Photoflash thermal diffusivity measurement of carbon nanotube-filled PVDF composite at low temperature

The suitability of a simple photoflash technique was further examined in the measurement of thermal diffusivity of nanotube-filled polyvinylidene difluoride (PVDF) film composites at low temperature. The effect of temperature and carbon nanotube (CNT) composition in PVDF composite on its thermal diffusivity is presented as equivalent to the effect of changing thermal phonon mean free path. It is done by assuming no other thermal carrier effects other than from phonons detected during measurement by using photoflash technique. The results show that thermal diffusivity of CNT-filled PVDF film composites was found to have consistently increased with increasing the CNT concentration or decreasing temperature, as in the case of insulators with dominant phonon thermal carriers. At any particular temperature, a dramatic increase in thermal diffusivity was noticed at the beginning as the CNT concentration was systematically increased up to a 1% turning point, from which the thermal diffusivity increased further at a much smaller rate with the CNT addition up to 10%. The thermal diffusivity of the samples was in the range of about (10–35) × 10− 8 m2/s depending on the temperature and the CNT concentration of the composites.