Preparation of ZnO/Co/C/RGO Composites for Enhanced Microwave Absorption
Source abstract
Abstract
ZnO/Co/C/reduced graphene oxide (RGO) composites are synthesized through carbonization of ZnCo-MOF-5/GO under an Ar/H 2 flow. The abundant active sites (e.g., functional groups and lattice defects), copious heterointerfaces (among Co, ZnO, C, and RGO), and wrinkled architecture trigger multiple dipole polarization, interface polarization, and enhanced conductive loss. By adjusting the content of RGO, the electromagnetic parameters for ZnO/Co/C/RGO composites were effectively regulated. The minimum reflection loss (RL min ) of ZnO/Co/C/RGO-50 composites is −52.72 dB at 1.70 mm, and the EAB is 3.57 GHz. Futhermore, CST simulation results further confirm the remarkable RCS reduction capacity for ZnO/Co/C/RGO-50 composites. The reduction value of RCS is 22.84 dB m 2, and effective absorption can reach the entire angle range. The superior microwave absorption property for ZnO/Co/C/RGO composites is benefited from cooperative action of dielectric loss (dipole polarization, interface polarization, conductive loss) and magnetic loss (natural resonance and exchange resonance).
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Electromagnetic wave absorption materials · Advanced Antenna and Metasurface Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Physics and Electronics
Gannan Normal University
School of Materials Science and Engineering
South China University of Technology
Funding
Bureau of Science and Technology of Ganzhou Municipality · Education Department of Jiangxi Province · National Natural Science Foundation of China · Natural Science Foundation of Jiangxi Province
References (61)
Show source-provided references
1. 10.1016/j.apsusc.2015.03.20310.1016/j.apsusc.2015.03.203 ↗
2. 10.1016/j.cej.2019.05.07910.1016/j.cej.2019.05.079 ↗
3. 10.1016/j.jallcom.2021.15896710.1016/j.jallcom.2021.158967 ↗
4. 10.1016/j.carbon.2021.02.08510.1016/j.carbon.2021.02.085 ↗
5. 10.1016/j.cej.2019.12320810.1016/j.cej.2019.123208 ↗
6. 10.1016/j.carbon.2024.11892510.1016/j.carbon.2024.118925 ↗
7. 10.1016/j.cej.2016.09.06510.1016/j.cej.2016.09.065 ↗
8. 10.1016/j.cej.2018.07.06410.1016/j.cej.2018.07.064 ↗
9. 10.1016/j.carbon.2024.11880410.1016/j.carbon.2024.118804 ↗
10. 10.1016/j.carbon.2023.01.05710.1016/j.carbon.2023.01.057 ↗
11. 10.1016/j.carbon.2022.05.04210.1016/j.carbon.2022.05.042 ↗
12. 10.1016/j.jallcom.2024.17369010.1016/j.jallcom.2024.173690 ↗
13. 10.1016/j.carbon.2022.08.09010.1016/j.carbon.2022.08.090 ↗
14. 10.1016/j.carbon.2021.09.01810.1016/j.carbon.2021.09.018 ↗
15. 10.1016/j.carbon.2023.11827810.1016/j.carbon.2023.118278 ↗
16. 10.1016/j.carbon.2023.11828010.1016/j.carbon.2023.118280 ↗
