Approaching the ultimate superconducting properties of (Ba,K)Fe2As2 by naturally formed low-angle grain boundary networks
Source abstract
Abstract
Abstract The most effective way to enhance the dissipation-free supercurrent in the presence of a magnetic field for type II superconductors is to introduce defects that act as artificial pinning centers (APCs) for vortices. For instance, the in-field critical current density of doped BaFe2As2 (Ba122), one of the most technologically important Fe-based superconductors, has been improved over the last decade by APCs created by ion irradiation. The technique of ion irradiation has been commonly implemented to determine the ultimate superconducting properties. However, this method is rather complicated and expensive. Here, we report a surprisingly high critical current density and strong pinning efficiency close to the crystallographic c-axis for a K-doped Ba122 epitaxial thin film without APCs, achieving performance comparable to ion-irradiated K-doped Ba122 single crystals. Microstructural analysis reveals that the film is composed of columnar grains with widths of approximately 30–60 nm. The grains are rotated around the b- (or a-) axis by 1.5° and around the c-axis by −1°, resulting in the formation of low-angle grain boundary networks. This study demonstrates that the upper limit of in-field properties reached in ion-irradiated K-doped Ba122 is achievable by grain boundary engineering, which is a simple and industrially scalable manner.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Iron-based superconductors research · Physics of Superconductivity and Magnetism · Rare-earth and actinide compounds
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (38)
Show source-provided references
1. Hiramatsu, H., Katase, T., Kamiya, T. & Hosono, H. Thin film growth and device fabrication of iron-based superconductors. J. Phys. Soc. Jpn. 81, 011011 (2012).10.1143/JPSJ.81.011011 ↗
2. Li, Q., Si, W. & Dimitrov, I. K. Films of iron chalcogenide superconductors. Rep. Prog. Phys. 74, 124510 (2011).10.1088/0034-4885/74/12/124510 ↗
3. Iida, K., Hänisch, J. & Tarantini, C. Fe-based superconducting thin films on metallic substrates: Growth, characteristics, and relevant properties. Appl. Phys. Rev. 5, 031304 (2018).10.1063/1.5032258 ↗
4. Sakoda, M., Iida, K. & Naito, M. Recent progress in thin film growth of Fe-based superconductors: superior superconductivity achieved by thin films. Supercond. Sci. Technol. 31, 093001 (2018).10.1088/1361-6668/aabddb ↗
5. Hänisch, J., Iida, K., Hühne, R. & Tarantini, C. Fe-based superconducting thin films-preparation and tuning of superconducting properties. Supercond. Sci. Technol. 32, 093001 (2019).10.1088/1361-6668/ab1c00 ↗
6. Qin, D. et al. A. Realization of epitaxial thin films of the superconductor K-doped BaFe2As2. Phys. Rev. Mater. 5, 014801 (2021).10.1103/PhysRevMaterials.5.014801 ↗
7. Iida, K., Hänisch, J. & Yamamoto, A. Grain boundary characteristics of Fe-based superconductors. Supercond. Sci. Technol. 33, 043001 (2020).10.1088/1361-6668/ab73ef ↗
8. Hänisch, J. & Iida, K. Superconductivity From Materials Science to Practical Applications 269–302, ch 10 (Springer, 2020).10.1007/978-3-030-23303-7_10 ↗
9. Katase, T. et al. Biaxially textured cobalt-doped BaFe2As2 films with high critical current density over 1 MA/cm2 on MgO-buffered metal-tape flexible substrates. Appl. Phys. Lett. 98, 242510 (2011).10.1063/1.3599844 ↗
10. Sato, H., Hiramatsu, H., Kamiya, T. & Hosono, H. Enhanced critical-current in P-doped BaFe2As2 thin films on metal substrates arising from poorly aligned grain boundaries. Sci. Rep. 6, 36828 (2016).10.1038/srep36828 ↗
11. Xu, Z., Yuan, P., Fan, F., Chen, Y. & Ma, Y. Transport properties and pinning analysis for Co-doped BaFe2As2 thin films on metal tapes. Supercond. Sci. Technol. 31, 055001 (2018).10.1088/1361-6668/aab261 ↗
12. Iida, K. et al. High-field transport properties of a P-doped BaFe2As2 film on technical substrate. Sci. Rep. 7, 39951 (2017).10.1038/srep39951 ↗
13. Fang, L. et al. Huge critical current density and tailored superconducting anisotropy in SmFeAsO0.8F0.15 by low-density columnar-defect incorporation. Nat. Commun. 4, 2655 (2013).10.1038/ncomms3655 ↗
14. Taen, T., Ohtake, F., Pyon, S., Tamegai, T. & Kitamura, H. Critical current density and vortex dynamics in pristine and proton-irradiated Ba0.6K0.4Fe2As2. Supercond. Sci. Technol. 28, 085003 (2015).10.1088/0953-2048/28/8/085003 ↗
15. Takahashi, A. et al. Effects of splyaed columnar defects on critical current density in CaKFe4As4. J. Phys.: Conf. Ser. 1590, 012015 (2020).
