The influence of high temperature exposure to air on the damage to 3D-C/SiC composites

Jun-tao HOU, Sheng-ru QIAO, Cheng-yu ZHANG, Yue-bing ZHANG

New Carbon Materials· Volume 24· Issue 2
Publisher page

Abstract

3D-C/SiC composites, exposed in air at 600, 900, and 1 300 °C for 0 to 15 h, were investigated by three point bend tests at room temperature, SEM, and energy dispersive spectroscopy. The results show that the damage curves, expressed as a relative change of elastic modulus, of the composites for a 15 h exposure, could be divided into a sharply increasing stage (stage I) and a steady increasing stage (stage II). Stage I may be caused by a direct oxidation of the carbon fibers and interface carbon layers by the oxygen in air, and stage II may be caused by a diffuse controlled oxidation of the inner part of the composites. The matrix micro-cracks, induced by a difference of coefficients of thermal expansion between matrix and carbon fibers in the cooling process after composite preparation act as oxygen diffuse paths and are where the oxidation takes place. The fact that the damage decreases with temperature for the same exposure time may be caused by the crack shrinking at high temperature, which decreases the oxidizable surface area and inhibits the diffusion of oxygen into the composites.
Source: expertdata · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Advanced ceramic materials synthesis · Additive Manufacturing and 3D Printing Technologies · Innovations in Concrete and Construction Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (14)

Show source-provided references
1. C/C–SiC composites for space applications and advanced friction systems[J]10.1016/j.msea.2005.08.204 ↗
2. Advanced ceramic matrix composite materials for current and future propulsion technology applications[J]10.1016/j.actaastro.2004.05.052 ↗
3. Preparation and mechanical properties of C/SiC composites with carbon fiberwoven perform[J]10.1016/j.matlet.2006.04.099 ↗
4. Interaction between fatigue and creep and life prediction method of 3D-C/SiC[C]
5. Tensile creep damage and creep mechanism of 3D-C/SiC composite[J]
6. Tensile creep damage of 2D-C/SiC composites evaluated using the fractal dimension and elastic modulus[J]
7. Effect of high temperature treatment on the fabrication and mechanical properties of C/C-SiC composites[J]
8. Development of damage in a 2D woven C/SiC composite under mechanical loading: I. Mechanical characterization[J]10.1016/S0266-3538(96)00094-2 ↗
9. Kinetics and mechanisms of oxidation of 2D woven C/SiC composites: I, Experimental approach[J]10.1111/j.1151-2916.1994.tb07096.x ↗
10. Effect of heat treatment on the thermal expansion of 2D and 3D C/SiC composites from room temperature to 1 400 °C[J]10.1016/S0008-6223(03)00125-8 ↗
11. Structure/oxidation behavior relationship in the carbonaceous constituents of 2D-C/PyC/SiC composites[J]10.1016/0008-6223(93)90086-P ↗
12. Effect of carbon interlayer on oxidation behavior of C/SiC composites with a coating from room temperature to 1 500 · [J]10.1016/S0921-5093(00)01405-2 ↗
13. Ultrasonic study of elasticity-porosity relationship in polystalline alumina [J]10.1063/1.1659671 ↗
14. Dependence of mechanical strength of brittle polycrystalline specimens on porosity and gain size[J]10.1111/j.1151-2916.1959.tb13596.x ↗