Sol-gel processing, spectral features and thermal stability of Li-stuffed Li6CaLa2Nb2O12:RE garnet phosphors (RE = Pr, Sm, Tb, Dy)

Abstract A series of garnet-type Li6CaLa2(1-x)Nb2O12:xRE phosphors (LCLN:xRE, RE = Pr, Sm, Tb and Dy) were prepared via sol-gel processing and subsequent calcination for the first time, with the course of phase evolution and the characteristics of the LCLN host and RE3+ luminescence being investigated in detail. It was found that ∼900–1000 °C is a suitable temperature for precursor calcination to produce the garnet phase and LCLN has a relatively low phonon energy (∼725 cm−1) and a relatively wide bandgap (∼4.53 eV) for luminescence. The LCLN:0.012Pr, LCLN:0.04Sm, LCLN:0.06 Tb and LCLN:0.06Dy typical phosphors were analyzed to have dominant excitation/emission bands at ∼278/489, 265/614, 268/549 and 264/581 nm, emission colors of white, orange, green and yellowish white, and fluorescence lifetimes of ∼0.43, 0.74, 0.90 and 0.44 ms, respectively. Temperature-dependent photoluminescence found that the four phosphors maintained ∼28, 37, 45 and 56% of their room-temperature intensities at 423 K, with activation energies for thermal quenching of ∼0.37, 0.29, 0.34 and 0.25 eV, respectively. The results demonstrated that the Li-stuffed LCLN garnet could be a suitable host for UV excitable multicolor phosphors.