Linking in situ charge accumulation to electronic structure in doped SrTiO3 reveals design principles for hydrogen-evolving photocatalysts
Source abstract
Abstract
Recently, high solar-to-hydrogen efficiencies were demonstrated using La and Rh co-doped SrTiO3 (La,Rh:SrTiO3) incorporated into a low-cost and scalable Z-scheme device, known as a photocatalyst sheet. However, the unique properties that enable La,Rh:SrTiO3 to support this impressive performance are not fully understood. Combining in situ spectroelectrochemical measurements with density functional theory and photoelectron spectroscopy produces a depletion model of Rh:SrTiO3 and La,Rh:SrTiO3 photocatalyst sheets. This reveals remarkable properties, such as deep flatband potentials (+2 V versus the reversible hydrogen electrode) and a Rh oxidation state dependent reorganization of the electronic structure, involving the loss of a vacant Rh 4d mid-gap state. This reorganization enables Rh:SrTiO3 to be reduced by co-doping without compromising the p-type character. In situ time-resolved spectroscopies show that the electronic structure reorganization induced by Rh reduction controls the electron lifetime in photocatalyst sheets. In Rh:SrTiO3, enhanced lifetimes can only be obtained at negative applied potentials, where the complete Z-scheme operates inefficiently. La co-doping fixes Rh in the 3+ state, which results in long-lived photogenerated electrons even at very positive potentials (+1 V versus the reversible hydrogen electrode), in which both components of the complete device operate effectively. This understanding of the role of co-dopants provides a new insight into the design principles for water-splitting devices based on bandgap-engineered metal oxides. Understanding the origin of unprecedented solar-to-hydrogen efficiencies in doped SrTiO3 has proved challenging. Linking in situ charge accumulation to electronic structure in this system now reveals design principles for hydrogen-evolving photocatalysts.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Electronic and Structural Properties of Oxides · Advanced Photocatalysis Techniques · Copper-based nanomaterials and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. Fujishima, A., Zhang, X. & Tryk, D. A. TiO2 photocatalysis and related surface phenomena. Surf. Sci. Rep. 63, 515–582 (2008).10.1016/j.surfrep.2008.10.001 ↗
2. Pai, Y. Y., Tylan-Tyler, A., Irvin, P. & Levy, J. Physics of SrTiO3-based heterostructures and nanostructures: a review. Rep. Prog. Phys. 81, 036503 (2018).10.1088/1361-6633/aa892d ↗
3. Goto, Y. et al. A particulate photocatalyst water-splitting panel for large-scale solar hydrogen generation. Joule 2, 509–520 (2018).10.1016/j.joule.2017.12.009 ↗
4. Zhao, Z. et al. Electronic structure basis for enhanced overall water splitting photocatalysis with aluminum doped SrTiO3 in natural sunlight. Energy Environ. Sci. 12, 1385–1395 (2019).10.1039/C9EE00310J ↗
5. Abe, R. Recent progress on photocatalytic and photoelectrochemical water splitting under visible light irradiation. J. Photochem. Photobiol. C 11, 179–209 (2011).10.1016/j.jphotochemrev.2011.02.003 ↗
6. Khan, S. U. M., Al-Shahry, M. & Ingler, W. B. Efficient photochemical water splitting by a chemically modified n-TiO2. Science 297, 2243–2245 (2002).10.1126/science.1075035 ↗
7. Asahi, R., Morikawa, T., Ohwaki, T., Aoki, K. & Taga, Y. Visible-light photocatalysis in nitrogen-doped titanium oxides. Science 293, 269–271 (2001).10.1126/science.1061051 ↗
8. Konta, R., Ishii, T., Kato, H. & Kudo, A. Photocatalytic activities of noble metal ion doped SrTiO3 under visible light irradiation. J. Phys. Chem. B 108, 8992–8995 (2004).10.1021/jp049556p ↗
9. Herrmann, J. M., Disdier, J. & Pichat, P. Effect of chromium doping on the electrical and catalytic properties of powder titania under UV and visible illumination. Chem. Phys. Lett. 108, 618–622 (1984).10.1016/0009-2614(84)85067-8 ↗