17. 10.1016/j.mtphys.2023.10096610.1016/j.mtphys.2023.100966 ↗
18. 10.1021/acsami.2c2293510.1021/acsami.2c22935 ↗
19. 10.1021/acsanm.4c0004010.1021/acsanm.4c00040 ↗
20. 10.1016/j.ceramint.2017.05.08210.1016/j.ceramint.2017.05.082 ↗
21. 10.1016/j.ceramint.2020.05.28310.1016/j.ceramint.2020.05.283 ↗
22. 10.1016/j.matchemphys.2021.12453010.1016/j.matchemphys.2021.124530 ↗
23. 10.1016/j.cej.2017.09.13910.1016/j.cej.2017.09.139 ↗
24. 10.1016/j.susmat.2020.e0021910.1016/j.susmat.2020.e00219 ↗
25. 10.1002/advs.20210555310.1002/advs.202105553 ↗
26. 10.1016/j.compositesa.2022.10706810.1016/j.compositesa.2022.107068 ↗
27. 10.1021/acssuschemeng.7b0256510.1021/acssuschemeng.7b02565 ↗
28. 10.1016/j.cej.2019.12381710.1016/j.cej.2019.123817 ↗
29. 10.1007/s42114-021-00304-210.1007/s42114-021-00304-2 ↗
30. 10.1021/acsami.1c0535110.1021/acsami.1c05351 ↗
31. 10.1016/j.jcis.2021.04.13710.1016/j.jcis.2021.04.137 ↗
32. 10.1021/acsami.1c2501910.1021/acsami.1c25019 ↗
33. 10.1016/j.carbon.2020.09.06810.1016/j.carbon.2020.09.068 ↗
34. 10.1016/j.carbon.2021.07.07210.1016/j.carbon.2021.07.072 ↗
35. 10.1016/j.ceramint.2021.05.15110.1016/j.ceramint.2021.05.151 ↗
36. 10.1016/j.carbon.2022.01.03210.1016/j.carbon.2022.01.032 ↗
37. 10.1021/acsami.6b0026410.1021/acsami.6b00264 ↗
38. 10.1016/j.jmst.2022.07.00410.1016/j.jmst.2022.07.004 ↗
39. 10.1016/j.jcis.2022.01.06310.1016/j.jcis.2022.01.063 ↗
40. 10.1016/j.jcis.2020.05.05810.1016/j.jcis.2020.05.058 ↗
41. 10.1016/j.apsusc.2020.14533610.1016/j.apsusc.2020.145336 ↗
42. 10.1016/j.carbon.2021.02.06110.1016/j.carbon.2021.02.061 ↗
43. 10.1016/j.jallcom.2018.12.24110.1016/j.jallcom.2018.12.241 ↗
44. 10.1016/j.cej.2022.13740910.1016/j.cej.2022.137409 ↗
45. 10.1016/j.jcis.2021.07.11810.1016/j.jcis.2021.07.118 ↗
46. 10.1021/acsnano.3c0217010.1021/acsnano.3c02170 ↗
47. 10.1016/j.cej.2021.13116010.1016/j.cej.2021.131160 ↗
48. 10.1016/j.carbon.2021.10.05210.1016/j.carbon.2021.10.052 ↗
49. 10.1016/j.cej.2019.01.09010.1016/j.cej.2019.01.090 ↗
50. 10.1016/j.apsusc.2021.14971510.1016/j.apsusc.2021.149715 ↗
51. 10.1016/j.apsusc.2012.06.07210.1016/j.apsusc.2012.06.072 ↗
52. 10.1016/j.jcis.2020.04.05310.1016/j.jcis.2020.04.053 ↗
53. 10.1021/acsami.9b0035610.1021/acsami.9b00356 ↗
54. 10.1016/j.jallcom.2020.15814110.1016/j.jallcom.2020.158141 ↗
55. 10.1016/j.jallcom.2017.09.31710.1016/j.jallcom.2017.09.317 ↗
56. 10.1016/j.scriptamat.2019.06.01810.1016/j.scriptamat.2019.06.018 ↗
57. 10.1021/acsaelm.3c0129610.1021/acsaelm.3c01296 ↗
58. 10.1039/C7TC03784H10.1039/C7TC03784H ↗
59. 10.1021/acssuschemeng.9b0052910.1021/acssuschemeng.9b00529 ↗
60. 10.1021/acsanm.8b0130310.1021/acsanm.8b01303 ↗
61. 10.1007/s12274-023-5799-310.1007/s12274-023-5799-3 ↗