Laser-synthesized Y 2 O 3 :Eu 3+ nanophosphors and their stabilization in water suspensions

Abstract Europium doped yttrium oxide nanophosphors (Y 2 O 3 doped with 5% Eu 3+ ), which consists of spherical single-phase monoclinic particles with an average size of 17 nm, was prepared by laser synthesis. While the monoclinic material has a low efficiency of only 19% of a μm-sized commercial Y 2 O 3 :Eu product, the cubic phase after calcination at 900 °C achieves 68% despite the remaining hydroxo-groups at the surface and still small crystallite size (56 nm). An ethanolammonium salt of citric acid (Dolapix CE64) was used as a dispersant in water suspension. To estimate the stability of the dispersed phase, the electrokinetic potential and agglomerate sizes were measured as a function of pH. With this dispersant, a 30 wt% nanopowder water suspension, showing a Newtonian viscosity of about 6 mPa × s, was obtained. Maximum content of the nanopowder of about 60 wt% can be accomplished in the slurry, still fluid enough to be used to cast a highly uniform and dense ceramic green body to sinter nanostructured Y 2 O 3 :Eu 3+ phosphors ceramics.