10. Daghrir, R., Drogui, P. & Robert, D. Modified TiO2 for environmental photocatalytic applications: a review. Ind. Eng. Chem. Res. 52, 3581–3599 (2013).10.1021/ie303468t ↗
11. Sakatani, Y. et al. Metal ion and N co-doped TiO2 as a visible-light photocatalyst. J. Mater. Res. 19, 2100–2108 (2004).10.1557/JMR.2004.0269 ↗
12. Kudo, A., Niishiro, R., Iwase, A. & Kato, H. Effects of doping of metal cations on morphology, activity, and visible light response of photocatalysts. Chem. Phys. 339, 104–110 (2007).10.1016/j.chemphys.2007.07.024 ↗
13. Torres, G. R., Lindgren, T., Lu, J., Granqvist, C. G. & Lindquist, S. E. Photoelectrochemical study of nitrogen-doped titanium dioxide for water oxidation. J. Phys. Chem. B 108, 5995–6003 (2004).10.1021/jp037477s ↗
14. Sivula, K. & Van De Krol, R. Semiconducting materials for photoelectrochemical energy conversion. Nat. Rev. Mater. 1, 15010 (2016).10.1038/natrevmats.2015.10 ↗
15. Tilley, S. D., Cornuz, M., Sivula, K. & Grätzel, M. Light-induced water splitting with hematite: improved nanostructure and iridium oxide catalysis. Angew. Chem. Int. Ed. 49, 6405–6408 (2010).10.1002/anie.201003110 ↗
16. Zhong, D. K. & Gamelin, D. R. Photo-electrochemical water oxidation by cobalt catalyst (‘Co–Pi’)/α-Fe2O3 composite photoanodes: oxygen evolution and resolution of a kinetic bottleneck. J. Am. Chem. Soc. 132, 4202–4207 (2010).10.1021/ja908730h ↗
17. Kuang, Y. et al. Ultrastable low-bias water splitting photoanodes via photocorrosion inhibition and in situ catalyst regeneration. Nat. Energy 2, 16191 (2017).10.1038/nenergy.2016.191 ↗
18. Kim, J. H. et al. Awakening solar water‐splitting activity of ZnFe2O4 nanorods by hybrid microwave annealing. Adv. Energy Mater. 5, 1401933 (2015).10.1002/aenm.201401933 ↗
19. Li, Y. et al. Cobalt phosphate-modified barium-doped tantalum nitride nanorod photoanode with 1.5% solar energy conversion efficiency. Nat. Commun. 4, 2566 (2013).10.1038/ncomms3566 ↗
20. Minegishi, T., Nishimura, N., Kubota, J. & Domen, K. Photoelectrochemical properties of LaTiO2N electrodes prepared by particle transfer for sunlight-driven water splitting. Chem. Sci. 4, 1120–1124 (2013).10.1039/c2sc21845c ↗
21. Maeda, K. et al. Photocatalyst releasing hydrogen from water. Nature 440, 295 (2006).10.1038/440295a ↗
22. Luo, J. et al. Cu2O nanowire photocathodes for efficient and durable solar water splitting. Nano Lett. 16, 1848–1857 (2016).10.1021/acs.nanolett.5b04929 ↗
23. Wang, Q., Hisatomi, T., Ma, S. S. K., Li, Y. & Domen, K. Core/shell structured La- and Rh-codoped SrTiO3 as a hydrogen evolution photocatalyst in Z-scheme overall water splitting under visible light irradiation. Chem. Mater. 26, 4144–4150 (2014).10.1021/cm5011983 ↗
24. Wang, Q. et al. Z-scheme water splitting using particulate semiconductors immobilized onto metal layers for efficient electron relay. J. Catal. 328, 308–315 (2015).10.1016/j.jcat.2014.12.006 ↗
25. Wang, Q. et al. Scalable water splitting on particulate photocatalyst sheets with a solar-to-hydrogen energy conversion efficiency exceeding 1%. Nat. Mater. 15, 611–615 (2016).10.1038/nmat4589 ↗
26. Wang, Q. et al. Particulate photocatalyst sheets based on carbon conductor layer for efficient Z-scheme pure-water splitting at ambient pressure. J. Am. Chem. Soc. 139, 1675–1683 (2017).10.1021/jacs.6b12164 ↗
27. Kawasaki, S. et al. Elucidation of Rh-induced in-gap states of Rh:SrTiO3 visible-light-driven photocatalyst by soft X-ray spectroscopy and first-principles calculations. J. Phys. Chem. C 116, 24445–24448 (2012).10.1021/jp3082529 ↗
28. Abe, Y., Kato, K., Kawamura, M. & Sasaki, K. Rhodium and rhodium oxide thin films characterized by XPS. Surf. Sci. Spectra 8, 117–125 (2001).10.1116/11.20010801 ↗
