Application of carboxymethyl cellulose-acrylate-OVPSS graft copolymer emulsion in paper reinforcement and protection
Source abstract
Abstract
Abstract Paper cultural relics are both precious, inheritable and fragile. However, with the passage of time, paper will also be affected by a variety of factors, and will appear mildew, yellow, brittle, or even completely damaged. In order to protect the cultural relics, extend lifespan paper, CMC-acrylate-OVPOSS graft copolymerization emulsion was synthesized by using carboxymethyl cellulose (CMC) as substrate, methyl methacrylate (MMA), butyl acrylate (BA), glycidyl methacrylate (GMA), hydroxyethyl methacrylate (HEMA), octavinyl polyhedral oligomeric silsesquioxane (OVPOSS) as graft copolymer. The CMC-acrylate-OVPOSS emulsion was coated on the surface of the paper to test its protective effect on the paper. The results showed that the mass concentration of 10 % reinforcement solution coated on the paper, mechanical properties of paper were greatly improved, and the gloss and whiteness of paper were slightly changed, the paper also had a certain aging resistance and acid and alkali corrosion resistance. At the same time, the reversibility experiment showed that the reinforcement material had a certain reversibility.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Building materials and conservation · Advanced Cellulose Research Studies · Cultural Heritage Materials Analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Chemical Engineering , 12636 Zhengzhou University , No. 100 Science Road , Zhengzhou , Henan , China (present address)
Zhengzhou Museum , Zhengzhou , China
References (39)
Show source-provided references
1. Afsharpour, M., Rad, F.T., Malekian, H. (2011) New cellulosic titanium dioxide nanocomposite as a protective coating for preserving paper-art-works. J. Cult. Heritage 12(4):380–383.10.1016/j.culher.2011.03.001 ↗
2. Anagnostopoulos, C.A., Tsiatis, M. (2016) Experimental data on the properties of polymer-modified cement grouts using epoxy and acrylic resin emulsions. Data Brief 9:463–469.10.1016/j.dib.2016.09.016 ↗
3. Ariafar, A.A., Afsharpour, M., Samanian, K. (2018) Use of TiO2/chitosan nanoparticles for enhancing the preservative effects of carboxymethyl cellulose in paper-art-works against biodeterioration. Int. Biodeterior. Biodegrad. 131:67–77.10.1016/j.ibiod.2017.04.025 ↗
4. Bergamonti, L., Potenza, M., Haghighi Poshtiri, A., Lorenzi, A., Sanangelantoni, A.M., Lazzarini, L., Lottici, P.P., Graiff, C. (2020) Ag-functionalized nanocrystalline cellulose for paper preservation and strengthening. Carbohydr. Polym. 231:115773.10.1016/j.carbpol.2019.115773 ↗
5. Chen, F., Dong, W., Lin, F., Ren, W., Ma, X. (2021) Composite proton exchange membrane with balanced proton conductivity and swelling ratio improved by gradient-distributed POSS nanospheres. Compos. Commun. 24:100676.10.1016/j.coco.2021.100676 ↗
6. Cong, C., Cui, C., Meng, X., Zhou, Q. (2014) Stability of POSS crosslinks and aggregates in tetrafluoroethylene-propylene elastomers/OVPOSS composites exposed to hydrochloric acid solution. Polym. Degrad. Stab. 100:29–36.10.1016/j.polymdegradstab.2013.12.032 ↗
7. Dong, Z., Xu, Z. (2012) Dynamic mechanical properties of paper. Guangxi J. Light Ind. 29(6):19–20.
8. Estan-Cerezo, G., Alonso, D.A., Martín-Martínez, J.M. (2017) Reactivity of novel ethyl cyanoacrylate and 6-hydroxyhexyl acrylate adhesive mixtures and their influence on adhesion and thermal stability. Eur. Polym. J. 88:75–92.10.1016/j.eurpolymj.2017.01.010 ↗
9. Feng, J., Ma, J., Pang, X., Tang, B. (2020) Non-destructive quantitative analysis of nano-mechanics of aged Xuan paper. J. Cult. Heritage 46:155–158.10.1016/j.culher.2020.06.002 ↗
10. Gheno, G., Badetti, E., Brunelli, A., Ganzerla, R., Marcomini, A. (2018) Consolidation of Vicenza, Arenaria and Istria stones: A comparison between nano-based products and acrylate derivatives. J. Cult. Heritage 32:44–52.10.1016/j.culher.2018.02.013 ↗
11. Guo, X., Ge, S., Wang, J., Zhang, X., Zhang, T., Lin, J., Zhao, C.X., Wang, B., Zhu, G., Guo, Z. (2018) Waterborne acrylic resin modified with glycidyl methacrylate (GMA): Formula optimization and property analysis. Polymer 143:155–163.10.1016/j.polymer.2018.04.020 ↗
12. Huang, X., Sun, J., Lv, K., Liu, J., Shen, H., Zhang, F. (2018) Application of core-shell structural acrylic resin/nano-SiO2 composite in water based drilling fluid to plug shale pores. J. Nat. Gas Sci. Eng. 55:418–425.10.1016/j.jngse.2018.05.023 ↗
13. Jia, M., Zhang, X., Weng, J., Zhang, J., Zhang, M. (2019) Protective coating of paper works: ZnO/cellulose nanocrystal composites and analytical characterization. J. Cult. Heritage 38:64–74.10.1016/j.culher.2019.02.006 ↗
14. Jin, S.-S., Qi, Y.-P., Shen, Y.-F., Li, H. (2019) The application of organosilicon modified polyurethane in reinforcing traditional paper. Nord. Pulp Pap. Res. J. 34:485–494.10.1515/npprj-2019-0014 ↗
15. Lei, H., He, D., Guo, Y., Tang, Y., Huang, H. (2018) Synthesis and characterization of UV-absorbing fluorine-silicone acrylic resin polymer. Appl. Surf. Sci. 442:71–77.10.1016/j.apsusc.2018.02.134 ↗
16. Li, P. (2011) A brief discussion on the damage causes and protection measures of paper cultural relics. Silk Road 19(24):96–97.