16. Mishev, V., Nakajima, M., Eisaki, H. & Eisterer, M. Effects of introducing isotropic artificial defects on the superconducting properties of differently doped Ba-122 based single crystals. Sci. Rep. 6, 27783 (2015).10.1038/srep27783 ↗
17. Fang, L. et al. High, magnetic field independent critical currents in (Ba,K)Fe2As2 crystals. Appl. Phys. Lett. 101, 012601 (2012).10.1063/1.4731204 ↗
18. Rauch, E. F. et al. Automated nanocrystal orientation and phase mapping in the transmission electron microscope on the basis of precession electron diffraction. Z. Kristallogr. 225, 103–109 (2010).10.1524/zkri.2010.1205 ↗
19. Zaikina, J. V. et al. Facile synthesis of Ba1–xKxFe2As2 superconductors via hydride route. J. Am. Chem. Soc. 136, 16932–16939 (2014).10.1021/ja509907r ↗
20. Cheetham, A. K., Fender, B. E. F. & Cooper, M. J. Defect structure of calcium fluoride containing excess anions I. Bragg scattering. J. Phys. C. 4, 3107–3121 (1971).10.1088/0022-3719/4/18/016 ↗
21. Jaroszynski, J. et al. Upper critical fields and thermally-activated transport NdFeAsO0.7F0.3 single crystal. Phys. Rev. B 78, 174523 (2008).10.1103/PhysRevB.78.174523 ↗
22. Lee, N., Jung, S.-G., Kim, D. & Kang, W. Potassium-doped BaFe2As2 superconducting thin films with a transition temperature of 40 K. Appl. Phys. Lett. 96, 202505 (2010).10.1063/1.3431583 ↗
23. Ishida, S. et al. Doping-dependent critical current properties in K, Co, and P-doped BaFe2As2 single crystals. Phys. Rev. B 95, 014517 (2017).10.1103/PhysRevB.95.014517 ↗
24. Horide, T. et al. Influence of matching field on critical current density and irreversibility temperature in YBa2Cu3O7 films with BaMO3 (M=Zr, Sn, Hf) nanorods. Appl. Phys. Lett. 108, 082601 (2016).10.1063/1.4942463 ↗
25. Palstra, T. T. M., Batlogg, B., Schneemeyer, L. F. & Waszczak, J. V. Thermally activated dissipation in Bi2.2Sr2Ca0.8Cu2O8+δ. Phys. Rev. Lett. 61, 1662–1665 (1989).10.1103/PhysRevLett.61.1662 ↗
26. Wang, X.-L. et al. Very strong intrinsic flux pinning and vortex avalanches in (Ba,K)Fe2As2 superconducting single crystals. Phys. Rev. B 82, 024525 (2010).10.1103/PhysRevB.82.024525 ↗
27. Geshkenbein, V., Larkin, A., Feigel’man, M. & Vinokur, V. Flux pinning and creep in high-Tc superconductors. Phys. C. 162-164, 239–240 (1989).10.1016/0921-4534(89)91006-X ↗
28. Blatter, G., Feigel’man, M. V., Geshkenbin, V. B., Larkin, A. I. & Vinokur, V. M. Vortices in high-temperature superconductors. Rev. Mod. Phys. 66, 1125–1388 (1994).10.1103/RevModPhys.66.1125 ↗
29. Tarantini, C. et al. Strong vortex pinning in Co-doped BaFe2As2 single crystal thin films. Appl. Phys. Lett. 96, 142510 (2010).10.1063/1.3383237 ↗
30. Matsui, H. et al. 4-fold enhancement in the critical current density of YBa2Cu3O7 films by practical ion irradiation. Appl. Phys. Lett. 101, 232601 (2012).10.1063/1.4769836 ↗
31. Opherden, L. et al. Large pinning forces and matching effects in YBa2Cu3O7-δ thin films with Ba2Y(Nb/Ta)O6 nano-precipitates. Sci. Rep. 6, 21188 (2016).10.1038/srep21188 ↗
32. Xu, A. et al. Broad temperature pinning study of 15 mol.% Zr-added (Gd,Y)-Ba-Cu-O MOCVD coated conductors. IEEE Trans. Appl. Supercond. 25, 6603105 (2015).
33. Kitaguchi, H. et al. MgB2 films with very high critical current densities due to strong grain boundary pinning. Appl. Phys. Lett. 85, 2842–2844 (2004).10.1063/1.1805195 ↗
34. Sun, G. L. et al. Single crystal growth and effect of doping on structural, transport and magnetic properties of A1-xKxFe2As2 (A=Ba, Sr). J. Supercond. Nov. Magn. 24, 1773–1785 (2011).10.1007/s10948-010-1123-z ↗
35. Dirks, A. G. & Leamy, H. J. Columnar microstructure in vapor-deposited thin films. Thin Solid Films 47, 219–233 (1977).10.1016/0040-6090(77)90037-2 ↗
36. Yuan, P. et al. Vortex pinning properties in Co-doped BaFe2As2 thin films with a high critical current density over 2 MA cm-2 at 9 T. Supercond. Sci. Technol. 30, 025001 (2016).10.1088/0953-2048/30/2/025001 ↗
37. Lee, J. et al. High critical current density over 1 MAcm-2 at 13 T in BaZrO3 incorporated Ba(Fe,Co)2As2 thin film. Supercond. Sci. Technol. 30, 085006 (2017).10.1088/1361-6668/aa73f5 ↗
38. Miura, M. et al. Enhanced critical current density in BaFe2(As0.66P0.33)2 nanocomposite superconducting films. Supercond. Sci. Technol. 32, 064005 (2019).10.1088/1361-6668/ab0faf ↗