Co₃Fe₇ Alloy Nanoparticles Encapsulated in N-Doped Carbon as Oxygen-Reduction Electrocatalysts for Rechargeable Zinc-Air Batteries

Bimetallic alloy catalysts have become highly sought-after star catalysts in the oxygen reduction reaction (ORR) due to their excellent catalytic activity and stability. In this study, an optimal catalyst (Co 3 Fe 7 @NC-800) involving Co 3 Fe 7 alloy nanoparticles encapsulated by N-doped carbon shield was constructed by employing Co-ZIF and g -C 3 N 4 assisted with Fe ions as source precursors through an impregnation-calcination method. The catalyst demonstrates a remarkable 4e – ORR activity in alkaline electrolyte with a high half-wave potential ( E 1/2 ) of up to 0.94 V, a large limiting current density ( J L ) of 5.81 mA·cm –2, and good durable stability, surpassing the benchmark Pt/C catalyst. It simultaneously displays moderate oxygen evolution reaction (OER) activity with an overpotential of 355.6 mV at 10 mA·cm –2 ( E J=10 ). Driven by a small oxygen potential gap Δ E of 0.646 V, the rechargeable zinc-air battery (ZAB) applied this catalyst as air cathode delivers a high power density of 141.7 mW·cm –2 and specific capacity of 800 mAh·g Zn –1, an excellent rate capability, and a good cycling stability over 200 h at 5 mA·cm –2 . The superior ORR activity and good ZAB performance perhaps result from the synergy of abundant available active sites mediated by Co 3 Fe 7 bimetallic alloy nanoparticles and N-doped carbon defects. This work will expand the application of non-noble metal ORR catalysts for future metal-air batteries in energy systems.