Tunable multicolor and enhanced red emission of monodisperse CaF2:Yb3+/Ho3+ microspheres via Mn2+ doping

Abstract Transition metal ions (e.g. Mn2+) and lanthanide co-doped upconversion (UC) materials have attracted wide attention in recent years due to their promising application in multicolor display. Here, we report the hydrothermal synthesis and characterization of Mn2+ doped monodisperse CaF2:Yb3+/Ho3+ microspheres. The results of X-ray diffraction (XRD) revealed that Mn2+ doping does not change the cubic phase of CaF2 material but will lead to diffraction peaks shifting slightly towards higher angle due to the substitution of larger Ca2+ by the relatively smaller Mn2+. Under the excitation of 980 nm continuous wave (CW) laser, these microspheres exhibit green-yellow-red tuning colors and remarkable enhancement of both red to green ratio (R/G) and red to blue ratio (R/B) when increasing Mn2+ concentration from 0 to 30 mol%. The energy migration process between Ho3+ and Mn2+ was proposed and supported by time-decay and power dependence measurements of Ho3+ UC emission. These upconversion materials may have potential applications in optical devices, color display, nanoscale lasers and biomedical imaging.