29. Modak, B. & Ghosh, S. K. Exploring the role of La codoping beyond charge compensation for enhanced hydrogen evolution by Rh–SrTiO3. J. Phys. Chem. B 119, 11089–11098 (2015).10.1021/acs.jpcb.5b02906 ↗
30. Murthy, D. H. K. et al. Revealing the role of the Rh valence state, La doping level and Ru cocatalyst in determining the H2 evolution efficiency in doped SrTiO3 photocatalysts. Sustain. Energy Fuels 3, 208–218 (2019).10.1039/C8SE00487K ↗
31. Iwashina, K. & Kudo, A. Rh-doped SrTiO3 photocatalyst electrode showing cathodic photocurrent for water splitting under visible-light irradiation. J. Am. Chem. Soc. 133, 13272–13275 (2011).10.1021/ja2050315 ↗
32. Godin, R., Kafizas, A. & Durrant, J. R. Electron transfer dynamics in fuel producing photosystems. Curr. Opin. Electrochem. 2, 136–143 (2017).10.1016/j.coelec.2017.03.012 ↗
33. Murthy, D. H. K. et al. Revealing the role of the Rh valence state, La doping level and Ru cocatalyst in determining the H2 evolution efficiency in doped SrTiO3 photocatalysts. Sustain. Energy Fuels 3, 208–218 (2019).10.1039/C8SE00487K ↗
34. Oropeza, F. E. & Egdell, R. G. Control of valence states in Rh-doped TiO2 by Sb co-doping: a study by high resolution X-ray photoemission spectroscopy. Chem. Phys. Lett. 515, 249–253 (2011).10.1016/j.cplett.2011.09.017 ↗
35. Glover, E. N. K., Ellington, S. G., Sankar, G. & Palgrave, R. G. The nature and effects of rhodium and antimony dopants on the electronic structure of TiO2: towards design of Z-scheme photocatalysts. J. Mater. Chem. A 4, 6946–6954 (2016).10.1039/C6TA00293E ↗
36. Fujisawa, Jichi, Eda, T. & Hanaya, M. Comparative study of conduction-band and valence-band edges of TiO2, SrTiO3, and BaTiO2 by ionization potential measurements. Chem. Phys. Lett. 685, 23–26 (2017).10.1016/j.cplett.2017.07.031 ↗
37. Kawasaki, S. et al. Epitaxial Rh-doped SrTiO3 thin film photocathode for water splitting under visible light irradiation. Appl. Phys. Lett. 101, 033910 (2012).10.1063/1.4738371 ↗
38. Rettie, A. J. E. et al. Combined charge carrier transport and photoelectrochemical characterization of BiVO4 single crystals: intrinsic behavior of a complex metal oxide. J. Am. Chem. Soc. 135, 11389–11396 (2013).10.1021/ja405550k ↗
39. Ma, Y., Le Formal, F., Kafizas, A., Pendlebury, S. R. & Durrant, J. R. Efficient suppression of back electron/hole recombination in cobalt phosphate surface-modified undoped bismuth vanadate photoanodes. J. Mater. Chem. A 3, 20649–20657 (2015).10.1039/C5TA05826K ↗
40. Zachäus, C., Abdi, F. F., Peter, L. M. & Van De Krol, R. Photocurrent of BiVO4 is limited by surface recombination, not surface catalysis. Chem. Sci. 8, 3712–3719 (2017).10.1039/C7SC00363C ↗
41. Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999).10.1103/PhysRevB.59.1758 ↗
42. Perdew, J. P. et al. Restoring the density-gradient expansion for exchange in solids and surfaces. Phys. Rev. Lett. 100, 136406 (2008).10.1103/PhysRevLett.100.136406 ↗
43. Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).10.1103/PhysRevB.54.11169 ↗
44. Moreno, J. & Soler, J. M. Optimal meshes for integrals in real- and reciprocal-space unit cells. Phys. Rev. B 45, 13891–13898 (1992).10.1103/PhysRevB.45.13891 ↗
45. Godin, R., Wang, Y., Zwijnenburg, M. A., Tang, J. & Durrant, J. R. Time-resolved spectroscopic investigation of charge trapping in carbon nitrides photocatalysts for hydrogen generation. J. Am. Chem. Soc. 139, 5216–5224 (2017).10.1021/jacs.7b01547 ↗
46. Wilkinson, F. Diffuse reflectance laser flash photolysis. J. Photochem. 17, 52 (1981).10.1016/0047-2670(81)85111-8 ↗
47. Kessler, R. W., Oelkrug, D. & Wilkinson, F. The detection of transient spectra within polycrystalline samples using the new technique of diffuse reflectance flash photolysis. Appl. Spectrosc. 36, 673–675 (1982).10.1366/0003702824639213 ↗