Preparation and properties of a novel decorative base paper for formaldehyde-free adhesive impregnation
Source abstract
Abstract
Abstract Formaldehyde-free adhesives are gaining attention due to their compatibility with green production methods. Decorative base paper (DBP) is known for its physical strength and printability and has a high ability for absorbing aldehyde-free adhesives for impregnation. In this paper, DBP was prepared with TiO2 and SiO2 combined with polyvinyl alcohol (PVA), where the amount of TiO2 was reduced in the pulp process. The prepared DBP was impregnated by aldehyde-free adhesive and hot-pressed on wood-based panels. The results showed that upon SiO2 coating, the surface smoothness of base paper increased by 132.3 %, whereas the tensile strength increased by 33.6 %. Furthermore, the colour density of cyan, magenta, yellow and black colours increased by 75.4 %, 99.2 %, 51.9 % and 90.5 %, respectively. The surface properties like surface bonding strength and wear resistance of the covered wood-based panels were found to satisfy the standard requirements, which indicates the products can be used for furniture products.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Material Properties and Processing · Advanced Cellulose Research Studies · Lignin and Wood Chemistry
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Research Institute of Wood Industry , Chinese Academy of Forestry , Beijing , People’s Republic of China
Funding
National Nonprofit Institute Research Grant of CAF
References (31)
Show source-provided references
1. Abdelatif, Y., Gaber, A.-A.M., Fouda, A.E.-A.S., and Elsokkary, T. (2022). Sustainable utilization of calcined sugarcane mud waste as nanofiller for fine paper production. Biomass Convers. Biorefinery, https://doi.org/10.1007/s13399-022-03571-1.10.1007/s13399-022-03571-1 ↗
2. Bhardwaj, S. and Bhardwaj, N.K. (2019). Mixing of oxidized starch and polyvinyl alcohol for surface sizing of paper. Nord. Pulp Pap. Res. J. 34: 343–353, https://doi.org/10.1515/npprj-2018-0063.10.1515/npprj-2018-0063 ↗
3. Gadhave, R.V., Kasbe, P.S., Mahanwar, P.A., and Gadekar, P.T. (2019). Synthesis and characterization of lignin-polyurethane based wood adhesive. Int. J. Adhesion Adhes. 95: 102427, https://doi.org/10.1016/j.ijadhadh.2019.102427.10.1016/j.ijadhadh.2019.102427 ↗
4. Huang, Q., Xu, M., Sun, R., and Wang, X. (2016). Large scale preparation of graphene oxide/cellulose paper with improved mechanical performance and gas barrier properties by conventional papermaking method. Ind. Crop. Prod. 85: 198–203, https://doi.org/10.1016/j.indcrop.2016.03.006.10.1016/j.indcrop.2016.03.006 ↗
5. Huang, X., Shen, J., and Qian, X. (2013). Filler modification for papermaking with starch/oleic acid complexes with the aid of calcium ions. Carbohydr. Polym. 98: 931–935, https://doi.org/10.1016/j.carbpol.2013.07.024.10.1016/j.carbpol.2013.07.024 ↗
6. Jeong, B., Park, B.-D., and Causin, V. (2019). Influence of synthesis method and melamine content of urea-melamine-formaldehyde resins to their features in cohesion, interphase, and adhesion performance. J. Ind. Eng. Chem. 79: 87–96, https://doi.org/10.1016/j.jiec.2019.05.017.10.1016/j.jiec.2019.05.017 ↗
7. Kan, Y.F., Sun, B., Kan, H.F., Bai, Y.M., and Gao, Z.H. (2021). Preparation and characterization of a melamine-urea-glyoxal resin and its modified soybean adhesive. Int. J. Adhesion Adhes. 111: 102986, https://doi.org/10.1016/j.ijadhadh.2021.102986.10.1016/j.ijadhadh.2021.102986 ↗
8. Kandelbauer, A., Petek, P., Medved, S., Pizzi, A., and Teischinger, A. (2010). On the performance of a melamine–urea–formaldehyde resin for decorative paper coatings. Eur. J. Wood. Wood. Prod. 68: 63–75, https://doi.org/10.1007/s00107-009-0352-y.10.1007/s00107-009-0352-y ↗