17. Li, Q., Xi, S., Zhang, X. (2014) Conservation of paper relics by electrospun PVDF fiber membranes. J. Cult. Heritage 15(4):359–364.10.1016/j.culher.2013.09.003 ↗
18. Li, Z., Huang, K. (2005) Discussion on the protection of books and archives data from the chemical composition of paper. J. Educ. Inst. Jilin Prov. 21(2):12–15.
19. Liu, J., Su, X., Nan, Y., Wu, Z., Liu, R. (2021) Synthesis of three kinds of multi-armed cardanol-based acrylic resins based on different routes for UV/EB-cured coatings. Prog. Org. Coat. 151:106035.10.1016/j.porgcoat.2020.106035 ↗
20. Liu, R., Qiu, Y. (2013) A silk screen for strengthening paper[P/OL]. 103114500A, 2013-03-07.
21. Mishra, R.K., Sabu, A., Tiwari, S.K. (2018) Materials chemistry and the futurist eco-friendly applications of nanocellulose: Status and prospect. J. Saudi Chem. Soc. 22(8):949–978.10.1016/j.jscs.2018.02.005 ↗
22. Ozimek, J., Sternik, D., Radzik, P., Hebda, E., Pielichowski, K. (2021) Thermal degradation of POSS-containing nanohybrid linear polyurethanes based on 1,6-hexamethylene diisocyanate. Thermochim. Acta 697:178851.10.1016/j.tca.2020.178851 ↗
23. Pan, C. (2019) Study on the reinforcement of old newsprint with cellulose derivatives. Master. Guangdong Univ. Techno.
24. Pi, P., Hou, K., Wen, X., Xu, S., Cheng, J., Xu, G., Wang, S. (2016) A facile one-step fabrication of robust superhydrophobic/superoleophilic cotton fabric using a crosslinkable POSS-containing fluorinated copolymer. Prog. Org. Coat. 101:522–529.10.1016/j.porgcoat.2016.09.023 ↗
25. Santos, D.M.D., Nagay, B.E., Silva, E.V.F., Bonatto, L.R., Sonego, M.V., Moreno, A., Rangel, E.C., Cruz, N.C., Goiato, M.C. (2016) In vitro analysis of different properties of acrylic resins for ocular prosthesis submitted to accelerated aging with or without photopolymerized glaze. Mater. Sci. Eng. C: Mater. Biol. Appl. 69:995–1003.10.1016/j.msec.2016.07.081 ↗
26. Standards, T.C.N. (2002a) Chinese standard: paper and board-Determination of tearing resistance. GB/T 455-2002, Beijing, China: The Chinese National Standards.
27. Standards, T.C.N. (2002b) Chinese standard: paper, board and pulp-Measurement of brightness. GB/T 7974-2002, Beijing, China: The Chinese National Standards.
28. Standards, T.C.N. (2008a) Chinese standard: paper and board – Accelerated aging. GB/T 464-2008, Beijing, China: The Chinese National Standards.
29. Standards, T.C.N. (2008b) Chinese standard: paper and board-Determination of folding endurance. GB/T 457-2008, Beijing, China: The Chinese National Standards.
30. Standards, T.C.N. (2008c) Chinese standard: paper and board-Determination of tensile properties. GB/T12914-2008, Beijing, China: The Chinese National Standards.
31. Standards, T.C.N. (2013) Chinese standard: paper and board-Measurement of specular gloss. GB/T 8941-2013, Beijing, China: The Chinese National Standards.
32. Sun, Z. (2020) The understanding and Research on the protection and restoration of paper cultural relics. Panor. Chin. Natl. 24(12):197–198.
33. Sun, M., Wang, J., Zhang, H., Zhang, B., Fan, Z., Su, B. (2015) Measurement of the reversible rate of conservation materials for ancient murals. J. Cult. Herit. 16(1):49–56.10.1016/j.culher.2014.01.010 ↗
34. Wang, M., Wang, M., Zhou, J., Chen, W., Ren, W. (2019) Properties of EPDM rubber modified by octavinyl silsequioxane. China Elastomerics 29(3):28–31.
35. Xu, B. (2020) Discussion on the protection of paper cultural relics in museums. Identi. Appreci. Cult. Relics 11(19):106–107.
36. Xu, J., Zhang, T., Jiang, Y., Chen, Q., Yang, D., Yu, Z. (2020) Synthesis of microcrystalline cellulose/TiO2/fluorine/styrene-acrylate coatings and the application for simulated paper cultural relic protection. Cellulose 27:1–14.10.1007/s10570-020-03210-w ↗
37. Zervos, S. (2013) Revising established tenets in paper conservation. Proc., Soc. Behav. Sci. 73:35–42.10.1016/j.sbspro.2013.02.016 ↗
38. Zhang, X. (2017) Current situation and Countermeasures of paper cultural relics protection. Chin. Foreign Commun. 3(8):50.
39. Zhang, X., Wang, Y., Zhan, C. (2007) Tradition and modern of paper cultural relics protection and restoration. Cult. Geogr. 2(1):61–65.