Luminescence quantum efficiency at 1.5μm of Er3+-doped tellurite glass determined by thermal lens spectroscopy

Abstract Erbium doped tellurite glasses (TeO 2 + Li 2 O + TiO 2 ) were prepared by conventional melt-quenching method to study the influence of the Er 3+ concentration on the luminescence quantum efficiency ( η ) at 1.5 μm. Absorption and luminescence data were used to characterize the samples, and the η parameter was measured using the well-known thermal lens spectroscopy. For low Er 3+ concentration, the measured values are around 76%, and the concentration behavior of η shows Er–Er and Er–OH − interactions, which agreed with the measured lifetime values.