9. Kentta, E., Lamminmaki, T., Rautkoski, H., Teir, S., Bacher, J., Kettle, J., and Sarlin, J. (2013). Silica pigment produced from silicate mining sidestreams for ink-jet paper coating application. Nord. Pulp Pap. Res. J. 28: 22–27, https://doi.org/10.3183/npprj-2013-28-01-p022-027.10.3183/npprj-2013-28-01-p022-027 ↗
10. Khwaldia, K. (2013). Physical and mechanical properties of hydroxypropyl methylcellulose–coated paper as affected by coating weight and coating composition. Bioresources 8: 3438–3452, https://doi.org/10.15376/biores.8.3.3438-3452.10.15376/biores.8.3.3438-3452 ↗
11. Kwon, S., Oh, K., Shin, S.J., and Lee, H.L. (2020). Effects of hydroxyethyl methacrylate comonomer in styrene/acrylate latex on coating structure and printability. Prog. Org. Coat. 147: 105862, https://doi.org/10.1016/j.porgcoat.2020.105862.10.1016/j.porgcoat.2020.105862 ↗
12. Lin, C.C., Chang, F.L., Perng, Y.S., and Yu, S.-T. (2016). Effects of single and blended coating pigments on the inkjet image quality of dye sublimation transfer printed paper: SiO2, CaCO3, talc, and sericite. Adv. Mater. Sci. Eng., https://doi.org/10.1155/2016/4863024.10.1155/2016/4863024 ↗
13. McCreath, S., Boinard, P., Boinard, E., Gritter, P., and Liggat, J.J. (2018). High clarity poly(caprolactone diol)-based polyurethane adhesives for polycarbonate lamination: effect of isocyanate and chain-extender. Int. J. Adhesion Adhes. 86: 84–97, https://doi.org/10.1016/j.ijadhadh.2018.08.003.10.1016/j.ijadhadh.2018.08.003 ↗
14. Morsy, F.A., El-Sherbiny, S., Hassan, M.S., and Mohammed, H.F. (2014). Modification and evaluation of Egyptian kaolinite as pigment for paper coating. Powder Technol. 264: 430–438, https://doi.org/10.1016/j.powtec.2014.05.040.10.1016/j.powtec.2014.05.040 ↗
15. Oh, K., Abhari, A.R., Im, W., and Lee, H.L. (2019). Stress development in a cellulose-nanofibril-containing pigment coating layer during drying. Ind. Eng. Chem. Res. 58: 18187–18196, https://doi.org/10.1021/acs.iecr.9b02906.10.1021/acs.iecr.9b02906 ↗
16. Ozcan, A., Sonmez, S., and Tutak, D. (2022). Effect of coating pigment type on paper printability with water-based inks. J. Coat. Technol. Res. 19: 1149–1157, https://doi.org/10.1007/s11998-021-00593-8.10.1007/s11998-021-00593-8 ↗
17. Peng, Y., He, B.H., and Zhao, L.H. (2015). The effect of pre-flocculation of lime mud by wet-end additives on paper properties. Nord. Pulp. Pap. Res. J. 30: 243–249, https://doi.org/10.3183/npprj-2015-30-02-p243-249.10.3183/npprj-2015-30-02-p243-249 ↗
18. Shen, J., Song, Z., Qian, X., and Yang, F. (2010). Carboxymethyl cellulose/alum modified precipitated calcium carbonate fillers: preparation and their use in papermaking. Carbohydrate Polym. 81: 545–553, https://doi.org/10.1016/j.carbpol.2010.03.012.10.1016/j.carbpol.2010.03.012 ↗
19. Song, S., Zhang, M., He, Z., Li, J.Z., and Ni, Y. (2012). Investigation on a novel fly ash based calcium silicate filler: effect of particle size on paper properties. Ind. Eng. Chem. Res. 51: 16377–16384, https://doi.org/10.1021/ie3028813.10.1021/ie3028813 ↗
20. Songfeng, E., Ning, D., Wang, Y., Huang, J., Jin, Z., Ma, Q., Yang, K., and Lu, Z. (2020). Ternary synergistic strengthening and toughening of bio-inspired TEMPO-oxidized cellulose nanofibers/borax/polyvinyl alcohol composite film with high transparency. ACS Sustain. Chem. Eng. 8: 15661–15669, https://doi.org/10.1021/acssuschemeng.0c05292.10.1021/acssuschemeng.0c05292 ↗
21. Songok, J., Bousfield, D., Ridgway, C., Gane, P., and Toivakka, M. (2012). Drying of porous coating: influence of coating composition. Ind. Eng. Chem. Res. 51: 13680–13685, https://doi.org/10.1021/ie301624e.10.1021/ie301624e ↗
