High tolerance of the superconducting current to large grain boundary angles in potassium-doped BaFe2As2
Source abstract
Abstract
Abstract Superconducting magnets based on high-temperature superconductors (HTSs) have become critical components in cutting-edge technologies such as advanced medical applications. In HTSs, weak links of superconductivity are inevitable at high-angle grain boundaries (GBs). Thus, two adjacent grains should be crystallographically aligned within the critical angle (θ c), for which the intergrain critical current density (J c) starts to decrease exponentially. The θ c of several iron-based superconductors (IBSs) is larger than that of cuprates. However, the decreases in both θ c and intergrain J c under magnetic fields for IBSs are still substantial, hampering their applications in polycrystalline forms. Here, we report that potassium-doped BaFe2As2 (Ba122:K) exhibits superior GB performance to that of previously reported IBSs. A transport J c of over 0.1 MA/cm2 across [001]-tilt GBs with misorientation angles up to θ GB = 24° was recorded even at 28 K, which is a required level for practical applications. Additionally, even in an applied magnetic field, θ c was unaltered, and the decay of the intergrain J c was small. Our results highlight the exceptional potential of Ba122:K for polycrystalline applications and pave the way for next-generation superconducting magnets.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Iron-based superconductors research · Intellectual Capital and Performance Analysis · Corporate Taxation and Avoidance
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. Lvovsky, Y., Stautner, E. & Zhang, T. Novel technologies and configurations of superconducting magnets for MRI. Supercond. Sci. Technol. 26, 093001 (2013).10.1088/0953-2048/26/9/093001 ↗
2. Muzzi, L., Marzi, G., Zenobio, A. & Corte, A. Cable-in-conduit conductors: lessons from the recent past for future developments with low and high temperature superconductors. Supercond. Sci. Technol. 28, 053001 (2015).10.1088/0953-2048/28/5/053001 ↗
3. Uglietti, D. A review of commercial high temperature superconducting materials for large magnets: from wires and tapes to cables and conductors. Supercond. Sci. Technol. 32, 053001 (2019).10.1088/1361-6668/ab06a2 ↗
4. Franceschi, S., Kouwenhoven, L., Schönenberger, C. & Wernsdorfer, W. Hybrid superconductor–quantum dot devices. Nat. Nanotechnol. 5, 703 (2010).10.1038/nnano.2010.173 ↗
5. Nishijima, S. et al. Superconductivity and the environment: a Roadmap. Supercond. Sci. Technol. 26, 113001 (2013).10.1088/0953-2048/26/11/113001 ↗
6. Bednorz, J. & Müller, K. Possible High Tc Superconductivity in the Ba-La-Cu-O System. Z. Phys. B 64, 189 (1986).10.1007/BF01303701 ↗
7. Kamihara, Y., Watanabe, T., Hirano, M. & Hosono, H. Iron-Based Layered Superconductor La[O1-xFx]FeAs (x = 0.05–0.12) with Tc = 26 K. J. Am. Chem. Soc. 130, 3296 (2008).10.1021/ja800073m ↗
8. Driscoll, J. & Wimbush, S. Processing and application of high-temperature superconducting coated conductors. Nat. Rev. Mater. 6, 587 (2021).10.1038/s41578-021-00290-3 ↗
9. Hosono, H., Yamamoto, A., Hiramatsu, H. & Ma, Y. Recent advances in iron-based superconductors toward applications. Materials Today 21, 278 (2018).10.1016/j.mattod.2017.09.006 ↗
10. Durrell, J. et al. Bulk superconductors: a roadmap to applications. Supercond. Sci. Technol. 31, 103501 (2018).10.1088/1361-6668/aad7ce ↗
11. Hilgenkamp, H. & Mannhart, J. Grain boundaries in high-Tc superconductors. Rev. Mod. Phys. 74, 485 (2002).10.1103/RevModPhys.74.485 ↗
12. Iida, K., Hänisch, J. & Yamamoto, A. Grain boundary characteristics of Fe-based superconductors. Supercond. Sci. Technol. 33, 043001 (2020).10.1088/1361-6668/ab73ef ↗
13. Sunwong, P., Higgins, J. S., Tsui, Y., Raine, M. J. & Hampshire, D. P. The critical current density of grain boundary channels in polycrystalline HTS and LTS superconductors in magnetic fields. Supercond. Sci. Technol. 26, 095006 (2013).10.1088/0953-2048/26/9/095006 ↗
14. Choi, K. Y. et al. High and uniform critical current density for large-size YBa2Cu3O7−δ single crystals. Curr. Appl. Phys. 11, 1020 (2011).10.1016/j.cap.2011.01.016 ↗
15. Chen, Y., Wu, C., Zhao, G. & You, C. An advanced low-fluorine solution route for fabrication of high-performance YBCO superconducting films. Supercond. Sci. Technol. 25, 069501 (2012).10.1088/0953-2048/25/6/069501 ↗
16. Amrein, A., Schultz, L., Kabius, B. & Urban, K. Orientation dependence of grain-boundary critical current densities in high-Tc bicrystals. Phys. Rev. B 51, 6792–6795 (1995).10.1103/PhysRevB.51.6792 ↗
17. Hänisch, J., Attenberger, A., Holzapfel, B. & Schultz, L. Electrical transport properties of Bi2223 [001] tilt grain boundaries. Phys. Rev. B 65, 052507 (2002).10.1103/PhysRevB.65.052507 ↗
18. Held, R. et al. Low-angle grain boundaries in YBa2Cu3O7−δ with high critical current densities. Phys. Rev. B 79, 014515 (2009).10.1103/PhysRevB.79.014515 ↗
19. Iijima, Y., Tanabe, N., Ikeno, Y. & Kohno, O. Biaxially aligned YBa2Cu3O7−x thin film tapes. Physica C 185, 189–1959 (1991).
