth Innovation Team of Shaanxi Universities Project · Shaanxi Province Natural Science Basic Research Program
References (51)
Show source-provided references
1. 10.1002/adfm.20241610810.1002/adfm.202416108 ↗
2. 10.1007/s12613-024-2999-010.1007/s12613-024-2999-0 ↗
3. 10.1002/adfm.20241231410.1002/adfm.202412314 ↗
4. 10.1016/j.cej.2024.15089310.1016/j.cej.2024.150893 ↗
5. 10.1007/s12598-022-02141-810.1007/s12598-022-02141-8 ↗
6. 10.1016/j.chphma.2022.10.00210.1016/j.chphma.2022.10.002 ↗
7. 10.1002/adfm.20241592110.1002/adfm.202415921 ↗
8. 10.1002/adfm.20240453210.1002/adfm.202404532 ↗
9. 10.1016/j.jallcom.2018.12.01010.1016/j.jallcom.2018.12.010 ↗
10. 10.1016/j.carbon.2020.11.04310.1016/j.carbon.2020.11.043 ↗
11. 10.1016/j.carbon.2023.03.01410.1016/j.carbon.2023.03.014 ↗
12. 10.1016/j.compositesb.2022.11025410.1016/j.compositesb.2022.110254 ↗
13. 10.1016/j.ceramint.2021.05.21910.1016/j.ceramint.2021.05.219 ↗
14. 10.1016/j.carbon.2023.11865110.1016/j.carbon.2023.118651 ↗
15. 10.1016/j.jallcom.2018.03.20210.1016/j.jallcom.2018.03.202 ↗
16. 10.1016/j.jallcom.2023.17056110.1016/j.jallcom.2023.170561 ↗
17. 10.1002/smll.20220705110.1002/smll.202207051 ↗
18. 10.1016/j.synthmet.2023.11733410.1016/j.synthmet.2023.117334 ↗
19. 10.1016/j.carbon.2024.11924410.1016/j.carbon.2024.119244 ↗
20. 10.1007/s10853-021-05780-x10.1007/s10853-021-05780-x ↗
21. 10.1016/j.mtnano.2024.10052010.1016/j.mtnano.2024.100520 ↗
22. 10.1002/smll.20240587410.1002/smll.202405874 ↗
23. 10.1016/j.carbon.2020.10.06210.1016/j.carbon.2020.10.062 ↗
24. 10.1016/j.carbon.2020.01.08110.1016/j.carbon.2020.01.081 ↗
25. 10.1016/j.carbon.2022.04.00710.1016/j.carbon.2022.04.007 ↗
26. 10.1016/j.cej.2020.12602710.1016/j.cej.2020.126027 ↗
27. 10.1016/j.carbon.2021.08.02910.1016/j.carbon.2021.08.029 ↗
28. 10.1016/j.colsurfa.2022.13015610.1016/j.colsurfa.2022.130156 ↗
29. 10.1016/j.jallcom.2023.17262510.1016/j.jallcom.2023.172625 ↗
30. 10.1016/j.carbon.2017.11.05510.1016/j.carbon.2017.11.055 ↗
31. 10.1016/j.jclepro.2022.13425810.1016/j.jclepro.2022.134258 ↗
32. 10.1016/j.jmst.2023.07.06110.1016/j.jmst.2023.07.061 ↗
33. 10.1016/j.jmst.2022.05.04510.1016/j.jmst.2022.05.045 ↗
34. 10.1016/j.cej.2023.14481810.1016/j.cej.2023.144818 ↗
35. 10.1016/j.carbon.2021.08.02110.1016/j.carbon.2021.08.021 ↗
36. 10.1016/j.carbon.2021.12.02510.1016/j.carbon.2021.12.025 ↗
37. 10.1016/j.jmst.2022.04.04710.1016/j.jmst.2022.04.047 ↗
38. 10.1016/j.jmrt.2023.05.17710.1016/j.jmrt.2023.05.177 ↗
39. 10.1016/j.matchemphys.2021.12524610.1016/j.matchemphys.2021.125246 ↗
40. 10.1016/j.compositesb.2020.10849110.1016/j.compositesb.2020.108491 ↗
41. 10.1002/pc.2839810.1002/pc.28398 ↗
42. 10.1016/j.jallcom.2022.16673210.1016/j.jallcom.2022.166732 ↗
43. 10.1016/j.jmst.2022.07.03610.1016/j.jmst.2022.07.036 ↗
44. 10.1016/j.ceramint.2023.05.24210.1016/j.ceramint.2023.05.242 ↗
45. 10.1016/j.apsusc.2023.15722310.1016/j.apsusc.2023.157223 ↗
46. 10.1016/j.jmst.2022.02.05110.1016/j.jmst.2022.02.051 ↗
47. 10.1016/j.carbon.2023.02.06610.1016/j.carbon.2023.02.066 ↗
48. 10.1016/j.jmst.2024.07.00610.1016/j.jmst.2024.07.006 ↗
49. 10.1016/j.compositesa.2024.10855810.1016/j.compositesa.2024.108558 ↗
50. 10.1063/5.020051010.1063/5.0200510 ↗
51. 10.1007/s40820-024-01549-410.1007/s40820-024-01549-4 ↗