22. Sonmez, S. (2017). Investigation of effect of hot-folio printability of mineral pigments. Oxid. Commun. 40: 963–972.
23. Sousa, S., Costa, A.P., and Simões, R. (2019). Poly(lactic acid) composites reinforced with Kraft pulp fibres: production by a papermaking process and characterisation. Compos. Appl. Sci. Manuf. 121: 273–282, https://doi.org/10.1016/j.compositesa.2019.03.024.10.1016/j.compositesa.2019.03.024 ↗
24. Xiong, X.Q., Yuan, Y.Y., Niu, Y.T., and Zhang, L.T. (2020). Development of a cornstarch adhesive for laminated veneer lumber bonding for use in engineered wood flooring. Int. J. Adhesion Adhes. 98: 1–5.10.1016/j.ijadhadh.2019.102534 ↗
25. Xu, J.F., Li, X.Y., Liu, R., Shang, Z., Long, L., Qiu, H.Y., and Ni, Y.H. (2020). Dialdehyde modified cellulose nanofibers enhanced the physical properties of decorative paper impregnated by aldehyde-free adhesive. Carbohydrate Polym. 250: 116941, https://doi.org/10.1016/j.carbpol.2020.116941.10.1016/j.carbpol.2020.116941 ↗
26. Xu, J.F., Long, L., and Yu, J.H. (2015). Preparation and characterization of self-emulsifying styrene acrylate emulsion used as surface-treatment agent for decorative base paper. Sci. Silvae Sin. 51: 116–123.
27. Yoon, S.Y. and Deng, Y.L. (2007). Experimental and modeling study of the strength properties of clay-starch composite filled papers. Ind. Eng. Chem. Res. 46: 4883–4890, https://doi.org/10.1021/ie0613523.10.1021/ie0613523 ↗
28. Zhang, Z., Zhang, Q., Zhang, M., Huang, R., and Han, Y. (2018). Effect of pigment sizing on printability and coating structure of decorative base paper. Nord. Pulp Pap. Res. J. 33: 105–112, https://doi.org/10.3183/npprj-2018-33-01-p112-118.10.1515/npprj-2018-3005 ↗
29. Zhou, Y., Zeng, G., Zhang, F., Luo, J., Li, X., Li, J., and Fang, Z. (2021). Toward utilization of agricultural wastes: development of a novel keratin reinforced soybean meal-based adhesive. ACS Sustain. Chem. Eng. 9: 7630–7637, https://doi.org/10.1021/acssuschemeng.1c01920.10.1021/acssuschemeng.1c01920 ↗
30. Zhu, P., Kuang, Y., Chen, G., Liu, Y., Peng, C., Hu, W., Zhou, P., and Fang, Z. (2017). Starch/polyvinyl alcohol (PVA)-coated painting paper with exceptional organic solvent barrier properties for art preservation purposes. J. Mater. Sci. 53: 5450–5457, https://doi.org/10.1007/s10853-017-1924-6.10.1007/s10853-017-1924-6 ↗
31. Zhu, W.K., Ji, M.X., Chen, F.Q., Wang, Z., Chen, W., Xue, Y.Y., and Zhang, Y. (2020). Formaldehyde‐free resin impregnated paper reinforced with cellulose nanocrystal (CNC): formulation and property analysis. J. Appl. Polym. Sci. 137: 1–10, https://doi.org/10.1002/app.48931.10.1002/app.48931 ↗