20. Wu, X. D. et al. Properties of YBa2Cu3O7−δ thick films on flexible buffered metallic substrates. Appl. Phys. Lett. 67, 2397 (1995).10.1063/1.114559 ↗
21. Goyal, A. et al. High critical current density superconducting tapes by epitaxial deposition of YBa2Cu3Ox thick films on biaxially textured metals. Appl. Phys. Lett. 69, 1795 (1996).10.1063/1.117489 ↗
22. Katase, T. et al. Advantageous grain boundaries in iron pnictide superconductors. Nat. Commun. 2, 409 (2011).10.1038/ncomms1419 ↗
23. Si, W. et al. Grain boundary junctions of FeSe0.5Te0.5 thin films on SrTiO3 bi-crystal substrates. Appl. Phys. Lett. 106, 032602 (2015).10.1063/1.4906429 ↗
24. Sarnelli, E. et al. Properties of Fe(Se, Te) bicrystal grain boundary junctions, SQUIDs, and nanostrips. IEEE. Trans. Appl. Supercond. 27, 7400104 (2017).10.1109/TASC.2016.2636248 ↗
25. Iida, K., Omura, T., Matsumoto, T., Hatano, T. & Ikuta, H. Grain boundary characteristics of oxypnictide NdFeAs(O,F) superconductors. Supercond. Sci. Technol. 32, 074003 (2019).10.1088/1361-6668/ab1660 ↗
26. Omura, T., Matsumoto, T., Hatano, T., Iida, K. & Ikuta, H. Fabrication of grain boundary junctions using NdFeAs(O,F) superconducting thin films. J. Phys.: Conf. Ser. 1054, 012024 (2018).
27. Rotter, M., Tegel, M. & Johrendt, D. Superconductivity at 38 K in the Iron Arsenide (Ba1−xKx)Fe2As2. Phys. Rev. Lett. 101, 107006 (2008).10.1103/PhysRevLett.101.107006 ↗
28. Weiss, J. D. et al. High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks. Nat. Mater. 11, 682 (2012).10.1038/nmat3333 ↗
29. Wang, D. et al. First performance test of a 30 mm iron-based superconductor single pancake coil under a 24 T background field. Supercond. Sci. Technol. 32, 04LT01 (2019).10.1088/1361-6668/ab09a4 ↗
30. Cheng, Z. et al. Strengthened proximity effect at grain boundaries to enhance inter-grain supercurrent in Ba1-xKxFe2As2 superconductors. Materials Today Phys 28, 100848 (2022).10.1016/j.mtphys.2022.100848 ↗
31. Weiss, J. D. et al. Demonstration of an iron-pnictide bulk superconducting magnet capable of trapping over 1 T. Supercond. Sci. Technol. 28, 112001 (2015).10.1088/0953-2048/28/11/112001 ↗
32. Tokuta, S., Hasegawa, Y., Shimada, Y. & Yamamoto, A. Enhanced critical current density in K-doped Ba122 polycrystalline bulk superconductors via fast densification. iScience 25, 103992 (2022).10.1016/j.isci.2022.103992 ↗
33. Qin, D. et al. Realization of epitaxial thin films of the superconductor K-doped BaFe2As2. Phys. Rev. Mater. 5, 014801 (2021).10.1103/PhysRevMaterials.5.014801 ↗
34. Qin, D. et al. K-doped Ba122 epitaxial thin film on MgO substrate by buffer engineering. Supercond. Sci. Technol. 35, 09LT01 (2022).10.1088/1361-6668/ac8025 ↗
35. Iida, K. et al. Approaching the ultimate superconducting properties of (Ba,K)Fe2As2 by naturally formed low-angle grain boundary networks. NPG Asia Mater 13, 68 (2021).10.1038/s41427-021-00337-5 ↗
36. Rotter, M., Pangerl, M., Tegel, M. & Johrendt, D. Superconductivity and Crystal Structures of (Ba1−xKx)Fe2As2 (x = 0–1). Angew. Chem. Int. Ed. 47, 7949 (2008).10.1002/anie.200803641 ↗
37. Ishida, S. et al. Doping-dependent critical current properties in K, Co, and P-doped BaFe2As2 single crystals. Phys. Rev. B 95, 014517 (2017).10.1103/PhysRevB.95.014517 ↗
38. Verebelyi, D. et al. Low angle grain boundary transport in YBa2Cu3O7−δ coated conductors. Appl. Phys. Lett. 76, 1755 (2000).10.1063/1.126157 ↗
39. Hilgenkamp, H. & Mannhart, J. Superconducting and normal-state properties of YBa2Cu3O7-δ-bicrystal grain boundary junctions in thin films. Appl. Phys. Lett. 73, 265 (1998).10.1063/1.121775 ↗
40. Guo, Z. et al. Nanoscale texture and microstructure in a NdFeAs(O,F)/IBAD-MgO superconducting thin film with superior critical current properties. ACS Appl. Electron. Mater. 3, 3158 (2021).10.1021/acsaelm.1c00364 ↗